Modified butyl rubber sealing gasket material and preparation method thereof

A butyl rubber and sealing pad technology is applied in the field of modified butyl rubber sealing pad material and its preparation, which can solve the problems of low strength, poor wear resistance, unsatisfactory sealing effect, etc., achieve low cost, improve process performance, The effect of stable product quality

Inactive Publication Date: 2014-03-05
TONGLING SIDE TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance, and low strength, which are far from meeting the actual requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified butyl rubber sealing gasket material and preparation method thereof
  • Modified butyl rubber sealing gasket material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The present invention will be described in detail below through specific examples.

[0010] A modified butyl rubber gasket material, made of the following raw materials in parts by weight (kg): butyl rubber (BBK232) 60, SG-4 type PVC resin 15, triethyl citrate 6, epoxy oleic acid Butyl ester 1, sulfur 1, accelerator TMTM1, rutile titanium dioxide 18, 1-bromo-3-methyl-2-butene 2, trifluoroacetylacetonate holmium 1, bauxite powder 20, N339 carbon black 10, Titanate coupling agent TMC-TTS1, antioxidant 10101, modified attapulgite 10;

[0011] The modified attapulgite is made of the following raw materials in parts by weight (kg): attapulgite 20, toluene diisocyanate 3, trimethylolpropane triacrylate 2, barley oil 2, citric acid 2, nano titanium dioxide 1 , aluminum oxide 2, methyltriethoxysilane 1, accelerator TMTM1, corundum powder 2, pepper seed oil 1; the preparation method is to put attapulgite into a calciner at 700-720°C for 3- 4 hours, cool, soak in 10-12% hydroch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified butyl rubber sealing gasket material. The modified butyl rubber sealing gasket material is characterized by being prepared from the following raw materials in parts by weight: 60-65 parts of butyl rubber (BBK232), 15-20 parts of SG-4 type PVC (polyvinyl chloride) resin, 6-8 parts of triethyl citrate, 1-2 parts of epoxy butyl oleate, 1-2 parts of sulfur, 1-2 parts of accelerant TMTM, 18-22 parts of rutile titanium dioxide, 2-5 parts of 1-bromine-3-methyl-2-butene, 1-2 parts of trifluoroacetylacetone holmium, 20-25 parts of bauxite powder, 10-15 parts of N339 carbon black, 1-2 parts of titanate coupling agent TMC-TTS, 1-2 parts of antioxidant 1010 and 10-12 parts of modified attapulgite. The processing property of the rubber material is improved by adding the modified attapulgite; the toxic and side effects and the pollution to environments of the rubber material are reduced by using an environmentally-friendly compounding agent; the modified butyl rubber sealing gasket material is reasonable in formula, simple in process and low in cost and has good oil resistance, ageing resistance and insulativity, and the quality of products is stable.

Description

technical field [0001] The invention relates to the field of processing rubber composite materials, in particular to a modified butyl rubber sealing gasket material and a preparation method thereof. Background technique [0002] Gasket is a material used for sealing inside machinery, equipment, pipelines, etc. The gaskets currently used are mostly rubber gaskets, which are characterized by high temperature resistance, ozone resistance, natural aging resistance, vacuum resistance, fuel oil resistance, lubricating oil resistance, strong oxidant resistance, chemical resistance and good electrical insulation performance. Widely used in defense industry and civilian industry. However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance and low strength, which are far from meeting the actual requirements. Therefore researching and developing a kind of high-performance rubber gasket has become the task of top priority. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/22C08L27/06C08K13/06C08K9/00C08K9/02C08K3/34C08K5/103C08K3/22C08K5/11C08K5/1515
CPCC08K2003/2241C08L23/22C08K2201/011C08K2201/014C08L2201/08C08L27/06C08K13/06C08K9/00C08K9/02C08K3/34C08K5/103C08K2003/2227C08K5/11
Inventor 孔华英
Owner TONGLING SIDE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com