High-strength composite inorganic artificial stone and preparing method thereof

An artificial stone and composite technology, which is applied in the field of high-strength composite inorganic artificial stone and its preparation, can solve the problems of poor aging resistance, poor alkali resistance and salt corrosion resistance, and poor high temperature resistance, and achieves environmental protection in the production process. , The effect of high product yield and high flexural strength

Inactive Publication Date: 2015-01-14
WANFENG COMPOUND STONE TECH
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, resin-type artificial stone has pungent odor in the production process, poor high temperature resistance, poor alkali and salt corrosion resistance, poor aging resistance, and easy deformation during use. High cooktops, public places with high fire protection requirements, ultraviolet radiation, outdoor environments with alternating cold and hot, etc.
[0006] Inorganic artificial synthetic stone can effectively improve the shortcomings of resin-based artificial stone. At present, the inor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The aggregate is 30%, and the aggregate can be selected from one or more of marble, quartz sand, granite, and aluminum hydroxide. The aggregate in this embodiment is selected from marble and quartz sand, and grains of quartz sand and marble aggregate The size of the diameter is according to the weight gradation of the aggregate. The particle size of the quartz sand aggregate is 1~4mm accounting for 1.5% of the weight of the aggregate, and the particle size of the marble aggregate has a sieve number of 20 to 80 mesh, which accounts for 29% of the weight of the aggregate. The particle size of the marble aggregate with a sieve number of 80-200 mesh accounts for 31.5% of the aggregate weight, and the particle size of the marble aggregate with a sieve number of 200-400 mesh accounts for 38% of the aggregate weight. The cement is 48%. The cements used in this embodiment are ordinary Portland cement and sulphur-aluminum cement. Ordinary Portland cement accounts for 40% of the ce...

Embodiment 2

[0034] Aggregate is 30%. Granite is selected as the aggregate. The size of the granite is according to the weight gradation of the aggregate. The size of the granite aggregate is 1-10mm, which accounts for 1% of the weight of the aggregate. The particle size of the aggregate is 20-80 mesh, which accounts for 20% of the weight of the aggregate. The particle size of the granite aggregate is 80-200 mesh, which accounts for 35% of the weight of the aggregate. The particle size of the sieve is 200-400 mesh, accounting for 44% of the aggregate weight. The cement is 60%, and the cement used in this embodiment is ordinary Portland white cement. The compound modifier is 1%, and the compound modifier is one or more of VAE compound modifier, rubber compound modifier, 1~3mm glass fiber, epoxy resin modifier or high active filler Among them, the VAE compound modifier includes ethylene-vinyl acetate copolymer emulsion, vinyl acetate-vinyl ester-ethylene copolymer latex powder, vinyl acetate...

Embodiment 3

[0037] The aggregate is 65%. The aggregate is made of marble. The particle size of the marble aggregate is according to the weight gradation of the aggregate. The particle size of the marble aggregate is 1-10mm accounting for 3.5% of the weight of the aggregate. The particle size of the marble aggregate is other The sieve number is 20-80 mesh, accounting for 46% of the aggregate weight, the size of the marble aggregate is 80-200 mesh, accounting for 20% of the aggregate weight, and the size of the marble aggregate is 200-400 The purpose accounts for 30.5% of the aggregate weight. The cement is 25%, and the cement used in this embodiment is ordinary Portland cement. The compound modifier is 1%, and the compound modifier is one of VAE compound modifier, rubber compound modifier, 1~3mm glass fiber modifier, epoxy resin modifier or high active filler Or more, of which, the VAE compound modifier includes ethylene-vinyl acetate copolymer emulsion, vinyl acetate-vinyl ester-ethylene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength composite inorganic artificial stone and a preparing method thereof; the inorganic artificial stone comprises the following components by the weight percentage: 30-65% of aggregates, 25-60% of cement, 1-10% of a composite modifying agent, 1-5% of a water reducing agent, 0-1.5% of a retarder, and 8-20% of water, wherein the particle sizes of the aggregates are graded according to the weight of the aggregates. The preparing method of the inorganic artificial stone comprises the steps: successively adding the aggregates with predetermined weight particle size graduation, the cement, the composite modifying agent and the water reducing agent into a stirrer successively, uniformly stirring, adding an appropriate weight of water, then uniformly stirring, distributing the material and pressing under a vacuum state, carrying out wet culture and curing, cutting, and polishing to obtain the product. The inorganic artificial stone has the advantages of high bending strength, environmental-protection production process, lower cost, high yield rate of the product, outstanding performance and the like.

Description

technical field [0001] The invention relates to an inorganic artificial stone, in particular to a high-strength composite inorganic artificial stone and a preparation method thereof. Background technique [0002] Artificial stone is a new type of non-radioactive, non-polluting, reusable, green and environmentally friendly building interior decoration material. As a new strategic health and environmental protection product in line with the country's sustainable development, it was introduced into the domestic market in the 1980s. The artificial stones currently on the market are mainly organic artificial stones with polymer resin materials as adhesives, which are mainly divided into three categories: artificial marble (referred to as artificial granite), artificial quartz stone and acrylic. Although our country started late in the artificial stone industry, after more than 20 years of rapid development, it ranks among the top in the world in terms of market size and applicat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B28/06C04B20/00
Inventor 林志伟尹兴肖绍展蔡鹏江浩王波
Owner WANFENG COMPOUND STONE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap