Microorganism-pollution-resistant asphalt-base high-molecular water-emulsion waterproof paint and preparation method thereof

A technology based on polymer and waterproof coatings, which is applied in asphalt coatings, chloroprene homopolymer coatings, epoxy resin coatings, etc. to improve high temperature performance and adhesion, excellent storage stability, and convenient construction and painting Effect

Active Publication Date: 2014-02-05
ZHEJIANG YUXI CORROSION CONTROL CORP
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, for coatings, there is an anti-mildew and anti-algae problem, and how to provide an anti-mildew and anti-algae coating has become a technical problem to be solved urgently in this field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microorganism-pollution-resistant asphalt-base high-molecular water-emulsion waterproof paint and preparation method thereof
  • Microorganism-pollution-resistant asphalt-base high-molecular water-emulsion waterproof paint and preparation method thereof
  • Microorganism-pollution-resistant asphalt-base high-molecular water-emulsion waterproof paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Component A: Pump 60# asphalt specially used for waterproof materials into the asphalt tank and heat to 160°C-180°C, add 3% aromatic oil, stir at 80 rpm for half an hour, and then add 3% epoxy resin E-51, After stirring for 30 minutes, it was ground by a colloid mill, and the prepared polymer modified asphalt material was stirred for 2 hours to defoam, and when the temperature dropped to about 150°C, 0.1% BIT preservative Nuosept498, 0.5% BCM antifungal agent and N-3 were added ,4-dichlorophenyl-N`,N`-dimethylurea 0.2%, stir for later use. Pump hot water at 60°C into the soap tank, add sulfonated tall oil soap or tall oil (tall oil anionic slow-cracking emulsifier) ​​1%, 0.02% AEO-9 and 0.6% ethylenediamine , while adjusting the pH value to 11 with NaOH to make soap. The prepared polymer modified asphalt and soap solution are simultaneously passed through a high-speed shearing machine to make a modified emulsified asphalt emulsion with a mass concentration of 60%, and ...

Embodiment 2

[0040] Component A: Pump 60# asphalt into the asphalt tank and heat to 160℃~180℃, put in 2% aromatic oil, stir at 100 rpm for half an hour, then put in 2% epoxy resin E-44, and stir for 30 minutes After being ground by a colloid mill, the prepared polymer modified asphalt material was stirred for 2 hours to defoam, and when the temperature dropped to about 150°C, 0.1% BIT preservative Nuosept498, 0.5% BCM antifungal agent and N-3,4- Dichlorophenyl-N`,N`-dimethylurea 0.2%, stirred for later use. Pump hot water at 60°C into the soap tank, add 1% sulfonated tall oil soap, 0.02% AEO-9 and 0.6% 1,3-propylenediamine, and adjust the pH value to 11 with NaOH at the same time. into soap. The prepared polymer-modified asphalt and soap solution are simultaneously passed through a high-speed shearing machine to make a modified emulsified asphalt emulsion with a mass concentration of 60%. Add 15% neoprene latex, 10% styrene-butadiene latex and 0.5% IPBC antifungal agent, add slowly and k...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elastic recovery rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a microorganism-pollution-resistant asphalt-base high-molecular water-emulsion waterproof paint. The paint is prepared by taking high-concentration ultrafine suspension microemulsion anion modified emulsified asphalt, multiple synthetic high-molecular polymers such as SBS rubber, chloroprene rubber, epoxy resin and the like, a composite anticorrosion mildew-resistant algicide and multiple functional agents as raw materials and mixing by employing a special production technology. Tests show that after a film is formed from the paint, no embrittlement happens at a low temperature of -25 DEG C, no flow happens at a high temperature of 120 DEG C, the elasticity recovery rate reaches up to 90%, and the mildew-resistant and algae-resistant degrees both reach first level.

Description

technical field [0001] The invention belongs to the technical field of waterproof building materials, in particular to an anti-biological asphalt-based polymer water-emulsion waterproof coating and a preparation method thereof. Background technique [0002] The microbial contamination that may occur in the production and storage of coatings is mainly caused by bacteria, which should be solved by adding preservatives, purifying the environment and strict production management. The coating has hydrophilic components, has a certain degree of water absorption, and at the same time contains the nutrients needed by microorganisms, and it is easy to grow mold and algae in a hot and humid environment. Therefore, for coatings, there is an anti-mildew and anti-algae problem, and how to provide an anti-mildew and anti-algae coating has become a technical problem to be solved urgently in this field. Contents of the invention [0003] The present invention aims at the above-mentioned ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D163/00C09D111/02C09D109/06C09D7/12C09D5/00
Inventor 欧曙辉
Owner ZHEJIANG YUXI CORROSION CONTROL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com