Dynamic hot water reaction hard microporous fiber calcium silicate board and manufacturing method thereof

A calcium silicate board and fiber technology, applied in the field of lightweight boards, can solve problems such as poor weathering resistance, poor impact resistance, and non-moisture-proof gypsum boards, and achieve high hardness, strength, and good temperature resistance.

Inactive Publication Date: 2010-09-22
陈耀强
View PDF1 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The current board market is mainly wood plywood, gypsum board, glass magnesium board, calcium silicate board, cement fiber board, but the above-mentioned boards have different defects, such as: wood plywood is not fireproof, not moisture-proof, and contains toluene , formaldehyde and other harmful gases; gypsum boards are ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]The dynamic hot water reaction rigid microporous fiber calcium silicate plate provided by the present embodiment, its component comprises batching and water that weight ratio is 1: 4, and batching comprises the composition (molar ratio) of following proportioning: Diatomite 20 %, 20% of quartz powder, 5% of glass powder, 36% of lime, 4% of water glass, 2% of bentonite, 6% of 42.5# water, 4% of plant fiber and 3% of alkali-resistant glass fiber; among them, diatomite, quartz The fineness of powder and glass powder is less than 80 microns, the SiO content of diatomite is above 85%, the SiO content of quartz powder is above 92%, the SiO content of glass powder is above 98%, and the CaO content of lime is 62%. above. The product obtained by this ratio has excellent high temperature resistance under the premise of ensuring that other properties meet the general requirements.

Embodiment 2

[0037] The dynamic hot water reaction rigid microporous fiber calcium silicate board provided in this embodiment differs from that of Example 1 in that the molar ratio of the components of the ingredients is: 30% of diatomite, 10% of quartz powder, and 7% of glass powder. %, 35% lime, 5% sodium silicate, 2% bentonite, 5% 42.5# water, 4% plant fiber and 3% alkali-resistant glass fiber. The product obtained by this ratio has high temperature resistance and high flexural performance at the same time.

Embodiment 3

[0039] The dynamic hot water reaction rigid microporous fiber calcium silicate board provided in this embodiment differs from that of Example 1 in that the molar ratio of the components of the ingredients is: 10% diatomite, 30% quartz powder, and 5% glass powder. %, lime 35%, water glass 5%, Pengrun soil 2%, 42.5# water 6%, plant fiber 4% and alkali-resistant glass fiber 3%; the products obtained by this ratio ensure that other properties meet the general needs Under the premise, it has excellent high flexural performance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a dynamic hot water reaction hard microporous fiber calcium silicate board which is characterized in that a board body is obtained through a reaction of ingredients and water in the weight ratio of 1:4. The ingredients comprise the following components in proportion (molar ratio): 45-47 percent of siliceous material, 40-42 percent of calcareous material, 7 percent of fiber and 6-7 percent of reaction promoter, wherein the siliceous material is one or a mixture of diatomaceous earth, quartz powder, glass dust, opoka and river sand powder; the calcareous material is lime and/or cement; the fiber is one or a mixture of mineral fiber, vegetable fiber and polymer fiber; and the reaction promoter is water glass and/or bentonite. The ingredients which do not contain toluene, formaldehyde or radioactive substances are adopted to react with water in the invention, so that no harmful gas is produced. The finished product has fire prevention, moisture prevention, mold prevention, high tensile strength, high flexural strength and good temperature resistance, and is a multipurpose product suitable for internal walls, external walls and ground surfaces.

Description

Technical field [0001] The invention relates to a lightweight plate, specifically a dynamic hot water reaction hard microporous fiber calcium silicate that is safe, has high compressive resistance, high flexural resistance, and good weather resistance, and is applicable to various indoor and outdoor environments. Board; The present invention also relates to the manufacturing method of the dynamic hot water reaction hard microporous calcium silicate board. Background technique [0002] The current board market is mainly wood plywood, gypsum board, glass magnesium board, calcium silicate board, cement fiber board, but the above-mentioned boards have different defects, such as: wood plywood is not fireproof, not moisture-proof, and contains toluene , formaldehyde and other harmful gases; gypsum boards are not moisture-proof, have low flexural strength, and poor impact resistance; High-pressure production process, easy to delaminate, poor acid rain resistance, poor wind pressur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B28/10C04B14/44
CPCC04B2111/00025C04B2111/00318C04B2111/28C04B2111/27C04B2111/00068C04B28/186C04B2111/00094C04B2111/60C04B2111/2092Y02P40/60Y02W30/91C04B7/00C04B12/04C04B14/06C04B14/068C04B14/08C04B14/104C04B14/22C04B14/38C04B16/06C04B18/24C04B40/0082C04B40/024
Inventor 陈耀强
Owner 陈耀强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap