Hexagonal cobalt-nickel alloy nanocluster-graphene composite material, preparation method and application thereof
A technology of cobalt-nickel alloy and composite materials, which is applied in nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., can solve the problems of easy oxidation and small particle size, etc., and the method is simple and easy to absorb. Good wave performance, cheap and easy-to-obtain raw materials
Inactive Publication Date: 2016-03-23
BEIJING NORMAL UNIVERSITY +1
View PDF5 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Therefore, for pure metals and alloys, the main difficulty is that they are easily oxidized in air due to the very small particle size
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0035] Preparation of raw graphite oxide and composites
[0036] Preparation of graphite oxide
[0037] Graphite oxide was prepared by the modified Hummers method as a raw material for the preparation of hexagonal cobalt-nickel alloy-graphene composites.
[0038] Weigh 5 grams of graphite powder (Shanghai Yifan Graphite Co., Ltd.), 5 grams of NaNO 3 (Xilong Chemical Factory, Shantou City, Guangdong Province), and 230 ml concentrated H 2 SO 4 (Beijing Chemical Plant), placed in an ice-water bath, slowly added 30 grams of KMnO 4 (Tianjin Kemiou Chemical Reagent Development Company), this process takes about 15 minutes. Remove the ice-water bath, put it in a 35°C water bath, and slowly add 460 ml of distilled water. During this process for about 30 minutes, the product gradually turns from black to brown.
[0039] Then put it in a 98°C oil bath for 15 minutes.
[0040]After withdrawing from the oil bath, add 1400 ml warm water, stir, add 100 ml H 2 o 2 (Beijing Chemical P...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| concentration | aaaaa | aaaaa |
| boiling point | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a hexagonal phase nickel-cobalt alloy nanocluster-graphene composite material and a preparation method and application thereof, and belongs to the field of electromagnetic wave absorption materials. The hexagonal phase nickel-cobalt alloy nanocluster-graphene composite material with good wave absorption performance is prepared at a low cost according to the thermal decomposition method which is easy, convenient and fast to implement and good in reduction effect. The preparation method comprises the steps of (a) adding graphite oxide into 2-pyrrolidone and dispersing the graphite oxide; (b) adding cobalt acetylacetonate, nickel acetylacetonate and octadecylamine, heating the mixture to 110-140 DEG C in the atmosphere of inert protective gas, maintaining the temperature for 20-40 minutes, then heating the mixture to 230-245 DEG C, and maintaining the temperature for 1.5-2.5 hours; (c) adding an organic solvent to stop the reaction suddenly; (d) isolating a reaction product; (e) optionally washing and drying the reaction product.
Description
technical field [0001] The invention relates to the field of electromagnetic wave absorbing materials, in particular to a hexagonal phase cobalt-nickel alloy nanocluster-graphene composite material, its preparation method and application. Background technique [0002] The rapid development of wireless communication technology in industry, commerce, and military industry has brought great convenience to our life, but at the same time, it has also brought electromagnetic wave hazards. This makes it extremely urgent to prepare materials that can absorb electromagnetic waves and to study devices that can absorb electromagnetic waves. Therefore, research on materials with high absorption capacity, wide absorption range, good oxidation resistance, strong thermal stability, and low density for electromagnetic waves has attracted widespread attention. [0003] Although important progress has been made in the synthesis of magnetic particles, maintaining the stability of magnetic par...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24B22F1/00B82Y30/00B82Y40/00H05K9/00
Inventor 马淑兰潘国华孙根班马腾
Owner BEIJING NORMAL UNIVERSITY