Flexible strip processing line suitable for producing various high-strength steel
A high-strength steel and processing line technology, applied in the direction of heat treatment furnace, heat treatment equipment, process efficiency improvement, etc., can solve the problem of inability to produce high-strength grade hot-dip galvanized and plated alloyed hot-dip galvanized sheets, affecting the surface quality of cold-rolled sheets Normal operation, poor surface quality of high-strength cold-rolled sheets, etc., to achieve the effect of rich product variety, low alloy content and low production cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0051] Example 1
[0052] Referring to Figure 1, the process route of the present embodiment is, raw material 1-uncoiling cleaning 2-heating 3-soaking 4-slow cooling 5-jet cooling 6 (high hydrogen jet cooling)-overaging 10-final cooling 11-leveling 12- Finishing 13 - Oiling and post-processing 14 - Coiling 15 - Finished product 16.
[0053] The process of the invention can produce general cold-rolled sheets and phase-transformation-strengthened high-strength steel cold-rolled sheets, and is especially suitable for the production of cold-rolled TRIP steel and DP steel below 80 kilograms, cold-rolled 80 kilograms of TRIP steel and 80 kilograms of DP steel The process parameters are shown in Table 1. As can be seen in Table 1, for TRIP steel, it is important to control the soaking temperature, aging temperature and time of its continuous annealing, and the rapid cooling rate is not required; for high-strength DP steel, its continuous annealing is not high. The key process contr...
Example Embodiment
[0057] Example 2
[0058] Referring to Figure 2, the process route of the present embodiment is, raw material 1-uncoiling cleaning 2-heating 3-soaking 4-slow cooling 5-jet cooling 6 (high hydrogen jet cooling)-reheating 9-overaging 10-final cooling 11 - Flattening 12 - Finishing 13 - Oiling and post-processing 14 - Coiling 15 - Finished product 16.
[0059] Compared with Example 1, the process of the present invention can realize the over-aging process of low temperature and then high temperature. This process can use low-carbon aluminum killed steel to produce mild steel products with excellent anti-aging properties, and produce low-carbon aluminum products with excellent anti-aging properties. The process parameters of the killed mild steel product are shown in Table 2. As can be seen in Table 2, in order to produce low-carbon aluminum killed steel with excellent aging resistance, it is important to control the soaking temperature and aging process of its continuous anneali...
Example Embodiment
[0065] Example 3
[0066] Referring to FIG. 3, the process route of this embodiment is, raw material 1-uncoiling cleaning 2-electroplating 17 (electroplating Fe or Ni)-reheating 9-hot-dip galvanizing 18-alloying 19-final cooling 11-leveling 12-passivation ( or including oiling) and post-processing 20-finishing 13-oiling and post-processing 14-coiling 15-finished product 16.
[0067] The process of this embodiment uses high-strength or ultra-high-strength hot-rolled acid-washed sheets (such as hot-rolled high-strength steel) as raw materials, and by plating extremely thin layers of Ni, Fe and other elements on the surface, the hot-dip galvanizing of high-strength steel is improved. Then heat it to between 450 and 550 ° C, hot-dip galvanizing (or alloying with the coating) in a zinc pot, and then cool to enter the post-process such as leveling. Due to the short reheating galvanizing time (within one minute), the decomposition of the strengthening phase can be greatly reduced or...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap