Oil-resistant corrosion-resistant cable sheath material

A cable sheathing and corrosion-resistant technology, applied in the direction of insulated cables, cables, circuits, etc., can solve the problem of high product cost, and achieve the effects of improving heat resistance, flame retardant and smoke suppression, improving aging resistance and enhancing performance.

Inactive Publication Date: 2014-12-10
ANHUI MENTOR CABLE GROUP
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, only a few countries in the world, such as the United States, Japan, Russia and China, have installed devices, and the total global annual production capacity is about 75,000 tons, which makes the product cost too high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An oil-resistant and corrosion-resistant cable sheath material proposed by the present invention, its raw materials include by weight: 20 parts of chlorosulfonated polyethylene, 25 parts of ethylene-vinyl acetate resin, 25 parts of semi-reinforcing carbon black, light calcium carbonate 8 parts, 5 parts of titanium dioxide, 1.5 parts of antimony trioxide, 20 parts of nano-magnesium hydroxide, 15 parts of nano-clay, 1 part of polyethylene wax, 4 parts of Rhine powder 25, 1 part of antioxidant RD, 3 parts of oleic acid ester , 0.5 parts of tricresyl phosphate, 1.5 parts of dicumyl peroxide, wherein the particle size of nano magnesium hydroxide is 30-50nm;

[0016] During the preparation process, add chlorosulfonated polyethylene and ethylene-vinyl acetate resin into the internal mixer, heat to 68°C and mix for 2 minutes, then raise the temperature to 90°C, then add antimony trioxide, nano-magnesium hydroxide, Mix nanoclay, polyethylene wax, Rhine powder 25, antioxidant RD,...

Embodiment 2

[0018] An oil-resistant and corrosion-resistant cable sheath material proposed by the present invention, its raw materials include by weight: 25 parts of chlorosulfonated polyethylene, 23 parts of ethylene-vinyl acetate resin, 30 parts of semi-reinforcing carbon black, light calcium carbonate 6 parts, 6 parts of titanium dioxide, 1.2 parts of antimony trioxide, 23 parts of nano-magnesium hydroxide, 12 parts of nano-clay, 1.3 parts of polyethylene wax, 25 parts of Rhine powder, 1.2 parts of antioxidant RD, 1.3 parts of oleic acid ester , 1 part of tricresyl phosphate, 1.2 parts of dicumyl peroxide;

[0019] During the preparation process, add chlorosulfonated polyethylene and ethylene-vinyl acetate resin into the internal mixer, heat to 73°C and mix for 1 min, then raise the temperature to 100°C, then add antimony trioxide, nano-magnesium hydroxide, Mix nanoclay, polyethylene wax, Rhine powder 25, antioxidant RD, and dicumyl peroxide for 2 minutes, then add semi-reinforcing car...

Embodiment 3

[0021] An oil-resistant and corrosion-resistant cable sheath material proposed by the present invention, its raw materials include by weight: 30 parts of chlorosulfonated polyethylene, 20 parts of ethylene-vinyl acetate resin, 32 parts of semi-reinforcing carbon black, light calcium carbonate 4 parts, 7 parts of titanium dioxide, 1 part of antimony trioxide, 25 parts of nano-magnesium hydroxide, 10 parts of nano-clay, 1.5 parts of polyethylene wax, 2 parts of Rhine powder, 2 parts of antioxidant RD, 1 part of oleic acid ester , 1.5 parts of tricresyl phosphate, 1 part of dicumyl peroxide, wherein the particle size of nano magnesium hydroxide is 30-50nm;

[0022] During the preparation process, add chlorosulfonated polyethylene and ethylene-vinyl acetate resin into the internal mixer, heat to 70°C and mix for 1.5min, then raise the temperature to 95°C, then add antimony trioxide and nano-magnesium hydroxide , nanoclay, polyethylene wax, Rhine powder 25, anti-aging agent RD, dic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an oil-resistant corrosion-resistant cable sheath material which is prepared from the following raw materials in parts by weight: 20-30 parts of chlorosulfonated polyethylene, 20-25 parts of ethylene-vinyl acetate resin, 25-32 parts of semi-reinforcing carbon black, 4-8 parts of light calcium carbonate, 5-7 parts of titanium white, 1-1.5 parts of antimony trioxide, 20-25 parts of nano magnesium hydroxide, 10-15 parts of nano clay, 1-1.5 parts of polyethylene wax, 2-4 parts of Aflux 25, 1-2 parts of anti-aging agent RD, 1-3 parts of oleate, 0.5-1.5 parts of tritolyl phosphate and 1-1.5 parts of dicumyl peroxide. The oil-resistant corrosion-resistant cable sheath material has the advantages of excellent oil resistance, excellent heat resistance, excellent flame retardancy, favorable corrosion resistance and favorable aging resistance.

Description

technical field [0001] The invention relates to the technical field of cable sheaths, in particular to an oil-resistant and corrosion-resistant cable sheath material. Background technique [0002] Chlorosulfonated polyethylene is produced by chlorination and chlorosulfonation of low-density polyethylene or high-density polyethylene. It is a white or yellow elastomer, soluble in aromatic hydrocarbons and chlorinated hydrocarbons, insoluble in fats and alcohols, can only swell but not dissolve in ketones and ethers, has excellent ozone resistance, atmospheric aging resistance, and chemical corrosion resistance etc., good physical and mechanical properties, aging resistance, heat resistance and low temperature resistance, oil resistance, flame resistance, wear resistance and electrical insulation resistance. However, only a few countries in the world, such as the United States, Japan, Russia, and China, have installed devices, and the total global annual production capacity is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/34C08L23/08C08L23/06C08K13/02C08K3/04C08K3/26C08K3/22C08K3/34C08K5/14C08J3/24H01B7/17
CPCC08K2003/2241B29C35/02C08L23/0853C08L23/34H01B3/441C08L23/06C08K13/02C08K3/04C08K2003/265C08K3/2279C08K2003/2224C08K3/346
Inventor 周国庆陆书东
Owner ANHUI MENTOR CABLE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com