Anti-aging abs-tpu plastic alloy

A plastic alloy, anti-aging technology, applied in the field of plastic alloys, can solve the problems of poor anti-aging performance, achieve excellent thermal aging performance, improve impact resistance, and improve stress cracking resistance

Inactive Publication Date: 2015-11-18
重庆市格林得斯塑胶有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the current ABS-TPU plastic alloys have poor aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Each raw material was weighed according to the data corresponding to Example 1 in Table 1. Add each component into a high-speed mixer, control the speed at 350 rpm at room temperature, mix for 8 minutes, take it out and transfer it to a screw extruder, extrude and granulate at a temperature of 185°C to obtain anti-aging ABS- TPU plastic alloy.

[0021] Table 1: Anti-aging ABS-TPU plastic alloy formula table Unit: kg

[0022]

Example 1

Example 2

Example 3

Example 4

ABS resin

100

100

100

100

TPU resin

20

20

20

20

[0023] 4,4'-Thiobis(6-tert-butyl-3-methylphenol)

0.4

0.8

/

0.5

1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane

0.4

/

0.8

0.5

Dioctadecyl Thiodipropionate

0.2

0.2

0.2

/

[0024] The TPU resin is TPU resin with a brand name of 192 from Bayer Company in Germany;

[0025] The ABS resin is selected ...

Embodiment 2-4

[0027] Each raw material was weighed according to the data corresponding to Examples 2-4 in Table 1. The method described in Example 1 was used to prepare the anti-aging ABS-TPU plastic alloy.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-aging ABS-TPU plastic alloy composed of the components of, by weight: 100 parts of ABS, 15-25 parts of TPU, and 0.5-1.5 parts of an anti-aging agent. With the ABS-TPU plastic alloy, TPU stress resistance and cracking resistance are sufficiently improved; stabilities of TPU against oxygen, ozone, and ultraviolet rays can be improved; ABS impact resistance, wearing resistance, and forming and processing performances can be improved. The plastic alloy can be used for producing auto parts, pulleys, low-load gears, and gaskets. The plastic alloy has excellent thermal-aging resistance, and can be applied under extreme-high-temperature environments.

Description

technical field [0001] The invention relates to a plastic alloy, in particular to an anti-aging ABS-TPU plastic alloy. Background technique [0002] ABS resin (acrylonitrile-styrene-butadiene copolymer, ABS is the acronym for AcrylonitrileButadieneStyrene) is a thermoplastic polymer material structure with high strength, good toughness and easy processing. [0003] ABS is a general-purpose thermoplastic engineering plastic developed in the 1940s. It is a plastic variety with excellent comprehensive mechanical properties. It not only has good rigidity, hardness and processing fluidity, but also has high toughness. It can be injected, extruded or heated. forming. [0004] Thermoplastic polyurethane elastomer, Thermoplastic polyurethane, referred to as TPU. [0005] However, the current ABS-TPU plastic alloy has poor aging resistance. Contents of the invention [0006] In view of the above-mentioned deficiencies in the prior art, the technical problem to be solved by the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08L75/04C08K5/375C08K5/13C08K5/372
Inventor 黄美蓉
Owner 重庆市格林得斯塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com