Composite anti-freezing emulsified asphalt and preparation method thereof

A technology of emulsified asphalt and frost resistance, which is applied in the direction of building components, building insulation materials, buildings, etc. It can solve the problems of long-term storage stability, poor adhesion of mixture, and deterioration of asphalt adhesion. , to achieve the effect of improving long-term storage, reducing the remaining amount on the sieve, and enhancing stability

Active Publication Date: 2013-04-24
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can also be seen from the Marshall stability data in its examples that the cohesiveness of the mixture is not good, so the stability is small
[0004] CN101148544A discloses a kind of asphalt emulsion for cold pouring and its preparation method. A small amount of solvent oil is used in this asphalt emulsion. Although the amount of diesel oil or kerosene is l

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Take 6400g of Liaohe crude oil straight-run asphalt with a penetration of 148 (1 / 10 mm), heat it to 115°C for later use; take 1 g of carboxymethyl cellulose, slowly add it to 110 g of isopropanol while stirring, and stir thoroughly Evenly, after it is completely dissolved, take 10 g of the zwitterionic surfactant N-cocoyl-β-alanine sodium, slowly add it to the above-mentioned isopropanol, stir well, and make a paste for later use; take Cationic surfactant cetyltrimethylammonium chloride 30g, anionic surfactant fatty (18) alcohol polyoxyethylene (3) sodium ether sulfate 20 g, nonionic surfactant oleyl alcohol polyoxyethylene (20) Dissolve 1g of ether together in 3428g of water to fully dissolve the surfactant to prepare a soap solution for later use, and keep the temperature at 42°C. Then the above-mentioned hot asphalt, paste, and soap liquid are transported to the colloid mill respectively, and after being uniformly dispersed and ground by the colloid mill, it becomes ...

Embodiment 2

[0036] Take 6000g of Oman crude oil solvent deoiled bitumen from Maoming Petrochemical Company with a penetration of 98 (1 / 10 mm), heat it to 125°C for later use; take 50g of ethanol and 150g of tert-butanol, mix well, and take 5g of carboxyethyl Cellulose is slowly added to the above-mentioned mixed alcohol solution while stirring, fully stirred evenly, after it is completely dissolved, take 1g of the zwitterionic surfactant N-lauryl-β-alanine, and slowly add it to the above-mentioned alcohol, Stir evenly to make a paste for later use; take 90 g of cationic surfactant octadecyltrimethylammonium chloride, 1 g of anionic surfactant fatty (18) amine polyoxyethylene (4) sodium sulfate, non Dissolve 30 g of ionic surfactant octylphenol polyoxyethylene (20) ether in 3673 g of water to fully dissolve the surfactant to prepare a soap solution, and keep the temperature at 50°C for later use. Then the above-mentioned hot asphalt, paste, and soap liquid are transported to the colloid mi...

Embodiment 3

[0038] Take 4200g of Kuwait crude oil oxidized asphalt from Qilu Petrochemical Company with a penetration of 56 (1 / 10 mm), and heat it to 155°C for later use; take 3g of hydroxyethyl cellulose, slowly add it to 480g of propanol while stirring, and stir thoroughly Evenly, after it is completely dissolved, take 50g of the zwitterionic surfactant N-tallowyl-β-iminodipropionate disodium, slowly add it to the above alcohol solution, stir evenly, and make a paste for later use; Cationic surfactant octadecyltrimethylbenzyl ammonium chloride 370g, anionic surfactant sodium lauryl sulfate 67g, nonionic surfactant lauryl polyoxyethylene (20) ether 70g, dissolved In 4760g of water, fully dissolve the surfactant to prepare a soap solution, and keep the temperature at 55°C for later use. Then the above-mentioned hot asphalt, paste, and soap liquid are transported to the colloid mill, and after being uniformly dispersed and ground by the colloid mill, it becomes an oil-in-water emulsion. T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite anti-freezing emulsified asphalt and a preparation method thereof. A formula of the emulsified asphalt comprises asphalt, a cationic surfactant, an anionic surfactant, a zwitterionic surfactant, alcohol, cellulose and water. The preparation method comprises steps of: preparing cellulose, alcohol and the zwitterionic surfactant into a paste at room temperature; and preparing the cationic surfactant into a liquid soap; and uniformly dispersing hot asphalt, the paste and liquid soap by colloid mill to obtain the anti-freezing emulsified asphalt. The emulsified asphalt not only has good freezing resistance, good long-term storage performance and small sieve residual amount, but also avoids irritant odor caused by heated volatile alcohols in the preparation of soap liquid through single usage of alcohol and production process of emulsified asphalt.

Description

technical field [0001] The invention relates to an emulsified asphalt and a preparation method thereof, in particular to a composite long-term storage-stable frost-resistant emulsified asphalt and a preparation method thereof. The emulsified asphalt of the invention can be used for road maintenance and repair. Background technique [0002] In the process of road maintenance and repair, emulsified asphalt is one of the commonly used materials. Compared with hot asphalt, it has the advantages of energy saving, convenient use, and environmental protection. However, the emulsified asphalt used in the past has the disadvantage of poor frost resistance, and it is easy to break the emulsification due to freezing during winter storage, so that it cannot continue to be used. In addition, the pavement paved with emulsified asphalt is prone to low-temperature shrinkage cracking or freeze-thaw loosening in winter, which is also caused by the poor frost resistance of the emulsified asph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08J3/09C08J3/03C04B26/26
Inventor 陈保莲张静范思远陈闯
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap