Film-coating production technology for nano zinc oxide

A nano-zinc oxide and production process technology, applied in the direction of zinc oxide/zinc hydroxide, nanotechnology, etc., can solve problems such as insufficient preparation methods, achieve stable nano-size and nano-material properties, mild and friendly reaction conditions, and grain development full effect

Active Publication Date: 2012-06-27
SHANOGUAN KAIHONG NANOMATERIAL
View PDF4 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0040] In summary, nano-zinc oxide has broad application prospects, but its conventional preparation methods are insufficient at present.
At the same

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Film-coating production technology for nano zinc oxide
  • Film-coating production technology for nano zinc oxide

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0067] Example 1

[0068] A planting film-type nano zinc oxide production process is characterized by including the following steps:

[0069] (1) Leaching: using ammonia and ammonium bicarbonate as the leaching solvent, leaching the zinc in the secondary zinc oxide into a zinc ammonia complex solution; this step

[0070] The main reaction formula is as follows:

[0071] ZnO+3NH 3 ·H 2 O+NH 4 HCO 3 =Zn(NH 3 ) 4 CO 3 +4H 2 O

[0072] The leaching is a two-stage type, which is carried out in two leaching tanks respectively. The filter residue after the first stage leaching is added to the second stage leaching tank under stirring and then leached, the second stage leaching filter residue is discarded, and the second stage The second leaching solution of the stage leaching is added to the first stage leaching tank as the leaching solvent, and the secondary zinc oxide is poured into the first leaching tank with stirring, the leaching first leaching solution enters the next step, and the cyc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a film-coating production technology for nano zinc oxide and belongs to the technical field of fine petrochemicals and chemicals. The technological process is that an alkali carbonic acid zinc film is coated uniformly on the surfaces of light calcium carbonate and inner pores thereof, subjected to decentralized processing, and then calcined and activated in a dynamic calcination furnace at the temperature of 400 to 500 DEG C, so as to prepare the nano zinc oxide. The nano zinc oxide prepared through the technology belongs to a low-zinc product (containing 24 to 30 percent zinc), has the advantages of stable nano size, stable nano material properties, completely developed crystal grains, small particle diameter, uniformity in distribution, low reunion degree, high activity and good dispersivity, and can be widely applied to rubber, tires, catalysis, magnetism, optics, electricity, chemistry, physics, biology and the like.

Description

technical field [0001] The invention relates to a production process of petrochemical and chemical fine chemicals, in particular to a production process of film-planting nano zinc oxide. Background technique [0002] Nano zinc oxide is a new type of fine inorganic chemical product with multiple functions and high added value. Its particle size is between 1-100 nanometers, also known as ultra-fine zinc oxide. Due to the miniaturization of crystal grains, the specific surface area increases sharply, and its surface electronic structure and crystal structure change, resulting in surface effects, volume effects, quantum size effects and macroscopic tunnel effects that macroscopic objects do not have, as well as high transparency and high dispersion. Features. Research in recent years has found that it has special properties and new uses that cannot be compared with general zinc oxide products in terms of catalysis, magnetism, light, electricity, chemistry, physics, biology, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G9/02B82Y40/00
Inventor 梁鹤贤陈升刘优强黄有余
Owner SHANOGUAN KAIHONG NANOMATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap