Road guardrail coating with width marking and warning function and preparation method thereof

A coating and functional technology, applied in the direction of anti-corrosion coatings, luminescent coatings, polyester coatings, etc., can solve the problems of poor vision, poor night vision, oxidation blackening, etc., to achieve obvious warning effect, good road width and warning effect Effect

Inactive Publication Date: 2011-01-19
上海朗琦土木工程技术有限公司 +1
View PDF3 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the vision at night is poor, especially the purely galvanized guardrail. After a period of use, it will o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The preparation method of the road guardrail paint with display width and warning function, it comprises the steps:

[0036] 1) The selection of raw materials: according to the percentage by weight of each raw material:

[0037] Acrylic 13%,

[0038] Rare Earth Calcium Silicate 5%,

[0039] Organic bentonite and calcium carbonate (15% each) 30%,

[0040] Chrome Yellow 0.1%,

[0041] Auxiliary 0.5%,

[0042] Xylene 29.4%,

[0043] 100 mesh glass beads 22%;

[0044] Among them, the additives are leveling agent, dispersant, defoamer, and antifungal agent, and the percentages by weight are: leveling agent 0.1%, dispersant 0.2%, defoamer 0.15%, and antifungal agent 0.05%;

[0045] Described leveling agent is Levaslip455,

[0046] Described dispersant is Tamol-SG-1,

[0047] Described defoamer is BYK-52,

[0048] The antifungal agent is BIT;

[0049] 2) First add the metered xylene to the reaction kettle, and then add the metered leveling agent, dispersant, defoamer...

Embodiment 2

[0052] The preparation method of the road guardrail paint with display width and warning function, it comprises the steps:

[0053] 1) The selection of raw materials: according to the percentage by weight of each raw material:

[0054] Polyester resin 27%,

[0055] Rare Earth Calcium Aluminate 12%,

[0056] Filler 10%,

[0057] Phthalocyanine blue 0.6%,

[0058] Auxiliary 2.5%,

[0059] Ethyl acetate 32.9%,

[0060] 150 mesh glass beads 15%;

[0061] Wherein, the filler is organic bentonite, calcium silicate and calcium carbonate, and the weight percentages are: calcium silicate 3%, calcium carbonate 4%, organic bentonite 3%;

[0062] Auxiliaries are leveling agent, dispersant, defoamer, thickener and antifungal agent, and the percentage by weight is: leveling agent 0.5%, dispersant 0.5%, defoamer 0.5%, thickener 0.5% , antifungal agent 0.5%,

[0063] Described leveling agent is Byketol-OK,

[0064] Described dispersant is Disper BYK-101,

[0065] The defoamer is BYK-5...

Embodiment 3

[0071] The preparation method of the road guardrail paint with display width and warning function, it comprises the steps:

[0072] 1) The selection of raw materials: according to the percentage by weight of each raw material:

[0073] Polyurethane modified acrylic resin 22.5%,

[0074] Long afterglow luminescent material (rare earth calcium aluminate and rare earth magnesium aluminate) 5.5%,

[0075] Filler (titanium dioxide, calcium carbonate, kaolin) 17%,

[0076] Auxiliary (leveling agent, dispersant, defoamer, thickener, antifungal agent) 1.5%,

[0077] Toluene 34.5%,

[0078] 200 mesh glass beads 19%;

[0079] Among them, the long-lasting luminescent material is composed of rare earth calcium aluminate and rare earth magnesium aluminate, and the weight percentage is: 3.5% of rare earth calcium aluminate, 2.0% of rare earth magnesium aluminate;

[0080] The filler is composed of titanium dioxide, calcium carbonate and kaolin, and the weight percentage is: titanium di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a coating for road safety facilities, in particular to the coating for a road safety guardrail. The road guardrail coating with width marking and warning function is characterized by consisting of a coating and micro glass beads, wherein the coating is prepared from raw materials including a high molecular polymer resin, a long-afterglow light emitting material, a filler, a pigment, an auxiliary agent and a solvent; and the road guardrail coating comprises 10 to 40 weight percent of high molecular polymer resin, 2 to 30 weight percent of long-afterglow light emitting material, 5 to 50 weight percent of filler, 0 to 5 weight percent of pigment, 0.1 to 5 weight percent of auxiliary agent, 10 to 40 weight percent of solvent and 1 to 30 weight percent of micro glass beads. The road guardrail coating has a rust-proof and corrosion resistant effect on the guardrail and has the effect of marking the width and warning for a road at night.

Description

technical field [0001] The invention relates to a coating for road safety facilities, in particular to a coating for road safety guardrails. Background technique [0002] Road guardrail is an important facility for maintaining highways and ensuring safety, and it plays a role in preventing cars from rolling over and rushing out of the road. Hot-dip galvanizing is now commonly used for protection. Different protection systems should be selected for different atmospheric environments: in rural areas and areas with less serious pollution, a separate hot-dip galvanized layer protection or a separate powder spraying protective guardrail is used; in heavy industrial areas or coastal areas, especially in areas with acid rain In areas, a double-coat protection system of hot-dip galvanized layer and paint should be adopted. The double-coat protection system is to coat the surface of the hot-dip galvanized layer to form a protective layer, which is usually called a double-coat syste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D163/00C09D133/00C09D131/04C09D167/00C09D115/02C09D5/22C09D5/33C09D5/08
Inventor 冯守中宋乐山辛国树刘为炎王军
Owner 上海朗琦土木工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap