A kind of water-based inorganic zinc-rich paint and preparation method thereof

An inorganic zinc-rich coating, water-based technology, applied in the direction of alkali metal silicate coatings, coatings, etc., can solve problems such as uneven particle size distribution, inability to apply, coating gelation, etc., to achieve uniform reaction rate, no occurrence of The effect of stress concentration

Active Publication Date: 2017-10-27
CENT RES INST OF BUILDING & CONSTR CO LTD MCC GRP +2
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, due to problems such as uneven particle size distribution and poor stability of the high-modulus silicate water-based inorganic zinc-rich coating liquid components during the preparation process, the coating will gel during storage and cannot be applied.
At the same time, the coating is prone to disadvantages such as poor toughness, cracking, chipping, and poor early water resistance after construction and curing. The above coating problems are more likely to occur on the surface of substrates such as steel with low surface treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based inorganic zinc-rich paint and preparation method thereof
  • A kind of water-based inorganic zinc-rich paint and preparation method thereof
  • A kind of water-based inorganic zinc-rich paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In this example, the high-performance water-based inorganic zinc-rich coating is formed by blending and stirring a mixture of high modulus potassium silicate solution and zinc powder according to the mass ratio of 1:2.3; in terms of mass percentage,

[0033] The high modulus potassium silicate solution comprises the following components:

[0034] Potassium silicate solution 100kg

[0035] Water 59.4kg

[0036] Aluminum-modified silica sol 197kg, wherein the molar content of aluminum ion is 0.8%

[0037] Catalyst: Tetramethylammonium Hydroxide 4.6kg

[0038] Siloxane oligomer: bis(1,2-triethoxysilyl)ethane 6.05kg

[0039] Modifier: Octaamino cage silsesquioxane 10.7kg

[0040] Silicone acrylic emulsion 14.25kg

[0041] Anti-sedimentation agent: magnesium aluminum silicate inorganic gel 1.78kg

[0042] Defoamer 0.86kg

[0043] The zinc dust mixture includes the following components:

[0044] Zinc powder 90kg

[0045] Hardener: potassium zirconium carbonate 3.7kg ...

Embodiment 2

[0055] In this example, the high-performance water-based inorganic zinc-rich coating is formed by blending and stirring a mixture of high modulus potassium silicate solution and zinc powder according to the mass ratio of 1:2.6; in terms of mass percentage,

[0056] The high modulus potassium silicate solution comprises the following components:

[0057] Potassium silicate solution 100kg

[0058] water 79kg

[0059] Aluminum modified silica sol 295kg wherein the molar content of aluminum ion is 1.2%

[0060] Catalyst: tetraethylammonium hydroxide 6.12kg

[0061] Siloxane oligomer: bis(1,2-trimethoxysilyl)ethane 8.05kg

[0062] Modifier: octaepoxy cage silsesquioxane 14.22kg

[0063] Silicone acrylic emulsion 18.98kg

[0064] Anti-sedimentation agent: magnesium aluminum silicate inorganic gel 2.37kg

[0065] Defoamer 1.2kg

[0066] The zinc dust mixture includes the following components:

[0067] Zinc powder 92kg

[0068] Hardener: potassium zirconium carbonate 2.7kg

...

Embodiment 3

[0078] In this embodiment, the high-performance water-based inorganic zinc-rich coating is formed by blending and stirring a mixture of high modulus potassium silicate solution and zinc powder according to the mass ratio of 1:3.5; in terms of mass percentage,

[0079] The high modulus potassium silicate solution comprises the following components:

[0080] Potassium silicate solution 100kg

[0081] water 115kg

[0082] Aluminum modified silica sol 380kg wherein the molar content of aluminum ion is 1.2%

[0083] Catalyst: tetraethylammonium hydroxide 8.18kg

[0084] Siloxane oligomer: bis(1,2-trimethoxysilyl)ethane 10.25kg

[0085] Modifier: octaepoxy cage silsesquioxane 18.28kg

[0086] Silicone acrylic emulsion 21.58kg

[0087] Anti-sedimentation agent: magnesium aluminum silicate inorganic gel 2.15kg

[0088] Defoamer 1.4kg

[0089] The zinc dust mixture includes the following components:

[0090] Zinc powder 88kg

[0091] Hardener: potassium zirconium carbonate 2.7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a water-based inorganic zinc-rich paint and a preparation method thereof. The zinc-rich coating uses a high-modulus potassium silicate solution obtained by dropping aluminum-modified silica sol in a low-modulus potassium silicate solution as a binder, and adds catalysts, siloxane oligomers, The modifying agent makes the particle size distribution of the high modulus potassium silicate solution uniform, and the gelation reaction does not occur for a long time. The reaction rate of each part of the layer is uniform, and the advantages of no stress concentration occur. Experiments have proved that the zinc-rich coating of the present invention does not gel after being stored at 50°C for 90 days; the thickness of one-time film formation can reach 200 μm, without cracking and peeling; the steel surface treatment grade can reach Sa2 and can be applied; the coating’s salt spray resistance can reach 10000 hours.

Description

technical field [0001] The invention relates to a zinc-rich paint, in particular to a water-based inorganic zinc-rich paint with modified potassium silicate as a main binder and a preparation method thereof. Background technique [0002] The water-based inorganic zinc-rich coating uses high-modulus silicate as the main binder, and the silicate and zinc powder react and cross-link to form a film under certain conditions. Since the standard potential of zinc is lower than that of steel, when the corrosive medium penetrates, the steel and zinc powder form a primary battery, the zinc powder loses electrons as the negative electrode of the primary battery, and the steel receives electrons as the positive electrode to be protected. In addition, the dissolved zinc ions combine with the anions in the corrosive medium to form basic zinc salts and zinc-iron double salts, which fill the cracks in the coating film to achieve the purpose of isolation and rust prevention. Therefore, wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/04C09D7/12
Inventor 王炜邓宽高瀚文于钦萍崔梓杰赵希娟严岳荣
Owner CENT RES INST OF BUILDING & CONSTR CO LTD MCC GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com