Silicon oxynitride combined carborundum high-temperature ceramic material and preparation method thereof
A high-temperature ceramic and silicon oxynitride technology, applied in the field of high-temperature ceramic materials, can solve the problems of large equipment investment, long production cycle and high production cost, and achieve the effects of less equipment investment, no shape restriction, and short process flow.
Active Publication Date: 2013-01-23
成都蜀冶新材料有限责任公司
View PDF0 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the research on this kind of material is not yet mature enough, and the pressure forming process still has problems such as large equipment investment, high energy consumption, long production cycle, etc., and the production cost is still too high, thus limiting its wide application; still need a lot of research In-depth research work to improve material performance while reducing production costs
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0046] (1) The YDT silicon oxynitride bonded silicon carbide high-temperature ceramic material in this embodiment is composed of aggregate, powder, admixture, and binder, wherein:
[0047] Taking the sum of the mass of aggregate and powder as 100% of the total mass:
[0048] The aggregate content accounts for 70% of the total mass, and the powder content accounts for 30% of the total mass; the addition of vanadium pentoxide as an admixture is 0.3% of the total mass; the binder includes sodium lignosulfonate with a mass percentage concentration of 50% Solution (referring to aqueous solution, the same below), polyvinyl alcohol solution (referring to aqueous solution, the same below) and dextrin with a mass percentage concentration of 6% are respectively 4%, 1%, and 0.4% of the total mass;
[0049]The aggregate in the above components is silicon carbide aggregate, in which the SiC content is ≥ 97%; the particle size is: 1-2mm accounts for 15% of the total mass of aggregate and p...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a silicon oxynitride combined carborundum high-temperature ceramic material which is made of raw materials of aggregate, power lot, admixture and binding agent, wherein the mass sum of the aggregate and the power lot is based on 100 percent, the content of the aggregate is 65-75 percent and the content of the power lot is 25-35 percent; the aggregate is carborundum aggregate; the power lot comprises carborundum powder, silica powder, silicon nitride powder, ball clay powder and fume silica; the admixture is vanadic oxide; and the bonding agent comprises sodium lignosulponate solution with concentration of 50 percent, polyvinyl alcohol solution with concentration of 6 percent and dextrine. The material ensures that the preparation process is more reasonable and economic by optimizing various component and the consumption thereof; during sintering, electric heating is not needed, N2 gas is not needed for protection and used as a reaction material, and the high-temperature ceramic material with favorable performance can be obtained by only heating a gas furnace in the oxidizing atmosphere. The invention also discloses a preparation method for the material, which adopts a ramming process and has the characteristics of little investment on equipment, short production flow, low energy consumption, wide application range and the like.
Description
technical field [0001] The invention belongs to the technical field of high-temperature ceramic materials, and relates to a silicon oxynitride bonded silicon carbide high-temperature ceramic material and a preparation method thereof. Background technique [0002] Silicon carbide is a typical polycrystalline compound, which can be divided into two types: α-silicon carbide and β-silicon carbide, among which β-silicon carbide is the main raw material for preparing silicon carbide ceramics. Silicon carbide refractory has excellent high-temperature properties such as high strength, large thermal conductivity, good thermal shock resistance, wear resistance, and corrosion resistance. It is a high-quality high-temperature ceramic material; it is widely used in metallurgy, energy, chemical and other industries. [0003] At present, silicon carbide products on the market mainly fall into the following two categories according to their combination methods: [0004] (1), the traditiona...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/565C04B35/622
Inventor 张命荣
Owner 成都蜀冶新材料有限责任公司