A technology of composite cementitious material and geopolymer, applied in cement production and other directions, can solve the problems of large-scale utilization of environmental pollution, poor toughness, high brittleness, etc., and achieve the effects of high waste utilization rate, resource saving and energy saving.

Inactive Publication Date: 2009-09-30
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the defects of high brittleness and poor toughness of existing geopolymer materials, in order to solve the problem of environmental pollution caused by the large-scale utilization and storage of industrial solid waste, the purpose of the present invention is to provide a kind of industrial solid waste steel slag or Preparation method of geopolymer and organic polymer composite gelling material with fly ash as main raw material and organic polymer as structural modifier

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing geopolymer and organic macromolecule composite gelled material
  • Method for preparing geopolymer and organic macromolecule composite gelled material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1: Steel slag geopolymer and organic polymer composite cementitious material

[0030] Accurately take by weighing 1400g of steel slag, take this as the basis of measurement (100%); adopt the external mixing method, the dosage of sodium silicate is 20% of the weight of steel slag; the dosage of styrene / butyl acrylate copolymer emulsion is 0% of the weight of steel slag respectively % (control), 5%, 10%, 15%, 20% and 25%; the water-slag ratio is 0.36.

[0031] Sodium silicate is dissolved in water, and styrene / butyl acrylate copolymer emulsion is mixed into the solution at room temperature to form a stable high molecular alkaline solution.

[0032]Pour the steel slag into a double-rotation and double-speed slurry mixer for stirring, then add the polymer alkaline solution, stir at a high speed to form a uniformly mixed slurry, and put the slurry into a 40mm×40mm×160mm iron triple mold. Vibrate on the rubber sand vibrating table and scrape it flat with a scraper to...

Embodiment 2

[0036] Example 2: Preparation of fly ash geopolymer and organic polymer composite cementitious material

[0037] Accurately take by weighing fly ash 1200g, based on this (100%); Adopt external blending method, sodium silicate dosage is 22% of flyash weight; Styrene / butyl acrylate copolymer emulsion dosage is powder respectively 0% (control), 5%, 10%, 15%, 20% and 25% of the weight of coal ash; the water-cement ratio is 0.36.

[0038] Sodium silicate is dissolved in water, and styrene / butyl acrylate copolymer emulsion is mixed into the solution at room temperature to form a stable high molecular alkaline solution.

[0039] Pour the fly ash into the double-rotation and double-speed slurry mixer for stirring, then add the polymer alkaline solution, stir at a high speed to form a uniform slurry, and put the slurry into a 40mm×40mm×160mm iron triple mold middle. Vibrate on the glue sand vibrating table and scrape it flat with a scraper to obtain the molded fly ash geopolymer and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a geopolymer and organic macromolecule composite gelled material. In the method, slag or fly ash capable of providing geopolymer components and styrene / butyl acrylate copolymer emulsion are utilized to produce a slag or fly ash geopolymer and organic macromolecule composite gelled material under the action of silicate excitants; wherein the amount of styrene / butyl acrylate copolymer emulsion is 5-25 percent of the weight of phosphatic slag or slag, and the amount of the alkali excitant sodium silicate is 20-22 percent of the weight of the phosphatic slag or slag; and the flexural strength of the geopolymer polymer and organic macromolecule composite is superior to the inorganic aluminosilicate polymer in 28-day age, and the 28-day maximum flexural strength is 1.76 times of that of the inorganic aluminosilicate polymer. The preparation process has no discharge of waste water, waste gas and waste slag, does not need heating, is green, environment-friendly and energy-saving, reduces the consumption, and is one effective approach for large-scale resource utilization of industrial solid wastes.

Description

technical field [0001] The invention belongs to the preparation of inorganic-organic composite materials, in particular to a preparation method of geopolymer and organic macromolecule composite gelling material. Background technique [0002] China is a large energy country dominated by coal resources. Currently, the annual discharge of fly ash produced by coal combustion reaches 200 million tons. At the same time, my country is also a large iron and steel country. The slag and steel slag discharged by iron and steel plants are about 100 million tons each year. tons; more than 10 million tons of phosphorus slag are discharged annually from refining yellow phosphorus. The long-term placement of these waste residues not only takes up a lot of fertile land and destroys the ecology; but also long-term exposure to the sun and rain will pollute groundwater sources and rivers and lakes, causing serious environmental pollution. It is used as an inorganic aluminosilicate polymer glue w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/26C04B7/26C04B7/147
CPCC04B28/008C04B28/28Y02P40/10
Inventor 张耀君李圣徐德龙宋强吴永超吴勇张建文曹李红王亚超
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com