Method for preparing metallic matrix composite coating reinforced by alumina ceramics particles

A technology of alumina ceramics and composite materials, applied in metal material coating process, coating, heating inorganic powder coating and other directions, can solve the problems affecting the operation efficiency of thermal power plants, safe operation and power generation costs, and parts wear and ash removal. Technology, difficult to promote and use, etc., to achieve the effect of reducing the cost of coating preparation, high hardness and low price

Inactive Publication Date: 2009-11-18
JILIN UNIV
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the serious wear problem of dry ash removal system components has always been the main obstacle to the wide application of dry ash removal technology in my country, and it is also one of the main problems affecting the operation efficiency, operation...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing metallic matrix composite coating reinforced by alumina ceramics particles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1, adopt 22%Al 2 o 3 +78% NiCrBSi mixed spray powder, plasma spray parameters are: current 440A; voltage 47V; primary gas (Ar) 47L / min; secondary gas (H 2 )3L / min; powder feeding speed 30g / min; spraying distance 80mm; spraying speed 90mm / s, to prepare Al 2 o 3P / NiCrBSi composite coating. Al 2 o 3P The erosion wear resistance rate of / NiCrBSi coating is 6.9×10 -3 mm 3 / g-7.2×10 -3 mm 3 / g; coating / substrate interface bonding strength is 30MPa-34MPa.

Embodiment 2

[0021] Embodiment 2, adopt 20% Al 2 o 3 +80% NiCrBSi mixed spray powder, plasma spray parameters are: current 440A; voltage 47V; primary gas (Ar) 47L / min; secondary gas (H 2 )3L / min; powder feeding speed 30g / min; spraying distance 80mm; spraying speed 90mm / s, to prepare Al 2 o 3P / NiCrBSi composite coating. Al 2 o 3P The erosion wear resistance rate of / NiCrBSi coating is 7.2×10 -3 mm 3 / g-7.5×10 -3 mm 3 / g; coating / substrate interface bonding strength is 31MPa-35MPa.

Embodiment 3

[0022] Embodiment 3, adopt 24% Al 2 o 3 +76% NiCrBSi mixed spray powder, plasma spray parameters are: current 440A; voltage 47V; primary gas (Ar) 47L / min; secondary gas (H 2 )3L / min; powder feeding speed 30g / min; spraying distance 80mm; spraying speed 90mm / s, to prepare Al 2 o 3P / NiCrBSi composite coating. Al 2 o 3P The erosion wear resistance rate of / NiCrBSi coating is 7.0×10 -3 mm 3 / g-7.4×10 -3 mm 3 / g; coating / substrate interface bonding strength is 25MPa-30MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing metallic matrix composite coating reinforced with alumina ceramics particles in the technical fields such as materials, electric power, metallurgy, machinery and the like, belonging to surface engineering techniques. The metallic matrix composite coating reinforced by alumina ceramics particles (AL2O3P/NiCrBSi) is prepared on the surface of the mild steel base material based on the characteristics of high wear and erosion resistance, low cost of the alumina materials, fine self-fluxing nature, wettability and plasma spraying technology of the NiCrBSi alloy, and the property of wearing and erosion resistance is improved. The technique process of preparing WCP/NiCrBSi composite material coating is as follows: coating design; sifting dusty spray; mixing the powder according to certain ratio; superficial treatment of base material; controlling plasma spraying parameter; and preparing WCP/NiCrBSi coating.

Description

technical field [0001] The invention relates to a method for preparing an alumina ceramic particle-reinforced metal matrix composite material coating in the technical fields of materials, electric power, metallurgy, machinery, etc., and belongs to surface engineering technology. Background technique [0002] Electric power industry is the pillar industry of national economy. Fly ash and slag produced by coal-fired boilers in thermal power plants account for about 1 / 5 of the coal consumption. The treatment of fly ash and slag has become an important production link of thermal power generation. There are two main methods of ash removal: one is to use a hydraulic ash removal system to clean and transport ash (referred to as water ash removal); the other is to use a pneumatic ash removal system to clean and transport ash (referred to as dry ash removal) . Because the dry ash removal system has the advantages of saving water resources, no pollution to the environment, and reusa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C24/08C23C4/12C23C4/06C23C4/134
Inventor 孙大千宫文彪韩耀武王文权宣兆志任振安谷晓燕
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap