Vinylacetate nonsoap emulsion, redispersible rubber powder and preparation methods thereof
A technology of redispersible rubber powder and vinyl acetate, which is applied in the field of vinyl acetate soap-free emulsions, can solve the problems of poor redispersibility of redispersible latex powder, high air content of mortar, and low bonding strength, etc., and achieves Improve the bonding performance, increase the tensile bond strength, and improve the effect of water resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1
[0031] (1) Preparation of vinyl acetate soap-free emulsion
[0032] The monomer composition is vinyl acetate, vinyl tertiary carbonate, n-butyl acrylate and methyl acrylate, and its component formula is as follows:
[0033]
[0034] First, add water, sodium bicarbonate, protective colloid and emulsifier to the polymerization kettle, adjust the stirring speed to 60r / min, heat to 80±2°C, and stir for 1 hour. Add 15% mixed monomers composed of vinyl acetate, vinyl tertiary carbonate, n-butyl acrylate and methyl acrylate and 20% potassium persulfate initiator solution to the reaction kettle, react for 30 minutes, and finally form a blue transparent Seed emulsion. Then add the remaining mixed monomer and initiator solution dropwise to control the dropping rate so that the reaction temperature is controlled at 80±2°C, the polymerization reaction time is 3 hours, and the maturation is continued for 1 hour. The temperature is lowered to 40°C, and the material is filtere...
Example Embodiment
[0040] Example 2:
[0041] (1) Preparation of vinyl acetate soap-free emulsion
[0042] The monomer composition is vinyl acetate, vinyl tertiary carbonate, n-butyl acrylate and methyl acrylate, and its component formula is as follows:
[0043]
[0044] First, add water, sodium bicarbonate, protective colloid and emulsifier to the polymerization kettle, adjust the stirring speed to 60r / min, heat to 70±2°C, and stir for 1 hour. Add 5% of the mixed monomer composed of vinyl acetate, vinyl tertiary carbonate, n-butyl acrylate and methyl acrylate and 10% potassium persulfate initiator solution to the reaction kettle, react for 1 hour, and finally form a blue transparent Seed emulsion. Then add the remaining mixed monomer and initiator solution dropwise to control the dropping rate so that the reaction temperature is controlled at 90±2°C, the polymerization reaction time is 4 hours, and the maturation is continued for 1 hour. The temperature is lowered to 60°C, and the material is filte...
Example Embodiment
[0050] Example 3:
[0051] (1) Preparation of vinyl acetate soap-free emulsion
[0052] The monomer composition is vinyl acetate, vinyl tertiary carbonate, n-butyl acrylate and methyl acrylate, and its component formula is as follows:
[0053]
[0054] First add water, sodium bicarbonate, protective colloid and emulsifier to the polymerization kettle, adjust the stirring speed to 60r / min, heat to 75±2°C, and stir for 1 hour. Add 10% mixed monomers composed of vinyl acetate, vinyl tertiary carbonate, n-butyl acrylate and methyl acrylate and 15% potassium persulfate initiator solution to the reactor, react for 45 minutes, and finally form a blue transparent Seed emulsion. Then add the remaining mixed monomer and initiator solution dropwise to control the dropping rate so that the reaction temperature is controlled at 85±2°C, the polymerization reaction time is 5 hours, and the maturation is continued for 1 hour. The temperature is lowered to 50°C, and the material is filtered out to...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap