An adsorption material, plant-based technology, applied in the field of plant-based adsorption materials, can solve the problems of hindering the adsorption performance of materials, waste of resources, lack of adsorption capacity, etc., and achieve the effect of promoting the formation and development, avoiding waste of resources and reducing environmental pollution.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] Use a pomelo peeler to first peel off the oil bubble layer of the pomelo peel in Shatian grapefruit, and then cut off the remaining part of the pomelo peel to obtain a white, spongy pomelo sac; the pomelo sac is scalded with alkaline water, and the process conditions are: NaOH solution concentration 30%, the weight ratio of pomelo skin and solution is 1:5, the treatment temperature is 60°C, the treatment time is 3h, scald with alkaline water (the process is: the concentration of NaOH solution is 10%, the weight ratio of grapefruit skin and NaOH solution is 1:4 , the treatment temperature is 60°C, the treatment time is 2), and then washed with water until neutral, then centrifuged at 3000 rpm for 10 minutes to remove most of the water, then dried at 80°C until the water content is less than 10%, and crushed to particle size The size is 300-500 μm, weighed and packaged to obtain the plant-type adsorption material 1.
Embodiment 2
[0025] Use a pomelo peeler to first peel off the oil bubble layer of the honey pomelo pomelo peel, and then cut off the remaining part of the pomelo peel to obtain a white, spongy pomelo sac; the pomelo sac is scalded with alkaline water, and the process conditions are: NaOH solution concentration 20%, the weight ratio of pomelo peel and solution is 1:4, the treatment temperature is 80°C, and the treatment time is 3h. : 8, the treatment temperature is 90°C, and the treatment time is 4h) and then washed with water until neutral, then centrifuged at 4000 rpm for 5 minutes to remove most of the water, then dried at 70°C until the water content is less than 12%, and crushed to granules The diameter is 500~800μm, evenly spray preservative sodium benzoate (the dosage is 2‰ of the dry weight of pomelo sac granules) and rose essence (the dosage is 0.1‰ of the dry weight of pomelo sac granules), weigh and pack to obtain plant-type adsorption Material 2.
Embodiment 3
[0027] Use a pomelo peeler to first peel off the oil bubble layer of the pomelo pomelo peel, and then cut off the remaining part of the pomelo peel to obtain a white, spongy pomelo sac; the pomelo sac is scalded with alkaline water, and the process conditions are: NaOH solution concentration 10%, the weight ratio of pomelo skin and solution is 1:8, the treatment temperature is 70°C, the treatment time is 4h, scalding with alkaline water (the process conditions are: the concentration of NaOH solution is 20%, the weight ratio of grapefruit skin and NaOH solution is 1: 6. The treatment temperature is 70°C, the treatment time is 3h), and then washed with water until neutral, then centrifuged at 3000 rpm for 10 minutes to remove most of the water, then dried at 80°C until the water content is less than 8%, and crushed to granules The diameter is 400-600 μm, and the preservative potassium sorbate is evenly sprayed (the dosage is 2‰ of the dry weight of pomelo sac particles), weighed ...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com