Process for preparing vapour pressure air-entrained concrete light heat-insulation fireproof bricks by gold tailings

A technology of gold tailings and autoclaved aeration is applied in the field of preparation of refractory bricks to achieve the effect of significant energy saving, low bulk density and temperature increase.

Inactive Publication Date: 2008-10-22
福建省万旗非金属材料有限公司
View PDF0 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no relevant report on how to directly use gold tailings to prepare aerated concrete lightweight refractory bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Mix and grind 57kg of gypsum and 570kg of lime in a fine grinder to achieve pre-activation treatment to make gypsum lime powder, which is sent to the lime powder silo through the bucket elevator for standby.

[0031] (2) Take 3000kg of gold tailings in the ball mill feeding hopper, gradually add the ball mill for grinding, control the degree of slurry at about 60%, add a total of about 2000kg of water to make slurry while grinding the ball mill, and pump it by the mud pump Put it into the slurry storage tank for standby.

[0032] (3) Put 1000kg PC32.5R bagged cement into the cement storage tank for later use.

[0033](4) Each pouring mold (2.72m 3 ) Get 1.25kg aluminum powder paste, 1.10kg pull open powder and 2.20kg self-made composite admixture (turpentine amine soap: triterpene saponin=3: 7), put into aluminum powder mixer and stir into 5% water suspension Reserve in the aluminum powder storage tank (the above-mentioned aluminum powder paste, foam stabilizer, a...

Embodiment 2

[0037] (1) Mix and grind 60kg of gypsum and 600kg of lime in a fine grinder to achieve pre-activation treatment to make gypsum lime powder, which is sent to the lime powder silo through the bucket elevator for standby.

[0038] (2) Take 3000kg of gold tailings in the ball mill feeding hopper, gradually add the ball mill to grind, control the pulp degree at about 62.5%, add a total of about 1800kg of water to make slurry while grinding the ball mill, and pump it by the mud pump Put it into the slurry storage tank for standby.

[0039] (3) Put 1000kg PC32.5R bagged cement into the cement storage tank for later use.

[0040] (4) Each pouring mold (2.72m 3 ) get 1.35kg aluminum powder paste, 1.15kg saponins powder and 2.0kg self-made composite admixture (turpentine amine soap: triterpene saponin = 4: 6), put into aluminum powder mixer and stir into 5% water suspension and pour aluminum Reserve in the powder storage tank (the above-mentioned aluminum powder paste, foam stabilizer...

Embodiment 3

[0044] (1) Mix and grind 64kg of gypsum and 690kg of lime in a fine grinder to achieve pre-activation treatment to make gypsum lime powder, which is sent to the lime powder silo through the bucket elevator for standby.

[0045] (2) Take 3000kg of gold tailings in the ball mill feeding hopper, gradually add the ball mill for grinding, control the pulp degree at about 59.5%, add a total of about 2050kg of water to make slurry while grinding the ball mill, and pump it by the mud pump Put it into the slurry storage tank for standby.

[0046] (3) Put 1000kg PC32.5R bagged cement into the cement storage tank for later use.

[0047] (4) Each pouring mold (2.72m 3 ) get 1.3kg aluminum powder paste, 1.25kg acacia powder and 1.8kg self-made composite admixture (turpentine amine soap: triterpene saponin=5: 5), put into aluminum powder mixer and stir into 5% water suspension and pour aluminum Reserve in the powder storage tank (the above-mentioned aluminum powder paste, foam stabilizer,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a firebrick preparation method, in particular to a method of preparing an autoclaved aerated concrete light heat insulating firebrick with gold tailings. The invention takes the gold tailings as the main raw material which is made by a pre-activating treatment, then a certain amount of cement, lime, foam stabilizer of nekal bx or soap pod powder and aluminum power paste are added, and then plaster and self-made compound admixtures are added to prepare into sizing agent. The later preparing procedures are as follows: pour mold for gas-forming and stilling, dry heat pre-curing, cutting and stacking, being steamed in a caldron and being taken out of the caldron, and finally the firebrick is formed. The firebrick is put into the caldron to steam for 5 to 7 hours under constant voltage; the steam pressure is 1.1 to 1.5 MPa, the temperature is from 185 DEG C to 195 DEG C. The firebricks prepared by the method have good effect of heat insulation in stove owing to low coefficient of heat conductivity, thereby being used in the low temperature section of ceramics kiln collapses, tunnels, resistance furnace and being capable of realizing energy saving. The firebricks prepared by the method also have the advantage of being light owing to the volume and density being less than those of the majority of light heat insulating firebricks.

Description

technical field [0001] The invention relates to a method for preparing refractory bricks, in particular to a method for preparing autoclaved aerated concrete lightweight heat-insulating refractory bricks by using gold tailings. technical background [0002] Refractory bricks are widely used in thermal kilns such as industrial smelting, forging, and porcelain firing, and have become an indispensable and important material. With the advancement of technology, refractory bricks have gradually developed from heavy refractory bricks to various lightweight refractory bricks. Lightweight heat-insulating refractory bricks are composed of solid phase and gaseous phase, and the gas forms isolated air pockets in the bricks. Therefore, light-weight heat-insulating refractory bricks have a low thermal conductivity and play a better role in thermal kilns. thermal insulation effect. At present, in addition to the necessary pore-forming materials such as floating beads, perlite, vermiculi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/66
Inventor 谢文清林积梁罗伟
Owner 福建省万旗非金属材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com