Novel bamboo fiber/polypropylene composite material and method for preparing same
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A composite material, bamboo fiber technology, applied in the field of polypropylene materials, can solve problems such as difficulties, and achieve the effects of increasing flow rate, reducing melt viscosity, and improving rigidity
Inactive Publication Date: 2012-07-11
苏州晋圣博高分子材料科技有限公司
View PDF4 Cites 18 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] In the prior art, there is a composite material that uses bamboo fiber and additives to modify polypropylene. The invention patent 201010217542.6 (publication number CN101880423A, published on November 10, 2010) was applied by East China University of Science and Technology on June 30, 2010. Japan) disclosed a bamboo fiber/polypropylene composite materia...
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0033] Get the raw material of following parts by weight:
[0034]
[0035]
[0036] Concrete preparation method carries out as follows:
[0037] 1. Surface treatment of bamboo fiber: Put the bamboo fiber into a high-speed mixer at 110°C and stir for 50 minutes. After the bamboo fiber is fully dried, cool it to 60°C, then add titanate coupling agent, and heat it at 70°C. Under the temperature condition, carry out the stirring treatment of 3 minutes;
[0038] 2. Put the above-mentioned treated bamboo fiber, homopolypropylene, maleic anhydride grafted PP, antioxidant 1010, antioxidant 168, lubricant and molecular weight regulator into a high-speed mixer and mix evenly, then add to Extruding and granulating in a twin-screw extruder is the novel bamboo fiber / polypropylene composite material, wherein the twin-screw extruder is a parallel meshing twin-screw extruder with a length-to-diameter ratio of 40-40. 48. The barrel is equipped with 6 to 9 heating units and 1 to 2 ex...
Embodiment 2
[0040] Get the raw material of following parts by weight:
[0041]
[0042] Concrete preparation method carries out as follows:
[0043] 1. Surface treatment of bamboo fiber: Put the bamboo fiber into a high-speed mixer at 100°C and stir for 60 minutes. After the bamboo fiber is fully dried, cool it to 65°C, then add titanate coupling agent, and heat it at 80°C. Under the temperature condition, carry out the stirring treatment of 5 minutes; Others are the same as embodiment 1.
Embodiment 3
[0045] Get the raw material of following parts by weight:
[0046]
[0047] Concrete preparation method carries out as follows:
[0048] 1. Surface treatment of bamboo fiber: Put the bamboo fiber into a high-speed mixer at 120°C and stir for 40 minutes. After the bamboo fiber is fully dried, cool it to 70°C, then add titanate coupling agent, and heat it at 75°C. Under the temperature condition, carry out the stirring treatment of 6 minutes; Others are the same as embodiment 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a novel bamboo fiber/polypropylene composite material and a method for preparing the novel bamboo fiber/polypropylene composite material. The novel bamboo fiber/polypropylene composite material is prepared by treating the surface of bamboo fiber, adding a graft, an antioxidant, a lubricant and a molecular weight regulator into homopolymerized polypropylene as a substrate, and fully mixing according to proportion. The surface of the bamboo fiber is treated, thus the compatibility of the bamboo fiber and the polypropylene is improved, and the novel bamboo fiber/polypropylene composite material has excellent mechanical properties. In addition, the plasticizing properties of the polypropylene is improved, the melt viscosity is reduced, the flowability is improved, the compatibility and dispersibility of components of a system are effectively improved, and the interfacial adhesion of the material system is improved. Moreover, the aging resistance and the processing performance of the product are also improved, the polypropylene has thermal stability, and the rigidity of the polypropylene is greatly enhanced. Due to the addition of the lubricant and the molecular weight regulator, the flowability and the flow rate of the novel bamboo fiber/polypropylene composite material are improved. The novel bamboo fiber/polypropylene composite material is suitable for the process for extruding plastics into sheets, plates and pipes and also suitable for the process for injecting and molding small house appliance shells and bases.
Description
technical field [0001] The invention relates to the field of polypropylene materials, in particular to a novel bamboo fiber / polypropylene composite material and a preparation method thereof. Background technique [0002] Polypropylene is a large category of general-purpose materials. Due to its large shrinkage rate during thermal processing, aging due to the influence of light, heat, oxygen and climate during processing and use, and poor cold resistance, its use is limited. Bamboo fiber has unique antibacterial, deodorant properties and excellent coloring, wear resistance, resilience and electrical insulation, and has the advantages of easy processing and low cost. Wood-plastic composite material is a new type of composite material that has been booming at home and abroad in recent years. It refers to the use of polyethylene, polypropylene and polyvinyl chloride instead of the usual resin adhesive, and more than 50% of wood powder, rice husk, straw, etc. Waste plant fibers ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.