Composite straw sheet and preparation method thereof

A technology of straw boards and crop straws, which is applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of waste gas emission, high energy consumption, and increase the cost of straw production, so as to meet the hydration speed and promote Stimulate and promote the effect of rapid cementation

Active Publication Date: 2014-10-15
四川什邡国正环保科技有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] It is not difficult to see that the problems in the above-mentioned patents are: except river sand, chlorinated paraffin, methyl cellulose, kaolin, diatomaceous earth, nano silicon dioxide (even the cost of superfine powder is also higher), silane, etc., are all More expensive raw materials increase the production cost of straw
Use pottery clay etc. to modify, heat and stir at 50-60°C, steam the green body at 60-80°C, and finally heat it to 170-180°C, and maintain it under high heat and high pressure for 2-4 hours, involving 180°C steam, high pressure is necessary Boilers, involving safety, high energy consumption, and exhaust emissions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035]A preparation method of a composite straw board, by increasing the clinker content of commonly used sulphoaluminate cement, adding hydraulic calcium oxide as an activator, and then mixing it into composite sulphoaluminate cement as a gelling agent, and cementing Made from crop straw. (That is to say, in the sulphoaluminate cement commonly used in existing finished products, increase the content of sulphoaluminate cement clinker, and then add hydraulic calcium oxide; then these three kinds of raw materials are mixed into composite sulphoaluminate cement, and The composite sulphoaluminate cement is used as a gelling agent to cement crop straws to make a composite straw board.

[0036] The above three raw materials that need to be explained are all obtained from market purchases, and the grinding fineness ratio of the total surface area is 400m 2 / kg or more.

[0037] Preparation of composite sulphoaluminate cement (weight percentage measurement):

[0038] Add 60% of com...

Embodiment 1

[0042] (1) Separation (by weight): 60% of composite sulphoaluminate cement, 40% of rice straw on dry basis, and 50% of water on dry basis.

[0043] (2) Put metered water into the mixer first, start stirring, add metered composite sulphoaluminate cement, and stir for 1 to 2 minutes without stopping the machine;

[0044] (3) Add metered straw to the cement slurry while stirring continuously, and continue stirring for 10-13 minutes.

[0045] (4) Visually observe that the mixing system is uniform, soft, and meets the required plasticity state, and the material is discharged under stirring.

[0046] (5) Open the discharge valve, discharge the material into the mold of the plate channel guide plate forming machine, and automatically type it into the design specification, or use the robot to import the shaped steel wire mesh or the fixed-sized glass fiber mesh into the command part of the mixing body. The board is finished.

[0047] (6) Put it into the mold and form it without vibr...

Embodiment 2

[0050] Compared with Example 1, the difference lies in: 65% of composite sulphoaluminate cement, 35% of rape straw on a dry basis, and 45% of the total dry basis of the formula with water. (operation steps are with embodiment 1)

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a composite straw sheet. The method includes: increasing the content of sulphate aluminium cement clinker into common sulphate aluminium cement, adding hydraulic calcium oxide as an exciting agent, and conducting blending to form compound sulphoaluminate cement, and bonding the cement with crop straw to obtain the sheet. And the side effects of straw on cement setting and hardening can be overcome. In the method, the straw is not soaked by alkaline water, a chlorine-containing material is unnecessary for modification treatment on straw, wastewater discharge does not exist, heating is not needed, smoke dust and exhaust emission are absent. The advantages of light weight and abundant fiber of crop straw are utilized for low energy consumption and pollution-free preparation of the composite straw sheet.

Description

technical field [0001] The invention belongs to the technical field of building materials, and particularly relates to a composite straw cement plate prepared by using composite sulphoaluminate cement as a gelling agent and bonding crop straws with the cement in a normal temperature and pressure environment. Background technique [0002] Aiming at the coagulation of soluble carbohydrates in crop straws, especially sugars, to "hydraulic" cement, hardening is a fatal hazard and a problem that has not been solved so far, so it has been limited to use "air-hardening" magnesia cement to add Chlorine salt curing cement limited straw to make wallboard. Its products are deformed, afraid of water, strength regression, moisture absorption, returning halogen to corrode metal objects, which is not good for the environment. [0003] In addition, the Chinese patent announcement number is CN102887691A, and the announcement date is 2013.113, which discloses a new light-weight wall material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/06C04B18/24
CPCY02W30/91
Inventor 张凤阳
Owner 四川什邡国正环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More