Preparation method of copper chloride hydroxide

A copper chloride, basic technology, applied in the field of compound preparation, to achieve the effects of environmental protection, rosy skin, and high absorption and utilization rate

Active Publication Date: 2010-06-02
昕嘉生物技术(长沙)有限公司
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent document also discloses a method for producing basic copper chloride using purchased copper sulfate, common salt and hydrochloric acid as raw materials. This production method has certain advantages in terms of process operation, cost, and environmental friendliness, but still There is a lot of room for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of preparation method of basic copper chloride of the present invention, comprises the following steps: add the water of 200ml in reaction kettle earlier, then open stirring device, drop into the cupric chloride (CuCl2) of 33.61g in reaction kettle 2 2H 2 (2), slowly add the copper hydroxide slurry of 160g after being warmed up to 85 DEG C (the copper hydroxide wet material of 110g containing copper hydroxide 60% adds 50g water and forms after beating), the control reaction pH value is at 6.8, in After reacting for 5 hours at a constant temperature and normal pressure at 85°C, the temperature was lowered, stirred and cooled with cooling water, the material was fed and centrifuged (centrifugal speed was 400r / min), and dried in a rotary kiln at a drying temperature of 90°C until the water content of the reaction product was Below 0.2%, pass through a 40-mesh sieve after drying, and finally prepare the finished product.

[0020] The crystal composition and structur...

Embodiment 2

[0022] A kind of preparation method of basic copper chloride of the present invention, comprises the following steps: add the water of 200ml in reaction kettle earlier, then open stirring device, drop into the cupric chloride (CuCl2) of 67.22g in reaction kettle 2 2H 2 (2), then slowly add the copper hydroxide slurry of 310g after being warmed up to 150°C (210g copper hydroxide wet material containing copper hydroxide 60% adds 100g water and forms after beating), the control reaction pH value is at 7.2, React at a constant temperature and pressure for 1 hour at a temperature of 150°C and a pressure of 500KPa, then lower the temperature and pressure, stir and cool with cooling water, and centrifuge the material at a centrifugal speed of 1500r / min, and dry it in a rotary kiln at a drying temperature of 140°C until the reaction The water content of the product is below 0.2%, and after being dried, it is passed through a 40-mesh sieve, and finally the finished product is prepared....

Embodiment 3

[0025] A kind of preparation method of basic copper chloride of the present invention, comprises the following steps: first in reaction pot, add 2m 3 water, then turn on the stirring device, and drop 675Kg of copper chloride (CuCl 2 2H 2 (2), slowly add 2750Kg of copper hydroxide slurry (1750Kg copper hydroxide wet material containing 60% copper hydroxide plus 1m 3 beating after water), control the pH value of the reaction at 8.2, react at a constant temperature and pressure at a temperature of 122°C and a pressure of 200KPa for 2 hours, then lower the temperature and pressure, stir and cool with cooling water, and centrifuge the material before feeding, and the centrifugal speed is 1000r / min. Drying is carried out by using a rotary kiln at a drying temperature of 110° C. until the water content of the reaction product is below 0.2 percent, passed through a 40-mesh sieve after drying, and finally the finished product is prepared.

[0026] The crystal composition and structur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of copper chloride hydroxide. The method comprises the following steps: adding copper hydroxide slurry in copper chloride solution according to a ratio of 2.5-3.5:1, reacting under the condition that the temperature is 80-160 DEG C, the pH value is 4-9 and the pressure is 0-600kPa, obtaining the reaction product after the reaction; and rinsing, centrifuging and drying the reaction product to obtain copper chloride hydroxide. The method of the invention has simple and safe operation, less waste discharge, lower production cost, more complete resource utilization and less environmental pollution.

Description

technical field [0001] The invention relates to a preparation method of a copper compound, in particular to a preparation method of a copper halide. Background technique [0002] Copper plays an important role in maintaining the normal metabolism and immunity of the body. Feeding experiments show that adding high copper in the feed can improve the daily gain, feed intake and feed efficiency of animals, and has the effect of promoting growth. At present, copper sulfate is mainly used as a source of copper in feed, and its biggest advantage is its low price. However, a large amount of copper sulfate will cause other serious problems. On the one hand, it has an antagonistic effect on trace elements such as Fe and Zn, and on the other hand On the one hand, due to the high solubility of copper sulfate, it aggravates the pollution to the environment after being discharged in large quantities. More seriously, Cu in the feed 2+ It is easily reduced, and this reduction reaction wil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01G3/05A23K1/175
Inventor 黄逸强
Owner 昕嘉生物技术(长沙)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap