Marble glue and preparation method thereof

A marble glue, unsaturated technology, applied in the direction of adhesives, etc., can solve the problems of complex production process, long gel time, unfavorable large-scale production, etc., and achieve the effect of simple process, low cost and easy operation.

Inactive Publication Date: 2010-06-16
江苏大力士投资有限公司
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing marble glue has defects such as long gel time, slow curing, poor weather resistance, and short storage period; the preparation method of the existing marble glue has high cost and complicated manufacturing process, which is not conducive to realizing large-scale industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of marble glue, including A component and B component, by mass parts, each component composition is as follows:

[0022] A component B component

[0023] Unsaturated polyester resin: 50 parts Benzoyl peroxide: 30 parts

[0024] Heavy calcium: 80 parts Dibutyl phthalate: 40 parts

[0025] Titanium dioxide: 0.05 parts Fumed white carbon black: 5 parts

[0026] N,N-Dimethylaniline: 0.05 parts Heavy calcium: 35 parts

[0027] Fumed silica: 1.5 parts

[0028] Hydroquinone: 0.02 parts

[0029] tert-butylcatechol: 0.01 parts

[0030] Among them, the unsaturated polyester resin is prepared from phthalic anhydride, maleic anhydride, glycol and styrene, and the percentages of each component in the total mass of raw materials are: 20% of phthalic anhydride, 10% of maleic anhydride, 30% of glycol %, styrene 40%. The preparation method of unsaturated polyester resin comprises the following steps: (1) put the weighed phthalic anhydride, maleic anhydride and glycol into ...

Embodiment 2

[0033] A kind of marble glue, including A component and B component, by mass parts, each component composition is as follows:

[0034] A component B component

[0035] Unsaturated polyester resin: 45 parts Methyl ethyl ketone peroxide: 20 parts

[0036] Barite powder: 45 parts tert-butyl peroxide: 15 parts

[0037] Heavy calcium: 35 parts Talcum powder: 20 parts

[0038] Carbon black: 0.05 parts Dibutyl phthalate: 30

[0039] Nano calcium carbonate: 1.5 parts Precipitated white carbon black: 3

[0040] N, N-diethylaniline: 0.02 parts

[0041] Hydroquinone: 0.01 parts

[0042] tert-butylcatechol: 0.01 parts

[0043] Among them, the unsaturated polyester resin is prepared from phthalic anhydride, maleic anhydride, glycol and styrene, and the percentages of each component in the total mass of raw materials are: 25% phthalic anhydride, 15% maleic anhydride, 30% glycol %, styrene 30%. The preparation method of unsaturated polyester resin comprises the following steps: (1) p...

Embodiment 3

[0046] A kind of marble glue, including A component and B component, by mass parts, each component composition is as follows:

[0047] A component B component

[0048] Unsaturated polyester resin: 55 parts Cyclohexanone peroxide: 40 parts

[0049] Barite powder: 45 parts Dibutyl phthalate: 35 parts

[0050] Talc powder: 30 parts Fumed silica: 7 parts

[0051] Titanium dioxide: 0.07 parts Quartz powder: 20

[0052] Organic bentonite: 1.5 parts Heavy calcium: 10 parts

[0053] N,N-Dimethylaniline: 0.05 parts

[0054] Cobalt naphthenate: 0.03 parts

[0055] Hydroquinone: 0.02 parts

[0056] Nitrophenol: 0.02 parts

[0057] Among them, the unsaturated polyester resin is prepared from phthalic anhydride, maleic anhydride, glycol and styrene, and the percentages of each component in the total mass of raw materials are: 30% of phthalic anhydride, 25% of maleic anhydride, 25% of glycol %, styrene 20%. The preparation method of unsaturated polyester resin comprises the following...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses marble glue and a preparation method thereof. The marble glue comprises a component A and a component B, wherein component A comprises the following ingredients by mass parts: 45-55 parts of unsaturated polyester resin, 75-85 parts of stuffing, 1.3-1.7 parts of thickening agent, 0.03-0.07 part of pigment, 0.02-0.04 part of polymerization inhibitor and 0.02-0.08 part of accelerant; and component B comprises the following ingredients by mass parts: 30-40 parts of curing agent, 30-40 parts of plasticizer, 20-40 parts of stuffing and 3-7 parts of thickening agent. Component A and component B are uniformly mixed according to the mass ratio of 100:(1.5-3) to obtain the marble glue in the invention. The invention has the advantages of high curing speed at normal temperature, easy operation, no peculiar smell during curing and the like. The preparation method of marble glue has the advantages of simple technique, wide material sources and low cost, and is beneficial to realizing industrial production.

Description

technical field [0001] The invention relates to a marble glue and a preparation method thereof, in particular to a marble glue having the advantages of fast curing speed at room temperature, easy operation, and no peculiar smell after curing. The cost is low, and it is beneficial to realize industrialized large-scale production. Background technique [0002] At present, marble glue is widely used in the bonding between various stone materials or the repair of cracks and broken marks on the surface of stone materials. The performance of marble glue is mainly reflected in hardness, toughness, fast curing, polishing, and weather resistance. However, the existing marble glue has defects such as long gel time, slow curing, poor weather resistance, and short storage period; the preparation method of the existing marble glue is high in cost and complicated in manufacturing process, which is not conducive to realizing large-scale industrial production. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J167/06
Inventor 余永重甘水平沈建斌熊桥林传军
Owner 江苏大力士投资有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com