Nano polyacrylate emulsion for water-based wood coating and method for preparing same

A technology of polyacrylate emulsion and water-based wood paint, applied in latex paint, device for coating liquid on the surface, coating, etc., can solve the problems of low crosslinking density and affecting mechanical properties, etc.

Active Publication Date: 2010-02-03
上海展辰涂料有限公司 +1
View PDF1 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Invention Patent Publication No. CN 1438253A "High Solid Content Acrylate Microemulsion for Wood" and other patents and documents, the disclosed technology does not use each monomer for molecular design and synthesis process design. Therefore, the crosslinking density is not high, affecting mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] formula:

[0066] Styrene (St) 85 parts

[0067] Methyl methacrylate (MMA) 110.5 parts

[0068] Butyl acrylate (BA) 100.5 parts

[0069] 6 parts of isobornyl methacrylate (IBOMA)

[0070] 6.7 parts of diacetone acrylamide (DAAM)

[0071] 10 parts of hydroxycyclohexyl methacrylate

[0072] 4.2 parts of methacrylic acid (MAA)

[0073] 4.6 parts of N-methylolacrylamide (NMA)

[0074] β-cyclohexyl-epoxy-ethyl-ethoxysilane 6 parts

[0075] Adipic acid dihydrazide 1 part

[0076] 0.3 parts of trimethylolpropane triacrylate (TMPTA)

[0077] Tetraethylene glycol dimethacrylate (TEGDMA) 1 part

[0078] Anion-nonionic emulsifier nonylphenol polyoxyethylene (4) ether ammonium sulfate 2.95 parts

[0079] Reactive emulsifier sodium vinyl sulfonate 1.0 parts

[0080] Reactive emulsifier α-allyl alkylphenol polyoxyethylene ether ammonium sulfate 1.1 parts

[0081] Initiator ammonium persulfate 5 parts

[0082] PH stabilizer 2-amino-2-methyl-1-propanol 4.1 parts

[0083] 37...

Embodiment 2

[0117] formula:

[0118] Styrene (St) 80 parts

[0119] 105 parts of methyl methacrylate (MMA)

[0120] Butyl acrylate (BA) 105 parts

[0121] 8 parts of isobornyl methacrylate (IBOMA)

[0122] Diacetone acrylamide (DAAM) 5 parts

[0123] 11 parts of hydroxycyclohexyl methacrylate

[0124] 5 parts of methacrylic acid (MAA)

[0125] N-methylolacrylamide (NMA) 5 parts

[0126] β-cyclohexyl-epoxy-ethyl-ethoxysilane 1 part

[0127] Adipic acid dihydrazide 1.5 parts

[0128] 1 part Trimethylolpropane Triacrylate (TMPTA)

[0129] Tetraethylene glycol dimethacrylate (TEGDMA) 0.5 parts

[0130] Anion-nonionic emulsifier nonylphenol polyoxyethylene (4) ether ammonium sulfate 4 parts

[0131] Reactive emulsifier sodium vinyl sulfonate 1.5 parts

[0132] Reactive emulsifier α-allyl alkylphenol polyoxyethylene ether ammonium sulfate 1.5 parts

[0133] Initiator ammonium persulfate 4 parts

[0134] PH stabilizer 2-amino-2-methyl-1-propanol 5 parts

[0135] 365 parts of water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water resistanceaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a nano polyacrylate emulsion for a water-based wood coating and a method for preparing the same. In the method, a plurality of functional monomers are used in the design of a core-shell structure and a molecular branch chain interpenetrating network of the emulsion particles; the aim of the invention can be achieved by the polymerization technology under a condition of a reaction type emulsifier, simultaneously beta-cyclohexyl-epoxy-ethyl-ethoxy silane is used for making the coating film crosslinked in a drying process, the mechanical property of the coating prepared bythe method is greatly improved compared with the coating of the water-based polyacrylate emulsion which does not use the beta-cyclohexyl-epoxy-ethyl-ethoxy silane, the shock resistance of the coatingis over 45kg.cm, the hardness of the coating reaches H or above class, and the waterproof property of the coating reaches 240 hours.

Description

technical field [0001] The invention relates to a nano polyacrylate emulsion for water-based wood paint. Background technique [0002] Self-crosslinking water-based polyacrylate emulsion at room temperature is a composition used for coatings and adhesives. The performance and use of the water-based polyacrylate emulsion vary with the monomers, additives and synthesis processes used. Invention Patent Publication No. CN 1438253A "High Solid Content Acrylate Microemulsion for Woodenware" and other patents and documents, the disclosed technology does not use each monomer for molecular design and synthesis process design. Therefore, the crosslinking density is not high and affects mechanical properties. Contents of the invention [0003] The purpose of the present invention is to provide a kind of nanometer polyacrylate emulsion and preparation method thereof for waterborne wood lacquer, to overcome the above-mentioned defect that prior art exists. [0004] Described polyacry...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/14C08F2/24C08F2/38C09D133/12C09D5/02B05D7/06C08F220/18C08F212/08
Inventor 叶荣森刘顺
Owner 上海展辰涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap