Preparation method of titanium dioxide pigment
A technology of titanium dioxide and silicon dioxide, applied in chemical instruments and methods, inorganic pigment treatment, fibrous fillers, etc., can solve the problems of reducing weather resistance, limited light resistance, and the presence of large phosphoric acid, etc., to achieve light resistance and weather resistance Improve and enhance the dispersion performance, the effect of adding less phosphoric acid
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0055] Example 1
[0056] a. Take 250g of the titanium dioxide initial product, pulverize it with deionized water to prepare a slurry with a concentration of 250g / L, add monoisopropanolamine to disperse to a slurry viscosity of 220cp, and adjust the pH of the slurry with sodium hydroxide solution To 9.0;
[0057] b. Heat the slurry to 85°C, add sodium silicate, the added amount of sodium silicate is SiO in the sodium silicate 2 Calculated as TiO in the slurry 2 1.5% of the mass, and acid is added in parallel to control the pH of the slurry from 9.5 to 10.0, and mature for 30 minutes;
[0058] c. The temperature of the slurry is reduced to 50°C, sodium hydrogen phosphate is added, and aluminum sulfate is added in parallel to generate aluminum phosphate, and the addition speed of sodium hydrogen phosphate and aluminum sulfate is controlled to make the slurry pH 5.0-9.0; among them, phosphoric acid The amount of sodium hydrogen added is P in sodium hydrogen phosphate 2 O 5 Counted as T...
Example Embodiment
[0062] Example 2
[0063] a. Take 300g of the initial titanium dioxide, pulverize it with deionized water to make a slurry with a concentration of 270g / L, add monoisopropanolamine to disperse to a slurry viscosity of 150cp, and add alkali to adjust the pH of the slurry to 10.0 ;
[0064] b. Heat the slurry to 87°C, add sodium silicate, the added amount of sodium silicate is SiO in sodium silicate 2 Calculated as TiO in the slurry 2 2.5% of the mass, and acid is added in parallel to control the pH of the slurry from 9.5 to 10.0, and mature for 60 minutes;
[0065] c. The temperature of the slurry is reduced to 60°C, phosphoric acid is added, and sodium metaaluminate is added in parallel to generate aluminum phosphate, and the addition speed of phosphoric acid and sodium metaaluminate is controlled to make the slurry pH 5.0-9.0; among them, phosphoric acid Adding amount is P in phosphoric acid 2 O 5 Counted as TiO in the slurry 2 1.0% of mass, curing for 60min;
[0066] d. Add sodium m...
Example Embodiment
[0069] Example 3
[0070] a. Take 350g of the titanium dioxide initial product, pulverize it with deionized water to make a slurry with a concentration of 280g / L, add sodium hexametaphosphate to disperse to a slurry viscosity of 240cp, and add alkali to adjust the pH of the slurry to 11.0;
[0071] b. Heat the slurry to 90°C, add sodium silicate, the added amount of sodium silicate is SiO in the sodium silicate 2 Counted as TiO in the slurry 2 3.5% of the mass, and acid is added in parallel to control the pH of the slurry from 9.5 to 10.0, and mature for 30 minutes;
[0072] c. The temperature of the slurry is reduced to 70°C, sodium hexametaphosphate is added, and sodium metaaluminate is added in parallel to generate aluminum phosphate, and the addition speed of sodium hexametaphosphate and sodium metaaluminate is controlled to make the slurry pH 5.0 ~9.0; Among them, the amount of sodium hexametaphosphate added is the P of sodium hexametaphosphate 2 O 5 Counted as TiO in the slurry...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap