Zirconium oxide modified novel high temperature resistant ceramic car disc brake pad and preparation method thereof

A technology of high-temperature-resistant ceramics and disc brakes, applied in the field of disc brake pads, can solve problems such as environmental pollution and human health hazards, and achieve the effects of high carbon content, extended service life, and high bonding strength

Active Publication Date: 2013-10-02
武汉市祥龙摩擦材料有限责任公司
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a new type of zirconia-modified high-temperature-resistant ceramic car disc brake pad and its preparation method. Excessive chemical content, asbestos floating dust,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconium oxide modified novel high temperature resistant ceramic car disc brake pad and preparation method thereof
  • Zirconium oxide modified novel high temperature resistant ceramic car disc brake pad and preparation method thereof
  • Zirconium oxide modified novel high temperature resistant ceramic car disc brake pad and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1, a method for manufacturing a new high-temperature-resistant ceramic car disc brake pad modified by zirconia, the specific steps are as follows:

[0035] (1) Prepare the following fabric materials in parts by weight: 25 parts of barium sulfate, 7 parts of copper fiber, 10 parts of ceramic fiber, 15 parts of zirconia, 5 parts of synthetic graphite, 2 parts of antimony trisulfide, 5 parts of aramid fiber, 7 parts of mica powder, 9 parts of friction powder, 10 parts of phenolic resin, 1 part of light calcium carbonate, and 3 parts of rubber powder; pour the prepared fabric materials into the plow mixer and mix for 30 minutes, take out the mixture , put it in an oven and bake it at 70°C for 1 hour to form a fabric mixture for later use, wherein the synthetic graphite is the synthetic graphite of the model YUAI-MCH-01 produced by Shanghai Youai Metallurgical Materials Co., Ltd.;

[0036] (2) Prepare the following primer materials in parts by weight: 35 parts of ...

Embodiment 2

[0042] Embodiment 2, a method for manufacturing a new high-temperature-resistant ceramic car disc brake pad modified by zirconia, the specific steps are as follows:

[0043] (1) Prepare the following fabric materials in parts by weight: 20 parts of barium sulfate, 6 parts of copper fiber, 12 parts of ceramic fiber, 15 parts of zirconia, 10 parts of synthetic graphite, 3 parts of antimony trisulfide, 2 parts of aramid fiber, 8 parts of mica powder, 7 parts of friction powder, 6 parts of phenolic resin, 3 parts of light calcium carbonate, and 4 parts of rubber powder; pour the prepared fabric materials into the plow mixer and mix for 30 minutes, take out the mixture , put it in an oven and bake it at 70°C for 1 hour to form a fabric mixture for later use, wherein the synthetic graphite is the synthetic graphite of the model YUAI-MCH-01 produced by Shanghai Youai Metallurgical Materials Co., Ltd.;

[0044] (2) Prepare the following primer materials in parts by weight: 40 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a zirconium oxide modified novel high temperature resistant ceramic car disc brake pad and a preparation method of the brake pad. The brake pad is prepared by the following steps: mixing barium sulfate, red copper fiber, ceramic fiber, zirconium oxide, synthetic graphite, antimony trisulfide, aramid fiber, mica powder, frictional powder, phenolic resin, light calcium carbonate and rubber powder, and putting the mixture into an oven with 70 DEG C to form mixed surface material; preparing steel fiber, synthetic graphite, flake graphite, petroleum coke powder, blanc fixe, porous iron powder, phenolic resin, light magnesium oxide, rubber powder and wollastonite into mixed backing material in the same way; pre-pressing and molding the mixed backing material, the mixed surface material and steel backing on a cold-pressing molding machine, then putting the product into a hot-pressing molding mould, and carrying out hot-pressing molding; after that, putting the product into a heat treatment oven, and carrying out heat treatment; and grinding the surface of the product, processing by other existing steps, and packaging. The zirconium oxide modified novel high temperature resistant ceramic car disc brake pad is free from heat fade, stable in friction coefficient, good in friction performance, stable in brake, sensitive and reliable, low in hardness and low in wear rate.

Description

technical field [0001] The invention relates to a disc brake pad used for parking and driving brakes of automobiles, in particular to a new type of zirconia-modified high-temperature-resistant ceramic car disc brake pad and a preparation method thereof. Background technique [0002] Brake pads, also known as brake pads, are vital parts of motor vehicles. The quality of the braking performance is directly related to the safety of driving. Since the first automatic brake pads for automobiles were born, people have been continuously improving the brake pad With the continuous progress of the automobile industry, the requirements of automobiles for brake pads are also increasing, and the paint puts forward higher requirements for the thermal stability, wear resistance, and thermal recession of brake pads. The existing friction pads used for braking and transmission mainly include disc brake pads and drum brake pads. Among them, the disc brake pads have better reactivity and stab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F16D69/02C09K3/14
Inventor 陈和发
Owner 武汉市祥龙摩擦材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap