Preparation method of environmentally-friendly interior wall putty powder

An interior wall putty powder, green and environmental protection technology, applied in the direction of filling slurry, etc., can solve the problems of insufficient strength and hardness, poor stability, etc., and achieve the effect of saving usage, smooth wall surface and convenient construction

Inactive Publication Date: 2013-10-16
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These patents use building gypsum, desulfurized gypsum, and fluorogypsum as base materials to prepare putty, but the above-mentioned prior art still has shortcomings such as poor stability, strength and hardness that cannot meet specific construction requirements, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing green and environment-friendly interior wall putty powder. The putty powder consists of the following components in parts by weight: 15 parts of white cement, 5 parts of ash calcium powder, 6 parts of cassava gelatinized starch, and -320 mesh heavy calcium carbonate 26 parts of powder, 3 parts of -200 mesh expanded perlite, 2.5 parts of 3-5mm polypropylene fiber, 2 parts of polyvinyl alcohol, 3 parts of carboxymethyl cellulose, 2.5 parts of tertiary fly ash, 7 parts of sodium bentonite, 1 part of sodium fluorosilicate, 4 parts of dispersant, 0.4 part of defoamer, 0.4 part of antifungal agent;

[0018] Described preparation method comprises the steps:

[0019] S1, the cassava starch is gelatinized according to a conventional method to obtain cassava gelatinized starch for subsequent use, and the calcium bentonite is treated with sodium carbonate to obtain sodium bentonite for subsequent use;

[0020] S2. White cement, gray calcium powder, cassava ...

Embodiment 2

[0023] A method for preparing green and environment-friendly interior wall putty powder. The putty powder consists of the following components in parts by weight: 18 parts of white cement, 3 parts of ash calcium powder, 8 parts of cassava gelatinized starch, and -320 mesh heavy calcium carbonate 22 parts of powder, 5 parts of -200 mesh expanded perlite, 1.5 parts of 3-5mm polypropylene fiber, 4 parts of polyvinyl alcohol, 2 parts of carboxymethyl cellulose, 3.5 parts of tertiary fly ash, 5 parts of sodium bentonite, 2 parts of sodium fluorosilicate, 2 parts of dispersant, 0.6 part of defoamer, 0.2 part of antifungal agent;

[0024] Described preparation method comprises the steps:

[0025] S1, the cassava starch is gelatinized according to a conventional method to obtain cassava gelatinized starch for subsequent use, and the calcium bentonite is treated with sodium carbonate to obtain sodium bentonite for subsequent use;

[0026] S2. White cement, gray calcium powder, cassava...

Embodiment 3

[0029] A preparation method of green and environment-friendly interior wall putty powder. The putty powder consists of the following components in parts by weight: 16.5 parts of white cement, 4 parts of ash calcium powder, 7 parts of cassava gelatinized starch, and -320 mesh heavy calcium carbonate 24 parts of powder, 4 parts of -200 mesh expanded perlite, 2.0 parts of 3-5mm polypropylene fiber, 3 parts of polyvinyl alcohol, 2.5 parts of carboxymethyl cellulose, 3.0 parts of tertiary fly ash, 6 parts of sodium bentonite, 1.5 parts of sodium fluorosilicate, 3 parts of dispersant, 0.5 parts of defoamer, 0.3 parts of antifungal agent;

[0030] Described preparation method comprises the steps:

[0031] S1, the cassava starch is gelatinized according to a conventional method to obtain cassava gelatinized starch for subsequent use, and the calcium bentonite is treated with sodium carbonate to obtain sodium bentonite for subsequent use;

[0032] S2. White cement, gray calcium powder...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of environmentally-friendly interior wall putty powder. The preparation method comprises the following steps: S1. performing gelatinization treatment on cassava starch through a conventional method to obtain gelatinized cassava starch for future use, and treating calcium bentonite through sodium carbonate to obtain sodium bentonite for future use; S2. putting the following ingredients into a diffuser provided with a stirrer: 15-18 parts of white cement, 3-5 parts of sierozem powder, 6-8 parts of gelatinized cassava starch, 22-26 parts of heavy calcium carbonate powder (320 meshes), 3-5 parts of expanded perlite (200 meshes), 1.5-2.5 parts of polypropylene fiber (3-5mm), 2-4 parts of polyvinyl alcohol, 2-3 parts of sodium carboxymethyl cellulose, 2.5-3.5 parts of three-grade fly ash, 5-7 parts of sodium bentonite and 1-2 parts of sodium fluosilicate, and stirring the ingredients for 10-20 minutes; and S3. adding 2-4 parts of dispersing agent, 0.4-0.6 parts of antifoaming agent and 0.2-0.4 parts of parts of mildew preventive, and stirring for 30-40 minutes. The putty prepared by the preparation method disclosed by the invention is anti-cracking, free of peeling, dropping and toxic and harmful substances and is capable of properly perfecting the environmental quality.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a preparation method of green and environment-friendly interior wall putty powder. Background technique [0002] The structure of modern buildings is an organic whole, load-bearing walls, functional insulation layers, waterproof layers, decorative layers, materials at all levels complement each other and are indispensable. Putty is located between the wall leveling mortar and the paint layer, and plays an auxiliary role in further leveling and forming decorative texture patterns. The putty powder is convenient for packaging, storage and transportation, and it can be directly applied by adding water and stirring evenly on site. Common putty powders on the market are mainly composed of white cement, inert fillers, and chemical additives, which are obtained by uniform mixing. After this dry powder material is transported to the construction site, it can be scraped and ap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
Inventor 王和山
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com