Preparation method of catalytic combustion catalyst
A catalytic combustion and catalyst technology, which is applied in the direction of catalyst activation/preparation, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problems of complex preparation process, easy cracking of coating, large amount of additives, etc., and achieve the goal of preparation The process is simple, not easy to crack, and the effect of less additives
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029] Example 1
[0030] Pretreatment of the honeycomb ceramic substrate: the cordierite honeycomb ceramic substrate is hydrothermally treated at 40°C for 24 hours, and then dried at 100°C for 12 hours.
[0031] Aluminum sol preparation: add 25 g of pseudo-boehmite to 200 mL of deionized water, and add 10 g of concentrated nitric acid dropwise while stirring. After stirring for a certain period of time, heating to 80°C, adding nitric acid dropwise to completely peptize, controlling the pH value of the solution at 2-5, aging for 24 hours to obtain a transparent aluminum sol.
[0032] Coating loading: immerse the pretreated cordierite honeycomb ceramic carrier into the aluminum sol prepared above, take it out, blow off the remaining liquid, dry at 120°C for 6 hours, and fire at 500°C for 5 hours.
Example Embodiment
[0033] Example 2
[0034] Pretreatment of the honeycomb ceramic substrate: the cordierite honeycomb ceramic substrate is hydrothermally treated at 80°C for 6 hours, and then dried at 110°C for 6 hours.
[0035] Preparation of aluminum sol: the same as in Example 1.
[0036] Coating load: immerse the pretreated cordierite honeycomb ceramic carrier into the aluminum sol prepared above, take it out, blow off the remaining liquid, dry at 40°C for 12 hours, and fire at 600°C for 1 hour.
Example Embodiment
[0037] Example 3
[0038] Pretreatment of the honeycomb ceramic substrate: the cordierite honeycomb ceramic substrate is hydrothermally treated at 120°C for 4 hours, and then dried at 110°C for 10 hours.
[0039] Aluminum sol preparation: add 20 grams of pseudo-boehmite to 150 mL of deionized water, and add 8 grams of concentrated nitric acid dropwise while stirring. After stirring for a certain period of time, heating to 80°C, adding nitric acid dropwise to completely peptize the solution, controlling the pH value of the solution at 2-5, aging for 24 hours to obtain a transparent aluminum sol.
[0040] Coating loading: immerse the pretreated cordierite honeycomb ceramic carrier into the aluminum sol prepared above, take it out, blow off the residual liquid, dry at 100°C for 10 hours, and fire at 500°C for 5 hours.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap