Nano aqueous interior wall heat insulation paint and preparation method thereof

A technology for thermal insulation coatings and interior walls, applied to radiation-absorbing coatings, coatings, etc., can solve problems such as reduction, easy segregation, and difficult dispersion of coatings, and achieve enhanced infrared radiation absorption performance, simple preparation process, and enhanced thermal insulation effect Effect

Inactive Publication Date: 2011-01-19
CHINA MCC17 GRP
View PDF8 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this coating can play a role in thermal insulation to a certain extent, it is difficult to meet the country's energy-saving requirements for buildings.
The invention patent with the publication number CN1986664A discloses a kind of insulating coating with hollow glass microspheres as additives, which can reduce the surface of various energy objects, reduce their surface temperature and internal temperature, thereby improving the working environment and achieving the purpose of saving energy and reducing consumption. , but the existing hollow glass microspheres have poor wettability with water, are difficult to disperse in the coating and are easy to segregate during storage. After coating, they are not firmly adhered to the base layer and have poor durability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] According to the components and contents (weight percentage) listed below, the interior wall insulation coating of the present invention is formulated:

[0028] Component parts by weight

[0029] Styrene acrylic emulsion 26

[0030] Nano calcium carbonate 25

[0031] Nano silica 4

[0032] Nano zinc oxide 2

[0033] Nano alumina 2

[0034] Nano titanium dioxide 2

[0035] 10% sodium hexametaphosphate aqueous solution 1

[0036] Tributyl phosphate 0.1

[0037] Ethylene glycol 1

[0038] 2% carboxymethyl cellulose aqueous solution 0.5

[0039] Water balance

Embodiment 2

[0041] According to the components and contents (weight percentage) listed below, the interior wall insulation coating of the present invention is formulated:

[0042] Component parts by weight

[0043] Pure acrylic emulsion 28

[0044] Nano calcium carbonate 22

[0045] Nano silica 2

[0046] Nano zinc oxide 4

[0047] Nano alumina 4

[0048] Nano titanium dioxide 2

[0049] 10% sodium hexametaphosphate aqueous solution 1.2

[0050] Tributyl phosphate 0.15

[0051] Ethylene glycol 1

[0052] 2% carboxymethyl cellulose aqueous solution 0.3

[0053] Water balance

Embodiment 3

[0055] According to the components and contents (weight percentage) listed below, the interior wall insulation coating of the present invention is formulated:

[0056] Acrylic vinegar emulsion 25

[0057] Nano calcium carbonate 24

[0058] Nano silica 2.0

[0059] Nano zinc oxide 3.0

[0060] Nano alumina 3.0

[0061] Nano titanium dioxide 2.0

[0062] 10% sodium hexametaphosphate aqueous solution 1.1

[0063] Tributyl phosphate 0.1

[0064] Ethylene glycol 1.0

[0065] 2% carboxymethyl cellulose aqueous solution 0.4

[0066] Water balance

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a nano aqueous interior wall heat insulation paint and a preparation method thereof, which belong to the technical field of production of aqueous paint. The nano aqueous interior wall heat insulation paint comprises the following components in percentage by weight: 20 to 35 percent of emulsion, 20 to 30 percent of nano calcium carbonate, 8 to 16 percent of nano oxide composition, 0.2 to 2 percent of thickening agent, 0.5 to 2 percent of wetting and dispersing agent, 0.1 to 0.5 percent of antifoaming agent, 0.5 to 2 percent of anti-freezing agent and the balance of water. The preparation process comprises the following steps of: uniformly stirring the water, the dispersing agent, glycol and half the antifoaming agent at a low speed, sequentially adding the nano calcium carbonate and the nano oxide composition with stirring; uniformly stirring the nano calcium carbonate and the nano oxide composition and uniformly dispersing the mixture by shearing the mixture on a multifunctional disperser at a high speed; slowly adding the emulsion dropwise at a low stirring speed; subsequently adding the remaining antifoaming agent and the thickening agent; and uniformly stirring and mixing the mixture at the low speed. The heat insulation paint of the invention comprises the water serving as a solvent, does not contain an organic solvent, and has the advantages of low VOC content, simple preparation process and wide application.

Description

Technical field [0001] The invention belongs to the technical field of production of water-based paints, and specifically relates to a nano-water-based interior wall thermal insulation paint and a preparation method thereof. Background technique [0002] In my country's energy consumption, building energy consumption accounts for about 35% of the national energy consumption. my country has issued a series of policies and regulations that require mandatory energy-saving measures for buildings. In building thermal insulation materials, building thermal insulation coatings are more and more favored by people due to their advantages such as convenient use, good thermal insulation effect and economic feasibility. Water-based building energy-saving coating, it is a green and environmentally friendly coating with low volatile organic compound (VOC) content, safe production and construction, non-flammable, no (or low) toxicity, and no (or low) odor, which is in line with the development...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D5/32C09D7/12
Inventor 金仁才尹万云张千峰裴立宅陈均陶新秀乔军
Owner CHINA MCC17 GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products