High-temperature steam endurance ink for spraying code and printing

A technology of cooking ink and high temperature resistance, applied in the direction of ink, application, household appliances, etc., can solve the problems of fading, falling off, discoloration, etc., and achieve the effect of good adhesion and strong adhesion

Active Publication Date: 2011-03-23
北京赛腾标识系统股份公司
View PDF0 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, ordinary inks using solvent-based dyes as colorants have more or less deficiencies such as fading, discoloration, shedding, and penetration after high-temperature cooking, which cannot meet the current high-temperature cooking treatment requirements for inkjet inks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature steam endurance ink for spraying code and printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The present embodiment provides a kind of pigment slurry, and it has following composition (taking the gross weight of pigment slurry as 100%):

[0028] NeoCryl B-890 Acrylic Resin 32

[0029] SOLSPACE 28000 wetting and dispersing agent 8

[0030] MA100 carbon black 16

[0031] Butanone 40

[0032] Ethylene glycol butyl ether 4

[0033] Wherein, the Mw of the acrylic resin used is 12500, and the Tg is 85°C.

[0034] Preparation process: mix the above ingredients according to the proportion, and use a sand mill to grind 1mm glass beads until the particle size of the pigment is less than 1 micron to obtain the pigment slurry 1.

Embodiment 2

[0036] The present embodiment provides a kind of pigment slurry, and it has following composition (taking the gross weight of pigment slurry as 100%):

[0037] KC-101 aldehyde and ketone resin 32

[0038] IRGALITE Yellow B3RN 20

[0039] (C.I Pigment Yellow 83, Ciba Company)

[0040] BYK-161 wetting and dispersing additive 10

[0041] Butanone 34

[0042] Ethylene glycol butyl ether 4

[0043] Preparation process: mix the above ingredients according to the proportion, and use a sand mill to grind the pigment with 1 mm glass beads until the particle size of the pigment is less than 1 micron to obtain the pigment slurry II.

Embodiment 3

[0045] The present embodiment provides a kind of pigment slurry, and it has following composition (taking the gross weight of pigment slurry as 100%):

[0046] BL18 polyvinyl butyral resin 20

[0047] R930 titanium dioxide 20

[0048] BYK-110 wetting and dispersing additive 6

[0049] Butanone 30

[0050] N-methylpyrrolidone (N-methyl 2-pyrrolidone) 3

[0051] Ethanol 20

[0052] Lithium nitrate 1

[0053] Preparation process: mix the above-mentioned ingredients according to the proportion, and use a sand mill to grind the pigment with 1 mm glass beads until the particle size of the pigment is less than 1 micron, and obtain the pigment slurry 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
softening pointaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to high-temperature steam endurance ink for spraying code and printing, containing one or more organic solvents, resin and coloring agents. In addition, the consistency of the ink is 2.8-6.2CP / 25DEG C, the conductivity is 500-1,500muS and the surface tension is 27-30Dyn / cm. The high-temperature steam endurance ink for spraying code and printing can be applied to the surfaces of various packaged objects required to be treated at high temperature. The mark and the substrate adopting the high-temperature steam endurance ink have strong adhesive force and favorable adhesiveness and cannot fade, fall off, permeate and shift after being subjected to high-temperature digestion. The dried mark can be also scraped by a cleaning agent.

Description

technical field [0001] The invention relates to a high-temperature-resistant cooking ink for inkjet printing, which belongs to the high-temperature-resistant cooking printing ink for inkjet printers. Background technique [0002] Continuous inkjet printing system (CIJ) is a relatively complex inkjet system. Its biggest advantage is that it can achieve high-speed printing when printing numbers or letters. The ink used in this system is characterized by low viscosity and must be able to Chargeability and breakability. [0003] According to the printing substrate of the marking information and the use environment, there are also different requirements for the ink used. For example, in many food packaging products, after the packaging is sealed, it is necessary to print the identification information, and in order to sterilize and make the finished product, it needs to be cooked at high temperature. In the high-temperature cooking process, it is required that the printed infor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C09D11/14C09D11/08C09D11/322C09D11/324
Inventor 李旭东李昂陈洪霞
Owner 北京赛腾标识系统股份公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com