Silicon rubber with excellent electric arc resistant performance and preparation method thereof

An arc resistance and silicone rubber technology, applied in rubber insulators, organic insulators, etc., can solve the problem that arc resistance cannot meet the requirements, and achieve the effect of avoiding harm to human health and improving dispersion.

Inactive Publication Date: 2012-07-18
XI AN JIAOTONG UNIV
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although silicone rubber itself has certain corona resistance and arc resistance, in the case of arc ablation, its own arc resistance is far from meeting the requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicon rubber with excellent electric arc resistant performance and preparation method thereof
  • Silicon rubber with excellent electric arc resistant performance and preparation method thereof
  • Silicon rubber with excellent electric arc resistant performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1) Take 100 parts by mass (relative to 100 parts of silicone rubber) of nano-ATH and nano-BN particles for surface treatment: take 250 parts of ethanol and pour it into a beaker, add 10 parts of silane coupling agent to the ethanol, and then add 0.5 parts of acetic acid and 2.4 parts of water, adjust the pH value of the solution to 4~5, stir with a high-speed mixer (10min) to fully hydrolyze the silane coupling agent, and obtain solution A; add ATH and BN particles into solution A, and stir with a high-speed mixer (20min), obtain emulsion B;

[0032] 2) Emulsion blending of emulsion B and silicone rubber raw rubber: take 100 parts by mass of silicone rubber raw rubber and place it in a double-roller rubber mixing machine, add emulsion B after wrapping the rolls, and obtain silicone rubber raw rubber and inorganic particle emulsion The blend, and then heat the roller to volatilize all the ethanol in the blend;

[0033] 3) Add other additives: After the roller temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides silicon rubber with excellent electric arc resistant performance and a preparation method thereof. The silicon rubber comprises the following raw materials in parts by weight: 100 parts of crude silicon rubber, 50-200 parts of ATH (Aluminum Hydroxide), 25-100 parts of BN (Boron Nitride), 0.5-3.5 parts of vulcanizer, 1-3 parts of TAIC (Triallyisocyanurate), 1-5 parts of hydroxyl silicone oil, 1-5 parts of silane coupling agent and 100 parts of inorganic filler, wherein the inorganic filler is composed of the ATH and the BN. According to the silicon rubber provided by theinvention, an emulsion and the crude silicon rubber is directly subjected to emulsion blending on a double roller rubber mixing mill, thereby improving the dispersion and avoiding rising of nano-particles; by adding the BN on the basis of filling the ATH, the silicon rubber has less mass loss after high-voltage low current arc resistance test; meanwhile, the electric arc is always disassociated on the surface of the material in the electric arc ablation process; furthermore, the surface of the material has no burning phenomenon; the surface of the material only appears little yellowing after the test; and little black residue appears near an electrode.

Description

【Technical field】 [0001] The invention belongs to the field of electrical insulating polymer materials, in particular to a silicone rubber and a preparation method thereof. 【Background technique】 [0002] Silicone rubber materials have excellent comprehensive properties and are widely used in the field of electrical insulation, and have shown a rising trend in recent years. Since the main chain of silicone rubber is composed of silicon-oxygen bonds, silicon-oxygen bonds have greater bond energy than C-C bonds, and the Si element itself is not flammable, so silicone rubber has very good properties, such as its heat resistance, cold resistance Resistance, ozone aging resistance, weather resistance and good electrical insulation properties, as well as corona resistance and arc resistance. At the same time, silicone rubber also has a very wide temperature range, from -50°C to 300°C, which determines that silicone rubber is a very good electrical insulating material. [0003] A...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L83/06C08K13/06C08K3/22C08K3/38H01B3/28
Inventor 李建英雷璟李欣李盛涛
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products