A hot-melt adhesive, high-speed heating technology, applied in the direction of adhesives, epoxy resin adhesives, adhesive types, etc. The effect of strong relay, fast production speed and small equipment investment

Inactive Publication Date: 2012-09-05
成都鑫三洋科技发展有限公司
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing hot-melt adhesives for cables have weak adhesion, high melt viscosity, large equipment investment, and slow production speed, which cannot meet the needs of bonding cables.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] According to one embodiment of the present invention, the hot-melt adhesive is formed by mixing the following materials in parts by mass, 5 parts of EVA; 2 parts of rosin resin; 2 parts of wax; 3 parts of low-molecular polyolefin; 0.5 part of phenolic antioxidant; 0.5 parts of DCHP; the EVA contains 30% vinyl acetate monomer; the softening point of the rosin resin is 100° C.; the wax is a microcrystalline wax with a molecular weight of 3000 and a melting point of 65° C.

[0022] According to one embodiment of the present invention, it is formed by mixing the following materials in parts by mass, 8 parts of EVA; 4 parts of rosin resin; 4 parts of wax; 4 parts of low molecular polyolefin; 1.5 parts of phenolic antioxidant; 1.5 parts of DCHP; The EVA contains 35% vinyl acetate monomer; the rosin resin has a temperature of 110°C; the wax is a microcrystalline wax with a molecular weight of 4000 and a melting point of 85°C.

[0023] According to one embodiment of the present...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
softening pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing hot melt adhesive. The method comprises the steps of: mixing EVA (ethylene-vinyl acetate), a tackifier and a diluent according to parts by weight, and then heating, stirring, smelting and cooling the mixture. The hot melt adhesive comprises 5-10 parts of EVA, 2-6 parts of a tackifier, 5-10 parts of a diluent, 0.5-1.5 parts of an antioxidant and 0.5-1.5 parts of a plasticizer; the tackifier is one of abietic resin, petroleum resin, terpene resin, phenolic resin and epoxy resin; the diluent is one or two of wax and micro-molecular polyolefin; and the antioxidant is a phenolic antioxidant; and the plasticizer is DCHP (dicyclohexylphthalate). The stirring speed is 200-750 rpm; the heating temperature is 200-400 DEG C; and the cooling temperature is 10-25 DEG C.

Description

technical field [0001] The embodiment of the invention relates to a hot melt adhesive and a preparation method thereof. Background technique [0002] Hot-melt adhesive is a kind of plastic adhesive. Its physical state changes with temperature within a certain temperature range, but its chemical properties remain unchanged. It is non-toxic and tasteless. It is an environmentally friendly chemical product. Hot-melt adhesives have been used in many domestic industries. Wide application, the cable manufacturing industry also uses hot-melt tape or hot-melt adhesive film to wrap around the parts of the cables that need to be bonded, and melts after heating to play the role of bonding. The existing hot-melt adhesives for cables have weak bonding force, high melt viscosity, large equipment investment, and slow production speed, which cannot meet the needs of bonding cables. Contents of the invention [0003] The present invention aims to solve the above-mentioned defects of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J193/04C09J157/02C09J145/00C09J161/06C09J163/00C09J11/06
Inventor 曾维松
Owner 成都鑫三洋科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap