Method for copolymerization of alpha-methyl styrene (AMS) and maleic anhydride (MAn)

A technology of methyl styrene and maleic anhydride, which is applied in the field of copolymerization of α-methyl styrene and maleic anhydride, can solve problems such as narrow particle size distribution, achieve narrow particle size distribution, simple process system, and predictable morphology control effect

Inactive Publication Date: 2009-11-18
BEIJING UNIV OF CHEM TECH
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And the present invention can prepare the maleic anhydride and α-methylstyrene alternating copolymer microsphere that contains reactive anhydride group, in the dispersion system of this polymer microsphere, the surface of monodisperse polymer microsphere is clean, particle size Controllable, narrow particle size distribution, and can solve the disadvantages caused by the need to use stabilizers in traditional dispersion polymerization systems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for copolymerization of alpha-methyl styrene (AMS) and maleic anhydride (MAn)
  • Method for copolymerization of alpha-methyl styrene (AMS) and maleic anhydride (MAn)
  • Method for copolymerization of alpha-methyl styrene (AMS) and maleic anhydride (MAn)

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057]The molar ratio of MAn and AMS is 1:1, wherein MAn is 0.6139g, AMS is 0.7387g; the initiator is AIBN, 0.0329g; the medium is isoamyl acetate, 40mL. Adopt water-bath heating, react 6 hours under the temperature of 70 ℃, obtain the average particle diameter (Dn), dispersion coefficient (U) and polymerization conversion rate (C) of PMSMA copolymer microspheres p ), and the number average molecular weight (Mn) results of the polymer are shown in Table 1.

Embodiment 2

[0059] The molar ratio of MAn and AMS is 1:1, wherein MAn is 1.2258g, AMS is 1.4773g; the initiator is AIBN, 0.0329g; the medium is isoamyl acetate, 40mL. Adopt water-bath heating, react 6 hours under the temperature of 70 ℃, obtain the average particle diameter (Dn), dispersion coefficient (U) and polymerization conversion rate (C) of PMSMA copolymer microspheres p ), and the number average molecular weight (Mn) results of the polymer are shown in Table 1.

Embodiment 3

[0061] The molar ratio of MAn and AMS is 1:1, wherein MAn is 2.4515g, AMS is 2.9545g; the initiator is AIBN, 0.0329g; the medium is isoamyl acetate, 40mL. Adopt water-bath heating, react 6 hours under the temperature of 70 ℃, obtain the average particle diameter (Dn), dispersion coefficient (U) and polymerization conversion rate (C) of PMSMA copolymer microspheres p ), and the number average molecular weight (Mn) results of the polymer are shown in Table 1. Scanning electron micrographs of polymer microspheres are shown in figure 1 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing an alternating copolymer of alpha-methyl styrene (AMS) and maleic anhydride (MAn), belonging to the high molecular precipitation polymerization field. The method comprises the following steps: taking the mixed solution which is formed by respectively mixing organic acid alkyl ester or ketone with alkane as reaction medium, taking organic peroxide or azo compound as an initiator to initiate monomer AMS to copolymerize MAn and preparing the copolymer microsphere of the AMS and MAn; wherein, the copolymer microsphere features uniform grain diameter and monodispersity. The method has simple process and can synthesize good dispersion system featuring uniform grain diameter and even dispersion.

Description

technical field [0001] The invention relates to a method for copolymerizing alpha-methylstyrene (AMS) and maleic anhydride (MAn). Utilize the method of the present invention, can obtain the colloid of the copolymer of milky white α-methylstyrene and maleic anhydride under the condition of not adding any stabilizer, the disperse phase of colloid is the polymer microsphere of monodisperse, and polymer is spherical Composed of alternating copolymers of α-methylstyrene and maleic anhydride. Background technique [0002] α-Methylstyrene (AMS), maleic anhydride (MAn) copolymer is a new type of polymer material with low price and high potential value, which is widely used in additives for organic glass, latex coatings, and modifiers for plastic products , and used to improve the processability of materials and other fields. Among them, α-methylstyrene is a by-product produced when the cumene method co-produces phenol and acetone, and has high economic value. [0003] In addition...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F222/08C08F212/08C08F2/14
Inventor 邓建元陈铖杨万泰
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com