Method for preparing Nb-Si based superhigh-temperature alloy by SLM (selective laser melting) technology

A laser selective melting and ultra-high temperature alloy technology, which is applied in the direction of improving energy efficiency and process efficiency, and can solve the problem of difficulty in meeting the requirements of Nb-Si-based alloy investment casting, multi-machining and post-processing, and waste of alloy materials. and other problems, to achieve the effect of eliminating the process of designing and manufacturing molds, avoiding machining and post-processing, and improving overall performance

Inactive Publication Date: 2014-07-30
BEIHANG UNIV
View PDF5 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantages of traditional directional solidification mainly include: the cooling rate is low during the solidification process, which leads to the coarsening and growth of the alloy structure, which limits the improvement of the alloy performance. Elements, so it is very easy to have interface reaction with the contacting crucible at high temperature, causing alloy pollution, increased oxygen content, increased casting inclusions, and decreased mechanical properties
For investment casting of Nb-Si based alloys, the shell temperature capacity will exceed 2000°C. However, the shell temperature capacity current

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing Nb-Si based superhigh-temperature alloy by SLM (selective laser melting) technology
  • Method for preparing Nb-Si based superhigh-temperature alloy by SLM (selective laser melting) technology
  • Method for preparing Nb-Si based superhigh-temperature alloy by SLM (selective laser melting) technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027]Using SLM technology to prepare Nb-18Si-24Ti-2Cr-2Al-2Hf (at.%, atomic percentage) super high temperature alloy: the SLM laser selective melting system used mainly includes: Nd-YAG laser, computer system for forming control, Powder feeding system and argon atmosphere protection device;

[0028] 1. Select Nb-18Si-24Ti-2Cr-2Al-2Hf pre-alloyed powder prepared by argon atomization method, the powder is spherical or nearly spherical, and the diameter is between 10 and 60 μm;

[0029] 2. According to the shape of the alloy parts to be processed, use the computer to establish a three-dimensional CAD model, and use the slicing software to perform layered slice discretization in the height direction of the model. Section profile information and scanning processing path, save multi-layer slice information as STL file, and transfer to SLM laser melting system;

[0030] 3. Put the powder into the forming cavity, and fix the Ti6Al4V forming substrate with a thickness of 10mm on the ...

Embodiment 2

[0037] Using SLM technology to prepare Nb-16Si-22Ti-4Cr-2Al-2Hf (at.%, atomic percentage) super high temperature alloy: the SLM laser selective melting system used mainly includes: Nd-YAG laser, computer system for forming control, Powder feeding system and argon atmosphere protection device;

[0038] 1. Select Nb-16Si-22Ti-4Cr-2Al-2Hf pre-alloyed powder prepared by argon atomization method, the powder is spherical or nearly spherical, and the diameter is between 10 and 60 μm;

[0039] 2. According to the shape of the alloy parts to be processed, use the computer to establish a three-dimensional CAD model, and use the slicing software to perform layered slice discretization in the height direction of the model. Section profile information and scanning processing path, save multi-layer slice information as STL file, and transfer to SLM laser melting system;

[0040] 3. Put the powder into the forming cavity, and fix the Ti6Al4V forming substrate with a thickness of 10mm on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of preparation of high-temperature alloy, and particularly relates to a method for preparing NbSi superhigh-temperature alloy by SLM (selective laser melting) technology. SLM equipment is utilized, the process parameters are reasonably set, and an NbSi alloy forming piece is directly prepared by a CAD (computer-aided design) model in a one-step way. The prepared NbSi alloy has the characteristics of high density, fewer defects, fine phase size and uniform distribution, and mainly consists of Nbss solid solution and Nb5Si3 strengthening phase. The NbSi alloy prepared by the method has the advantages that a die is not needed, the interface reaction is avoided, the alloy pollution is reduced, the content of impurities is reduced, the utilization rate of material is high, and the comprehensive yield and production efficiency of the NbSi alloy can be improved.

Description

technical field [0001] The invention belongs to the technical field of high-temperature alloy preparation, and in particular relates to a method for preparing NbSi super high-temperature alloy by using laser selective melting technology. Background technique [0002] With the development of high-performance aero-engines and gas turbines in the direction of high flow ratio, high thrust-to-weight ratio, and high inlet temperature, the operating temperature of hot-end components such as turbine blades continues to increase, and the turbine inlet temperature also continues to increase. At present, the maximum service temperature of the third-generation nickel-based single crystal superalloy used in jet engines has reached 1100-1150 °C, which is close to 85% of the melting point of the alloy, and there is little potential for further improvement. Therefore, it is urgent to develop new structures. Material. At present, refractory silicides have become a hot spot in the research f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/105C22C27/02
CPCY02P10/25
Inventor 张虎孙少波贾丽娜李震徐惠彬
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap