Blend of PPC, PBAT, PCL and PBS and preparation method thereof

A blend and cold mixing technology, applied in the field of blending and preparation of PPC and PBAT, PCL and PBS, can solve the problems of pure PPC application difficulty, affecting storage and transportation, PPC forming agglomerates, etc., to achieve strong and tough , Fast biodegradation rate, easy processing effect

Inactive Publication Date: 2010-06-09
INNER MONGOLIA MENG XI HIGH TECH GRP CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the temperature is above Tg, PPC will form a cohesive block, which affects its storage and transportation; when the temperature is below Tg, PPC is in a glassy state and is brittle, so the application of pure PPC is very difficult.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Weigh 2000 grams of PPC (produced by Inner Mongolia Mengxi High-tech Group Company, glass transition temperature is 35 ℃), 20 grams of maleic anhydride, 20 grams of lipophilic modified light calcium carbonate (particle size is 800 mesh), stearic acid 2 grams, 100 grams of PBAT, 50 grams of PCL, and 50 grams of PBS were added to a high-speed mixer and stirred for 5 minutes at a cold mixing temperature of 0°C. The rotating speed of the mixer could be 1500 rpm; Mix the materials, extrude and granulate with a single-screw extruder, and the heating temperature in the highest heating zone is 173°C. Use the obtained pellets to test the sticky temperature of the pellets in the oven, and use the obtained pellets to prepare samples in the injection machine according to the requirements of GB / T 17037-1997, and then according to GB / T 1040-2006 According to the requirements of GB / T 2918-1998, the tensile performance test is carried out, and the test results are recorded.

Embodiment 2

[0018] Take by weighing 2000 grams of PPC (with embodiment 1), 30 grams of maleic anhydride, 50 grams of lipophilic modified light calcium carbonate (particle size is 1250 orders), 10 grams of epoxy soybean oil, PCL is 200 grams, and PBAT is 200 grams, PBS is 200 grams, join in the high-speed mixer, under the situation that the cold mixing temperature is 5 ℃, stir for 6 minutes, the rotating speed of the mixer can be 1000 rev / min; Out of granulation, the heating temperature in the highest heating zone is 175°C. The sticky starting temperature and tensile properties were tested with the obtained pellets, and the test results were recorded (same as in Example 1).

Embodiment 3

[0020] Take by weighing PPC (with embodiment 1) 2000 grams, maleic anhydride 20 grams, light calcium carbonate (particle size is 1250 order) 100 grams, stearic acid 20 grams, PCL is 100 grams, PBAT is 500 grams, PBS is Add 500 grams into a high-speed mixer, and stir for 10 minutes at a cold mixing temperature of 10°C. The speed of the mixer can be 800 rpm; release the cold mixture, and extrude and granulate with a single-screw extruder. The heating temperature in the heating zone is 176°C. The sticky starting temperature and tensile properties were tested with the obtained pellets, and the test results were recorded (same as in Example 1).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a blend of PPC, PBAT, PCL and PBS and a preparation method thereof. The blend consists of PPC, PBAT, PCL, PBS, an end-capping reagent, a lubricating agent and modified precipitated calcium carbonate. The preparation method comprises the following steps of: carrying out cold mixing on the PPC, the PBAT, the PCL, the PBS, the end-capping reagent, the lubricating agent and the modified precipitated calcium carbonate in a high-speed stirrer at the temperature not above 35 DEG C; and extruding and granulating cold mixed materials by a screw extruder, wherein the temperature of extruding and granulating is not more than 200 DEG C. With simple process method and common equipment, the invention is especially suitable for industrial production; meanwhile, the used materials are simple and easily obtained and can also be purchased in the market; the temperature of pastiness caking blocks of the blend processed by the method is greatly improved in comparison with pure PPC and the mechanical property of the blend is greatly improved in comparison with the pure PPC; and the blend widens the application range of the pure PPC and can be completely biodegraded.

Description

Technical field: [0001] The invention relates to a blend of PPC, PBAT, PCL and PBS and a preparation method, belonging to the field of polymer processing. Background technique: [0002] Environmental pollution is one of the urgent problems facing society today. Carbon dioxide is a waste gas produced in many industrial fields. It is discharged into the atmosphere, which not only pollutes the environment, but also wastes carbon resources. One of the raw materials for carbon dioxide-propylene oxide copolymer is carbon dioxide, which is copolymerized with carbon dioxide and propylene oxide. The reaction can fix carbon dioxide; at the same time, the obtained copolymer is a non-toxic, odorless, colorless solid with excellent barrier properties, and the copolymer has the characteristics of complete biodegradation, which can replace ordinary plastics to solve the "white pollution" problem, so it has Double environmental protection effect. Realizing the industrialized production of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08L67/04C08K13/06C08K9/04C08K3/26C08K5/09C08K5/1515B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/92704B29C2948/92895
Inventor 刘埃林汪英杰张光军陈有业高振勇郭颂旗李世英蒙昊王红霞武占存徐晓燕牛丽刚白景峰
Owner INNER MONGOLIA MENG XI HIGH TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com