Rubber for lifting rings for automobile exhaust pipes

An automobile exhaust and rubber technology, which is applied in the field of rubber for automobile exhaust pipe suspension rings, can solve problems such as poor high temperature resistance, and achieve the effect of improving heat resistance and aging resistance

Inactive Publication Date: 2015-01-14
LIUZHOU YINGHANG AUTO PARTS
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a kind of rubber for the suspension ring of automobile exhaust pipe, which can be used to prepare the suspension ring of automobile exhaust pipe, which can solve the problem of poor high temperature resistance of the suspension ring of automobile exhaust pipe prepared in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The rubber used for the suspension ring of the automobile exhaust pipe adopts the following raw materials: EPDM rubber 6.0kg; chlorosulfonated polyethylene rubber 4.0kg; Zhongchao carbon black N200 1.0kg; general furnace black N660 2.5kg; indirect method zinc oxide 0.5kg ; Tetramethylthiuram disulfide 0.3kg; Tetraethylthiuram disulfide 0.1kg; 2-thiol benzimidazole 0.2kg; Zinc stearate 0.1kg; Benzothiazole 0.5kg; Trimeric thiocyanate 0.05kg; Paraffin oil 1.5kg; Magnesium strong powder 0.5kg; Sulfur 0.02kg;

[0012] Its preparation method comprises the following steps: first, EPDM rubber, chlorosulfonated polyethylene rubber, Zhongchao carbon black N200, general furnace black N660, indirect method zinc oxide, 2-thiol benzimidazole, 2. Put 2'-dithiodibenzothiazole, paraffin oil and magnesium powder into the internal mixer for banburying. After the banburying, control the glue temperature below 120°C to discharge the glue to obtain the masterbatch; then put The masterbatch...

Embodiment 2

[0015] The rubber used for the suspension ring of the automobile exhaust pipe adopts the following raw materials: EPDM rubber 6.0kg; chlorosulfonated polyethylene rubber 4.0kg; Zhongchao carbon black N200 1.5kg; general furnace black N660 2.0kg; indirect method zinc oxide 1.0kg ; Tetramethylthiuram disulfide 0.2kg; Tetraethylthiuram disulfide 0.2kg; 2-thiol benzimidazole 0.1kg; Zinc stearate 0.03kg; Benzothiazole 0.3kg; Trimeric thiocyanate 0.08kg; Paraffin oil 1.0kg; Magnesium strong powder 1.0kg; Sulfur 0.01kg;

[0016] Its preparation method comprises the following steps: first, EPDM rubber, chlorosulfonated polyethylene rubber, Zhongchao carbon black N200, general furnace black N660, indirect method zinc oxide, 2-thiol benzimidazole, 2. Put 2'-dithiodibenzothiazole, paraffin oil and magnesium powder into the internal mixer for banburying. After the banburying, control the glue temperature below 120°C to discharge the glue to obtain the masterbatch; then put The masterbatc...

Embodiment 3

[0019] The rubber used for the suspension ring of the automobile exhaust pipe adopts the following raw materials: EPDM rubber 6.0kg; chlorosulfonated polyethylene rubber 4.0kg; Zhongchao carbon black N200 1.2kg; general furnace black N660 2.2kg; indirect method zinc oxide 0.8kg ; Tetramethylthiuram disulfide 0.25kg; Tetraethylthiuram disulfide 0.15kg; 2-thiol benzimidazole 0.15kg; Zinc stearate 0.2kg; Benzothiazole 0.4kg; Trimeric thiocyanate 0.06kg; Paraffin oil 1.4kg; Magnesium strong powder 0.7kg; Sulfur 0.015kg;

[0020] Its preparation method comprises the following steps: first, EPDM rubber, chlorosulfonated polyethylene rubber, Zhongchao carbon black N200, general furnace black N660, indirect method zinc oxide, 2-thiol benzimidazole, 2. Put 2'-dithiodibenzothiazole, paraffin oil and magnesium powder into the internal mixer for banburying. After the banburying, control the glue temperature below 120°C to discharge the glue to obtain the masterbatch; then put The masterb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses rubber for lifting rings for automobile exhaust pipes, which belongs to the technical field of rubber pipe products for automobiles. The rubber disclosed by the invention is prepared from ethylene-propylene-diene-terpolymer rubber, chlorosulfonated polyethylene rubber, intermediate super carbon black N200, general furnace black N660, indirect zinc oxide, tetramethyl thiuram disulfide, tetraethylthiuram disulfide, 2-mercaptobenzimidazole, zinc stearate, 2,2'-Dithio-dibenzo thiazole, a trithiocyanuric acid, paraffin oil, magnesium powder, and sulphur as raw materials in parts by weight. Compared with rubber for lifting rings for automobile exhaust pipes manufactured in the prior art, when the rubber disclosed by the invention is used for preparing lifting rings for automobile exhaust pipes by using the mutual synergistic effect of the raw materials, the heat resistance of the lifting rings for automobile exhaust pipes is effectively improved, and the aging resistance of the lifting rings for automobile exhaust pipes is also promoted.

Description

technical field [0001] The invention relates to the technical field of rubber hose products for automobiles, in particular to a rubber used for suspension rings of automobile exhaust pipes. Background technique [0002] In terms of the role of the automobile exhaust pipe on the automobile body, it plays the role of shock absorption and noise reduction, and prolongs the life of the exhaust muffler system. The main material of the exhaust pipe is stainless steel. For ordinary cars, because the exhaust gas of the car is under great pressure when it leaves the engine, the noise it produces may make people feel crazy. At this time, the main role of noise reduction is the exhaust pipe of the car. The device greatly reduces the noise of the car. The main function of the automobile exhaust pipe suspension ring is to fix the exhaust pipe to reduce the vibration generated by the exhaust pipe during movement and prevent the collision between the exhaust pipe and the chassis of the ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L23/34C08K13/02C08K3/04C08K3/22C08K5/40C08K5/37C08K5/098C08K5/47C08K3/06
CPCC08L23/16C08K2201/014C08L2201/08C08L2205/02C08L2205/03
Inventor 陈永亮
Owner LIUZHOU YINGHANG AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com