Magnesium-nickel-containing coating for marine climate-resistant preservative treatment

A marine climate and anti-corrosion treatment technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of environmental and human hazards, coatings containing hexavalent chromium, high curing temperature, etc., to achieve environmental friendliness, excellent corrosion resistance, and process temperature low effect

Active Publication Date: 2011-04-13
JIANGSU LINLONG NEW MATERIALS CO LTD
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this coating contains hexavalent chromium, which has certain pollution.
And due to the needs of passivation and bonding, 5%-10% chromic anhydride is generally added, and Cr6+ is highly toxic and carcinogenic, so it has serious harm to the environment and human body
In addition, the curing temperature of this coating is as high as 300°C, and the curing time is about 30 minutes, which consumes a lot of energy; it has low hardness and poor wear resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium-nickel-containing coating for marine climate-resistant preservative treatment
  • Magnesium-nickel-containing coating for marine climate-resistant preservative treatment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The invention provides a water-soluble aluminum-zinc-silicon coating for anticorrosion treatment of marine weather-resistant engineering parts, wherein the coating comprises aluminum-zinc-silicon alloy powder, an organic solvent, a nano-oxide particle reinforcing agent, deionized water, a binder, Corrosion inhibitor, dispersant and thickener.

[0025] Below, some preferred embodiments of the coating formulation proportioning of the present invention are given in conjunction with Table 1, but the content of each component of the present invention is not limited to the numerical value listed in this table, for those skilled in the art, completely Reasonable generalizations and inferences can be made on the basis of the numerical ranges listed in the tables.

[0026] Table 1 Coating formula ratio

[0027]

[0028] Wherein, the aluminum-zinc-silicon alloy powder is composed of Al, Zn, Si, Mg, and Ni. Below, some preferred examples of the mass percentages of the componen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a coating for marine climate-resistant engineering part preservative treatment, which comprises 30.0 to 50.0g of aluminum-zinc-silicone alloy powder, 10.0 to 25.0mL of organic solvent, 1.0 to 4.0g of nano-oxide particle reinforcing agent, 15.0 to 30.0mL of deionized water, 2.0 to 5.0g of adhesive, 1.0 to 3.0g of corrosion inhibitor, 0.1 to 2.0mL of a dispersing agent and 0.1 to 2.0g of thickening agent, wherein the aluminum-zinc-silicone alloy powder consists of aluminum, zinc, silicone, magnesium and nickel.

Description

technical field [0001] The invention relates to a water-soluble aluminum-zinc-silicon paint for anticorrosion treatment of marine climate-resistant engineering parts and a preparation method thereof. Background technique [0002] Offshore and marine engineering equipment is located in an environment with rainy, high temperature, salty fog and strong wind currents. According to the ISO9225 environmental evaluation standard, its service conditions are generally >C5 level, which belongs to the extremely harsh environment. The exposed parts will be subject to the combined effects of strong atmospheric corrosion, electrochemical corrosion and airflow erosion, and the service life of various steel structures is much lower than that of the general inland outdoor environment. For example, the wind power generation equipment in service under marine climate conditions is directly exposed to the extreme corrosive atmosphere due to the external components of the unit such as the nace...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/12C09D5/10
CPCC23F11/08C09D5/1656C09D5/084
Inventor 冯立新张敏燕缪强
Owner JIANGSU LINLONG NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap