Coating paint for plywood and preparation method of coating paint

A coating and topcoat technology, which is applied in the field of coating topcoat for plywood and its preparation, can solve the problems of few types, gloss, hardness, and low impact strength, and achieve high impact strength, good appearance, and excellent The effect of water resistance

Active Publication Date: 2014-10-01
WUXI CITY CHONGAN DISTRICT TECH ENTREPRENEURSHIP SERVICE CENT
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical issues solved: Aiming at the shortcomings of existing coatings for splints with few types and low gloss, hardness and impact strength, the invention provides a coating finish for plywood and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating paint for plywood and preparation method of coating paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] This embodiment provides a coating finish paint for splints, which is prepared in parts by mass from the following raw materials: 50 parts of epoxy-modified acrylic resin, 18 parts of hexamethoxymethylmelamine resin, 7 parts of butyl acrylate, phthalate 3 parts of dibutyl formate, 0.015 parts of 2-amino-2-methyl-1-propanol, 3 parts of polyacrylate resin, 0.15 parts of cellulose acetate butyrate, 0.15 parts of polyorganosiloxane, alcohol-soluble and light-resistant 8 parts of yellow GR, 4 parts of dimethyl ether, 0.5 parts of water resistance agent, 7 parts of isopropanol, 3 parts of isopropyl acetate, and 7 parts of distilled water.

[0016] A kind of preparation step of splint coating finish paint is as follows:

[0017] (1) First mix the epoxy-modified acrylic resin, polyacrylate resin and butyl acrylate evenly, and stir for 20 minutes at a stirring speed of 1500r / min;

[0018] (2) Then add hexamethoxymethylmelamine resin, dibutyl phthalate, 2-amino-2-methyl-1-propan...

Embodiment 2

[0020] This embodiment provides a coating finish paint for splints, which is prepared in parts by mass from the following raw materials: 52 parts of epoxy-modified acrylic resin, 20 parts of hexamethoxymethylmelamine resin, 8 parts of butyl acrylate, phthalate 4 parts of dibutyl formate, 0.017 parts of 2-amino-2-methyl-1-propanol, 4 parts of polyacrylate resin, 0.17 parts of cellulose acetate butyrate, 0.16 parts of polyorganosiloxane, alcohol-soluble and light-resistant Yellow GR 9 parts, dimethyl ether 5 parts, water resistant agent 0.6 parts, isopropanol 9 parts, isopropyl acetate 4 parts, distilled water 8 parts.

[0021] A kind of preparation step of splint coating finish paint is as follows:

[0022] (1) First mix the epoxy-modified acrylic resin, polyacrylate resin and butyl acrylate evenly, and stir for 22 minutes at a stirring speed of 1550r / min;

[0023] (2) Then add hexamethoxymethylmelamine resin, dibutyl phthalate, 2-amino-2-methyl-1-propanol, cellulose acetate b...

Embodiment 3

[0025] This embodiment provides a coating finish paint for splints, which is prepared in parts by mass from the following raw materials: 59 parts of epoxy-modified acrylic resin, 22 parts of hexamethoxymethylmelamine resin, 11 parts of butyl acrylate, phthalate 5 parts of dibutyl formate, 0.026 parts of 2-amino-2-methyl-1-propanol, 5 parts of polyacrylate resin, 0.23 parts of cellulose acetate butyrate, 0.23 parts of polyorganosiloxane, alcohol-soluble and light-resistant Yellow GR 14 parts, dimethyl ether 9 parts, water resistant agent 1.8 parts, isopropanol 13 parts, isopropyl acetate 5 parts, distilled water 11 parts.

[0026] A kind of preparation step of splint coating finish paint is as follows:

[0027] (1) Mix epoxy-modified acrylic resin, polyacrylate resin and butyl acrylate evenly, and stir for 28 minutes at a stirring speed of 1750r / min;

[0028] (2) Then add hexamethoxymethylmelamine resin, dibutyl phthalate, 2-amino-2-methyl-1-propanol, cellulose acetate butyrat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a coating paint for plywood and a preparation method of the coating paint. The coating paint is prepared from the following raw materials in parts by mass: 50-60 parts of epoxy modified acrylic resin, 18-24 parts of hexamethoxy methyl melamine resin, 7-12 parts of butyl acrylate, 3-6 parts of dibutyl phthalate, 0.015-0.028 part of 2-amino-2-methyl-1-propyl alcohol, 3-6 parts of polyacrylate resin, 0.15-0.25 part of cellulose acetate butyrate, 0.15-0.25 part of polysiloxane, 8-15 parts of alcohol-soluble fast yellow GR, 4-10 parts of dimethyl ether, 0.5-2 parts of water-proofing agent, 7-15 parts of isopropyl alcohol, 3-6 parts of isopropyl acetate, and 7-12 parts of distilled water. The paint provided by the invention has good appearance, processability and weatherability, and is not easy to be abraded after the plywood is coated with the paint, and the plywood can be kept attractive and durable for a long period of time.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a coating finish paint for splints and a preparation method thereof. Background technique [0002] Plywood, also known as plywood, is made of three or more layers of 1mm-thick veneer or sheet glued by hot pressing. It is the most commonly used material for hand-made furniture, such as furniture manufacturing, interior decoration, and residential construction. sheet. Plywood not only has all the advantages of natural wood, such as light bulk density, high strength, beautiful texture, insulation, etc., but also can make up for some natural defects of natural wood, such as knots, small format, deformation, and large differences in vertical and horizontal mechanics. The splint also has the advantages of good elasticity and toughness, impact and vibration resistance, easy processing and painting. [0003] In daily use, in order to improve the aesthetics and use value of the plywood, it is ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D7/12
Inventor 叶强过俊宏叶飞
Owner WUXI CITY CHONGAN DISTRICT TECH ENTREPRENEURSHIP SERVICE CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap