Method for extracting high-quality iron powder and borax from paigeite

A technology of boron ore and boron concentrate, applied in chemical instruments and methods, borates, boron oxides, etc., can solve the problems of poor boron activity, high energy consumption, and difficult separation of boron and iron, so as to improve the additional Value, reduce evaporation, increase the effect of crystallization rate

Active Publication Date: 2014-07-30
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] Aiming at the above-mentioned deficiencies in the prior art, the main purpose of the present invention is to overcome the problems of difficult separation of boron-containing iron ore concentrate, high energy consumption, and poor activity of boron, and to pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for extracting high-quality iron powder and borax from paigeite

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] Combine iron concentrate with 30wt% Na 2 CO 3 Mixed with 10wt% coal, the mixture and external coal are placed in a crucible in a tubular charging method, kept at a temperature of 1100°C for 3h, and then cooled. The roasted product is crushed and ground (the size of the crushed product is ≤ 10mm, the grinding fineness is -74μm, the content is more than 40%) for leaching and washing, the leaching and washing temperature is 95℃, the leaching and washing time is 30min, the ratio of washing liquid to solid is 1:1, and the leaching rate of boron and sodium has reached More than 90. The leaching residue is finely ground and magnetically separated to obtain a magnetic separation product (the fineness is -74μm, the content is more than 80%, and the magnetic field strength is 60-100kA / m), and then dried in an inert atmosphere to obtain TFe> 98.5% of high-quality iron powder, the recovery rate of iron is over 85%. Add lime milk to the alkaline filtrate, desiliconi...

Example Embodiment

[0039] Example 2

[0040] Combine iron concentrate with 40%wt Na 2 CO 3 Mixed with 10%wt coal, the mixture and external coal are placed in a crucible in a tubular charging method, kept at a temperature of 1150℃ for 4h, and then cooled. The roasted product is crushed and ground (the size of the crushed product is ≤10mm, the fineness of grinding is -74μm, the content is more than 40%) for leaching and washing, the leaching and washing temperature is 95℃, the leaching and washing time is 10min, the ratio of washing liquid to solid is 2:1, and the leaching rate of boron reaches 90% the above. The leaching residue is finely ground and magnetically separated to obtain a magnetic separation product (the fineness is -74μm, the content is more than 80%, and the magnetic field strength is 60-100kA / m), and then dried in an inert atmosphere to obtain TFe> 98.5% of high-quality iron powder, the recovery rate of iron is over 85%. Add lime milk to the alkaline filtrate, desiliconize at 100°C f...

Example Embodiment

[0041] Example 3

[0042] Combine iron concentrate with 20% Na 2 CO 3 Mixed with 5%wt coal, the mixture and external coal are placed in a crucible in a tubular charging method, kept at a temperature of 950℃ for 24h, and then cooled. The roasted product is crushed and ground (the size of the crushed product is ≤ 10mm, grinding fineness of -74μm, content accounted for more than 40%) for leaching and washing, leaching and washing temperature 95℃, leaching and washing time 90min, washing liquid solid ratio 1.5:1, boron leaching rate reached 90% the above. The leaching residue is finely ground and magnetically separated to obtain a magnetic separation product (the fineness is -74μm, the content is more than 80%, and the magnetic field strength is 60-100kA / m), and then dried in an inert atmosphere to obtain TFe> 98.5% of high-quality iron powder, the recovery rate of iron is over 85%. Add lime milk to the alkaline filtrate, desiliconize at 95°C for 120 min, then carbonize (carbonizati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Finenessaaaaaaaaaa
Magnetic field strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of metallurgy of steel and iron and processing of mineral resources and specifically relates to a method for extracting high-quality iron powder and borax from paigeite. The method provided by the invention comprises the following steps: (1) mixing boron-containing iron concentrate, solid Na2CO3 and coal together to obtain a mixture; (2) roasting the mixture under a reducing atmosphere at the temperature of 950-1150 DEG C to obtain a roasted product; (3) crushing and grinding the roasted product and then, leaching, washing and filtering ore slurry to obtain an alkaline filtrate and an iron-containing filter cake; (4) performing desilication, CO2 carbonization, filtration and crystallization on the alkaline filtrate to obtain qualified borax and simultaneously realize recycling of reaction medium Na2CO3; (5) performing magnetic separation, grinding and secondary magnetic separation on the obtained filter cake to obtain high-quality reducing iron powder (TFe is more than 98.5%) which can be used as an iron-based raw material for powder metallurgy. According to the method provided by the invention, by adding a large amount of Na2CO3, the leaching of boron minerals is simultaneously realized during iron reduction, the process flow is shortened and the energy consumption is reduced.

Description

technical field [0001] The invention belongs to the field of iron and steel metallurgy and mineral resources processing, in particular, the invention relates to a method for extracting high-quality iron powder and borax from boron iron ore. Background technique [0002] Wengquangou, Fengcheng, Liaoning has rich boron resources, accounting for 58% of the national boron reserves, mainly low-grade "black boron ore" (boron iron ore), of which w (TFe) is 27% to 30%, w (B 2 o 3 ) 6% to 8%, and the ore types are mainly boronite-magnetite type and boronite-magnetite type. [0003] Since the 1970s, a number of domestic units have carried out a large number of beneficiation experiments on Fengcheng boronite ore in Liaoning, and have achieved certain results. Basically, magnetite, boronite, and boronite in boronite have been basically realized. Separation and enrichment of useful minerals. However, since the main minerals of boronite are micro-fine particles and uneven distribution...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B1/02B03C1/02C01B35/12
Inventor 李永利齐涛曲景奎余志辉李洁赵宏欣
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap