Laser quenching coating and method for machining corrugated roller by using same
A technology of laser quenching and corrugated rollers, which is applied in coatings, manufacturing tools, heat treatment equipment, etc., can solve the problems of large internal stress of tile rollers, tooth loss of tile rollers, poor wear resistance, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] Laser quenching coating, by weight: 30 parts of SiC, Cr 2 o 3 12 parts, 40 parts of bentonite, 8 parts of rosin, 250 parts of alcohol. Dissolve rosin in an appropriate amount of alcohol solution. The amount of alcohol is generally 10%-15% of the total amount. SiC, Cr 2 o 3 1. Bentonite is processed into powder, and its particle size should be below 2 microns, and it is put into a mixer, and the dissolved rosin solution is added, and then the remaining alcohol is added and stirred evenly to obtain a laser quenching coating.
Embodiment 2
[0025] Laser quenching coating, by weight: 45 parts of SiC, Cr 2 o 3 7 parts, 30 parts of bentonite, 10 parts of rosin, 200 parts of alcohol. Dissolve rosin in an appropriate amount of alcohol solution. The amount of alcohol is generally 10%-15% of the total amount. SiC, Cr 2 o 3 1. Bentonite is processed into powder, and its particle size should be below 2 microns, and it is put into a mixer, and the dissolved rosin solution is added, and then the remaining alcohol is added and stirred evenly to obtain a laser quenching coating.
Embodiment 3
[0027] Laser quenching coating, by weight: 60 parts of SiC, Cr 2 o 3 10 parts, 50 parts of bentonite, 6 parts of rosin, 300 parts of alcohol. Dissolve rosin in an appropriate amount of alcohol solution. The amount of alcohol is generally 10%-15% of the total amount. SiC, Cr 2 o 3 1. Bentonite is processed into powder, and its particle size should be below 2 microns, and it is put into a mixer, and the dissolved rosin solution is added, and then the remaining alcohol is added and stirred evenly to obtain a laser quenching coating.
PUM

Abstract
Description
Claims
Application Information

- Generate Ideas
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com