Palm oil-base offset printing ink containing no mineral oil and preparation method thereof
A technology of oil-based glue and mineral oil, applied in the printing field, can solve the problems of no palm oil, etc., achieve low VOC content, good use safety, and expand the application range
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0034] Example 1
[0035] Use the following method to prepare palm oil-based offset printing ink without mineral oil:
[0036] (1) Take 20% palm oil, 20% methyl palmitate, 59% rosin-modified phenolic resin and 1% antioxidant BHT according to mass percentages and place them in the reactor, and heat up to 220℃ for one hour. , That is, the binder for offset printing ink is obtained.
[0037] (2) Take the pigment phthalocyanine blue BGS (dye index number CI Pigment Blue 15:3) 15%, the above-mentioned binder 60%, palm oil 10%, methyl palmitate 10%, and cobalt naphthenate 2.5% by mass percentage And 2.5% manganese naphthenate, uniformly blended.
[0038] After the ink is prepared, it is pre-dispersed by hand, rolled by a three-roll mill, added and retained oil, inspected and adjusted to obtain the finished ink.
[0039] The above desiccants cobalt naphthenate and manganese naphthenate are produced by Shanghai Changfeng Chemical Plant.
[0040] The technical indicators of the produced offset ...
Example Embodiment
[0043] Example 2
[0044] Use the following method to prepare palm oil-based offset printing ink without mineral oil:
[0045] (1) Take 25% palm oil, 25% ethyl palmitate, 50% rosin-modified phenolic resin according to mass percentage, put it in the reaction kettle, heat up to 220℃ and keep it for one hour to discharge the material to obtain the offset printing ink. material.
[0046] (2) Take 20% of the pigment carbon black, 65% of the above-mentioned binder, 5% of palm oil, 5% of ethyl palmitate, 2.5% of cobalt naphthenate and 2.5% of manganese naphthenate according to mass percentage, and the mixture is uniform.
[0047] After the ink is prepared, it is pre-dispersed by hand, rolled by a three-roll mill, added and retained oil, inspected and adjusted to obtain the finished ink.
[0048] The technical indicators of the produced offset printing ink are as follows:
[0049] project
Example Embodiment
[0050] Example 3
[0051] Use the following method to prepare palm oil-based offset printing ink without mineral oil:
[0052] (1) Preparation of binder: 10% by mass palm oil, 20.5% by mass isobutyl palmitate, 53% by mass rosin modified phenolic resin, 11% linseed oil, 5% alkyd The resin and 0.5% organoaluminum gelling agent AO-4 are placed in a reaction kettle, heated to 200-205°C for 0.5 hours and discharged to obtain a binder for offset printing ink.
[0053] (2) Preparation of ink: the mass percentage of 12% pigment titanium dioxide, the binder obtained in step (1) 50% mass percentage, palm oil 16%, ethyl palmitate 20%, cobalt naphthenate 1%, cycloalkane 1% manganese alkanoate, uniformly blended.
[0054] After the ink is prepared, it is pre-dispersed by hand, rolled by a three-roll mill, added and retained oil, inspected and adjusted to obtain the finished ink.
[0055] The composition of the alkyd resin is 20% coconut oil, 51% soybean oil, 17% benzoic acid, 11.8% pentaerythritol...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap