Flame-retardant reinforced warping-resistance PBT/PTT (polybutylene terephthalate/polytrimethylene terephthalate) alloy material and preparation method thereof

A technology of alloy materials and warping, which is applied in the field of polymer composite materials, can solve the problems affecting the performance of PBT/PTT alloy materials, PTT is easy to warp and deform when heated, and the low tracking resistance index can solve the problem of high flame retardancy High CTI value, smooth surface without warping, good mechanical properties

Active Publication Date: 2015-03-25
HEFEI GENIUS NEW MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, PTT is easy to warp and deform when heated, and the surface of the low-temperature molded part is rough and has more floating fibers, and the tracking index (CTI) is lower than that of the PBT / PTT alloy material, which affects the performance of the PBT / PTT alloy material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant reinforced warping-resistance PBT/PTT (polybutylene terephthalate/polytrimethylene terephthalate) alloy material and preparation method thereof
  • Flame-retardant reinforced warping-resistance PBT/PTT (polybutylene terephthalate/polytrimethylene terephthalate) alloy material and preparation method thereof
  • Flame-retardant reinforced warping-resistance PBT/PTT (polybutylene terephthalate/polytrimethylene terephthalate) alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 6

[0042] A preparation method of flame-retardant reinforced warpage-resistant PBT / PTT alloy material includes the following steps:

[0043] Dry PBT and PTT at 130℃ for 3 hours by blowing air. The intrinsic viscosity of PBT is 0.7dL / g and the density is 1.30g / cm. 3 , PTT has a viscosity of 0.7dL / g and a density of 1.33g / cm 3 ; According to the weight ratio, weigh 30 parts by weight of dried PBT, 30 parts by weight of PTT, 0.3 parts by weight of lubricant silicone oil, 0.1 parts by weight of transesterification inhibitor triphenyl phosphite, 0.3 parts by weight of antioxidant 1010, and nucleating agent surlyn 8920 0.5 parts by weight, flame retardant decabromodiphenyl ether 5 parts by weight, flame retardant synergist sodium antimonate 1 part by weight, toughening agent AX89002 parts by weight, mica powder surface-treated with titanate coupling agent ( (The particle size is 800 mesh) 10 parts by weight are mixed uniformly in a high-speed mixer; the uniformly mixed materials are blende...

Embodiment 7

[0045] A preparation method of flame-retardant reinforced warpage-resistant PBT / PTT alloy material includes the following steps:

[0046] Dry PBT and PTT at 130℃ for 3 hours by blowing air, the intrinsic viscosity of PBT is 1.3dL / g, and the density is 1.35g / cm 3 , PTT has a viscosity of 1.0dL / g and a density of 1.37g / cm 3 ; According to the weight ratio, weigh 40 parts by weight of dried PBT, 10 parts by weight of PTT, 1 part by weight of white wax oil as lubricant, 0.8 parts by weight of disodium hydrogen phosphate, transesterification inhibitor, 1680.8 parts by weight of antioxidant, and nucleating agent Aclyn 2855 Parts by weight, flame retardant brominated epoxy resin 10 parts by weight, flame retardant synergist antimony oxide 5 parts by weight, toughening agent AX8900 10 parts by weight, mica powder surface-treated by silane coupling agent (particle size is 600 mesh ) 30 parts by weight are uniformly mixed in a high-speed mixer; the uniformly mixed materials are blended with...

Embodiment 8

[0048] A preparation method of flame-retardant reinforced warpage-resistant PBT / PTT alloy material includes the following steps:

[0049] Dry PBT and PTT at 130℃ for 3 hours by blowing air. The intrinsic viscosity of PBT is 1.2dL / g and the density is 1.31g / cm. 3 , PTT has a viscosity of 0.8dL / g and a density of 1.36g / cm 3 ; According to the weight ratio, weigh 32 parts by weight of dried PBT, 22 parts by weight of PTT, 0.3 parts by weight of lubricant silicone oil, 0.2 parts by weight of white wax oil, 0.2 parts by weight of transesterification inhibitor triphenyl phosphite, and 0.2 parts by weight of disodium hydrogen phosphate Parts, antioxidant 10100.2 parts by weight, antioxidant 1680.3 parts by weight, ionomer nucleating agent 2.5 parts by weight, flame retardant decabromodiphenyl ether 5 parts by weight, brominated epoxy resin 3 parts by weight, flame retardant association 1 part by weight of sodium antimonate, 1 part by weight of antimony oxide, 7 parts by weight of toughen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flame-retardant reinforced warping-resistance PBT / PTT (polybutylene terephthalate / polytrimethylene terephthalate) alloy material, which comprises the following components in parts by weight: 30-40 parts of PBT, 10-30 parts of PTT, 0.3-1 part of lubricating agent, 0.1-0.8 part of ester exchange inhibitor, 0.3-0.8 part of antioxidant, 0.5-5 parts of nucleating agent, 5-10 parts of flame retardant, 1-5 parts of flame-retardant synergist, 2-10 parts of toughening agent, 0-30 parts of glass fiber and 10-30 parts of mineral powder. According to the invention, the PBT and the PTT are blended to be made into the alloy material, and the flame-retardant reinforced warping-resistance PBT / PTT alloy material has the advantage of low cost, solves the problem that high fire resistance and high CTI (comparative tracking index) value as well as high mechanical property of the PBT / PTT alloy material are difficult to coexist and has the characteristics of strong warping resistance and heat resistance. The flame-retardant reinforced warping-resistance PBT / PTT alloy material has good mechanical property, high flame retardance and high CTI value; and a product made of the flame-retardant reinforced warping-resistance PBT / PTT alloy material is smooth in smooth and free of warping.

Description

Technical field [0001] The invention relates to a polymer composite material, in particular to a flame-retardant reinforced warpage-resistant PBT / PTT alloy material and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PBT) is one of the toughest engineering thermoplastic materials. It is a semi-crystalline material with very good chemical stability, mechanical strength, electrical insulation properties and thermal stability. Polytrimethylene terephthalate (PTT) is a newly developed electrode after polyethylene terephthalate (PET) in the 1950s and polybutylene terephthalate (PBT) in the 1970s. A promising new type of polyester polymer material has the advantages of good mechanical properties, good elasticity, abrasion resistance, insulation, and low water absorption. And because of the breakthrough in the industrial synthesis method of 1,3-propanediol, the raw material for the synthesis of PTT in recent years, the large-scale production of P...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08K13/06C08K9/06C08K7/14C08K9/04C08K3/34C08K5/526C08K3/32B29B9/06B29C47/92B29C48/92
CPCB29C47/92B29C48/04B29C48/92B29C2948/92704B29C2948/92895
Inventor 费彬
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap