Preparation method of spun silk/PTT (polytrimethylene terephthalate) blended fabric with shape memory function

A technology of blending fabrics and spun silk, which is applied in the processing of textile materials, continuous processing of textile materials, fabrics, etc., to achieve the effects of easy shaping, comfortable wearing and simple process flow

Inactive Publication Date: 2014-07-30
SUZHOU UNIV
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The method of using spun silk / PTT blended yarn to prepare fabrics with shape memory function has not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The spun silk / PPT blended fabric fabric described in this example, its preparation steps are as follows:

[0038] 1. The spinning steps of spun silk / PTT blended yarn are as follows:

[0039] 1) Prepare spun silk fiber fine cotton sheet;

[0040]The preparation process of spun silk fiber fine cotton sheet is as follows: spun silk fiber dry cotton → cotton blending → wetting → cotton opening → roller combing → sorting → combing → silk fiber fine cotton sheet;

[0041] Among them, the requirements for blending cotton: the linear density of spun silk fiber in refined dry cotton is above 1.11dtex, the length is 80mm, the residual oil rate is less than 0.5%, the residual glue rate is 2%, the cleanliness is less than 30 degrees, and the moisture regain is 8%;

[0042] Among them, wetting requirements: use dipping wetting method, 0.05% antistatic agent 824-N, 0.64% smoothing agent 289, 0.1% dispersant WA, 0.2% electrolyte sodium citrate.

[0043] 2) Prepare PTT short fiber fi...

Embodiment 2

[0064] The spun silk / PPT blended fabric fabric described in this example, its preparation steps are as follows:

[0065] 1. The spinning steps of spun silk / PTT blended yarn are as follows:

[0066] 1) Prepare spun silk fiber fine cotton sheet;

[0067] The preparation process of spun silk fiber fine cotton sheet is as follows: spun silk fiber dry cotton → cotton blending → wetting → cotton opening → roller combing → sorting → combing → silk fiber fine cotton sheet;

[0068] Among them, the requirements for cotton blending: the linear density of spun silk fiber in fine dry cotton is above 1.18dtex, the length is 120mm, the residual oil rate is less than 0.5%, the residual glue rate is 3%, the cleanliness is less than 30 degrees, and the moisture regain is 8%;

[0069] Among them, wetting requirements: use dipping wetting method, 0.05% antistatic agent 824-N, 0.64% smoothing agent 289, 0.1% dispersant WA, 0.2% electrolyte sodium citrate.

[0070] 2) Prepare PTT short fiber fin...

Embodiment 3

[0091] The spun silk / PPT blended fabric fabric described in this example, its preparation steps are as follows:

[0092] 1. The spinning steps of spun silk / PTT blended yarn are as follows:

[0093] 1) Prepare spun silk fiber fine cotton sheet;

[0094] The production process of spun silk fiber fine cotton sheet is as follows: spun silk fiber dry cotton → cotton blending → wetting → cotton opening → roller combing → sorting → combing → silk fiber fine cotton sheet;

[0095] Among them, the requirements for blending cotton: the linear density of spun silk fiber in refined dry cotton is above 1.21dtex, the length is 100mm, the residual oil rate is less than 0.5%, the residual glue rate is 5%, the cleanliness is less than 30 degrees, and the moisture regain is 8%;

[0096] Among them, wetting requirements: use dipping wetting method, 0.05% antistatic agent 824-N, 0.64% smoothing agent 289, 0.1% dispersant WA, 0.2% electrolyte sodium citrate.

[0097] 2) Prepare PTT short fiber f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
decontamination rateaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a spun silk / PTT (polytrimethylene terephthalate) blended fabric with a shape memory function. The preparation method is characterized by comprising the following steps: blending PTT short fibers in the blended dry weight ratio of 30 to 70 percent with spun silk fibers to obtain spun silk / PTT blended yarns with the linear density of 83.3 to 166.7 dtex; taking the blended yarns as weft yarns and warp yarns, configuring the density of the warp yarns to be 450 to 600 yarns / 10cm, the density of the weft yarns to be 200 to 280 yarns / 10cm and the total coverage coefficient of the fabric to be 75+ / -3 percent, configuring the number of fabric tissues to be 2 or 4, making fabric gray cloth, and forming finished fabric by refining, four-time washing, drying and shaping. By applying the method provided by the invention, the fabric has high tensile-recovery elasticity, crease recovery,and a shape memory function of shaping, flattening, and smoothening easily, and meanwhile, has the advantages of high moisture permeability, high flexibility, high wear comfort and the like, is a functional spun silk shell fabric, and can serve as the shell fabric of high-end casual clothes.

Description

technical field [0001] The invention relates to a preparation method of spun silk / PTT blended fabric with shape memory function. Background technique [0002] Silk fabric has pearl-like soft luster, soft and smooth to the touch, especially the skin-fitting feeling is incomparable to other fibers. It has good hygroscopicity, good air permeability, good drape and elegant feeling when worn in summer. However, silk fabrics also have certain defects, such as: easy to wrinkle, poor elasticity, easy to shrink, yellowing, etc. In addition, real silk products have a single material, with a single mulberry silk as the main raw material, which has a narrow range of use and short wearing seasons. [0003] Polytrimethylene terephthalate (PTT) fiber has excellent resilience performance, and at the same time has the softness of nylon, the bulkiness of acrylic fiber, and the stain resistance of polyester, so it has a wide range of applications in clothing fabrics. Blending and interweavin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02G3/04D06B21/00D03D15/233D03D15/283D03D15/47
Inventor 眭建华朱思敏汪亮潘志娟汪明树
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com