Semi-inorganic environment-friendly insulating paint for non-oriented silicon steel and coating preparation method thereof
A technology of oriented silicon steel and insulating coatings, applied in the direction of coatings, etc., can solve the problems of poor corrosion resistance of coatings, reduce free phosphate content, etc., and achieve low cost, significant high temperature resistance and corrosion resistance, and good insulation. Effect
Inactive Publication Date: 2013-04-03
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF3 Cites 20 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0006] The purpose of the present invention is to overcome the shortcomings of the appeal, to provide a high temperature resistant cold-rolled non-oriented silicon steel insulation coating and coating preparation method thereof, the coating does not contain chromate harmful to the human body and the environment, and to ensure better In the case of interlayer resistivity, the content of free phosphate is reduced, and the problem of poor corrosion resistance of the coating is solved by its interaction with boric acid and water-based epoxy resin
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0034] The resin described in Example 1 is a silicone resin; the organic solvent is ethylene glycol; the other additives are leveling agents.
Embodiment 2
[0035] The resin described in Example 2 is a silicone resin; the organic solvent is glycerol; the other auxiliary agents are wetting agents.
Embodiment 3
[0036] Resin described in embodiment 3 is epoxy resin; Described organic solvent is the mixture of diethylene glycol monobutyl ether, glycerol; Described other auxiliary agent is wetting agent, leveling agent, defoamer agent.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Login to view more
Abstract
The invention discloses a semi-inorganic environment-friendly insulating paint for non-oriented silicon steel and a coating preparation method thereof, and belongs to the technical field of non-oriented silicon steel paint. The semi-inorganic environment-protecting insulating paint for the non-oriented silicon steel is prepared by the following components by mass percent: 5-40% of aluminum dihydrogen phosphate, 0.5-10% of manganese dihydrogen phosphate, 1-12% of zinc dihydrogen phosphate, 0.5-1.5% of zinc oxide, 0.1-1% of magnesium oxide, 1.0-7% of boric acid, 5.0-27% of resin, 2.0-6.0% of organic solvent, 0.1-0.8% of other auxiliaries, and the balance of water. The paint is an environment-friendly paint free from chromium; at the same time, the coating is uniform in brightness, better in corrosion resistance than the ordinary phosphate coating, and good in insulation, adhesiveness, punching, weldability, heat resistance and corrosion resistance. In addition, the source of the semi-inorganic environment-friendly insulating paint for the non-oriented silicon steel is rich, so that the production cost is low, and the paint can be widely applied.
Description
[0001] technical field [0002] The invention belongs to the technical field of silicon steel coatings, and in particular relates to an environmentally friendly insulating coating for non-oriented silicon steel and a preparation method of the coating. Background technique [0003] Electrical steel is a ferrosilicon soft magnetic alloy with extremely low carbon content, which is mainly used in the manufacture of motors, generators, transformer cores and various telecommunications equipment. At present, electrical steel coatings are divided into three categories: all-inorganic coatings, semi-inorganic coatings and organic coatings. The general development trend is: all organic coatings are gradually eliminated, and inorganic coatings will gradually replace semi-inorganic coatings. However, due to the nature of the inorganic coating itself and the constraints of various conditions, at present, the international electrical steel manufacturers usually use more semi-inorganic coa...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/12C09D5/25
Inventor 何建平孙新王涛薛海荣郭云霞汤静郭虎刘明珠张晓雪
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap