Silicone rubber composite rubber tube lined with polytetrafluoroethylene and manufacturing method thereof
A technology of polytetrafluoroethylene and composite rubber hose, which is applied in the direction of rubber layered products, laminated, layered products, etc., and can solve the problem of large thickness of polytetrafluoroethylene lined pipe, poor oil resistance, poor solvent resistance, and low sealing performance And other problems, to achieve the effect of improving the scope of use, low equipment cost, and perfect sealing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0019] Example 1
[0020] Attached below Figure 1-2 To describe in detail the silicone rubber composite hose of the present invention and its manufacturing process.
[0021] A manufacturing process of a silicone rubber composite hose with polytetrafluoroethylene as the inner lining layer, including the following steps: plasma treatment of the polytetrafluoroethylene film tape 2; winding the plasma-treated polytetrafluoroethylene film tape 2 in the The mold core 1 of the required size can be wound in different layers according to the needs; the glass tape 3 is wound on the outer layer of the PTFE film tape 2, and then heated and shaped. After the shaping is completed, the glass tape 3 is removed to form the PTFE inner Liner 4, evenly brush the surface of the tetrafluoroethylene lining tube 4 with sodium-naphthalene-tetrahydrofuran solution or directly soak in the sodium-naphthalene-tetrahydrofuran solution; clean the surface of the tetrafluoroethylene lining tube 4 with alcohol an...
Example Embodiment
[0030] Example 2
[0031] See figure 2 , A silicone rubber composite hose includes from the inside to the outside: a polytetrafluoroethylene lined tube 4; a first silicone rubber layer 5; a reinforcing layer 6; and a second silicone rubber layer 5. Preferably, the reinforcing layer 6 may preferably include polyester fiber cloth, glass cloth, or carbon fiber cloth.
[0032] Preferably, the silicone rubber composite hose can be manufactured through the following manufacturing process. Specifically, 1 first, put the PTFE film tape 2 in the plasma chamber, the pressure is 100pa, the oxygen flow is 10L / min and the power of 350W, and the plasma bombardment treatment is performed for 3 minutes; 2 the plasma treated PTFE film Tape 2 is wound on the mold core 1 of the required size, and can be wound in different layers according to the needs; 3 After winding, a layer of glass tape 3 is wound on the outer layer of the PTFE film tape 2, and then it can be placed in the oven for heating For...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap