High-temperature wear-resisting coating for casting and preparation method thereof

A high-temperature wear-resistant and coating technology, applied in casting molding equipment, coatings, molds, etc., can solve problems such as large thermal conductivity, poor thermal conductivity, and affecting the service life of models

Active Publication Date: 2015-02-04
YANCHENG AOTONG TESCO FOUNDRY CO LTD
View PDF6 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of the machinery industry, the requirements for casting coatings are getting higher and higher. However, the existing coatings have high thermal conductivity and poor thermal conductivity, which affects the service life of the model and reduces the quality of castings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment provides a high-temperature wear-resistant coating for casting, and the coating includes the following components in parts by mass:

[0025] Quartz: zircon powder: diatomaceous earth = 1:1.5:1 weight ratio mixture: 15 parts, water and isopropanol: 22 parts, polyester polyethylene emulsion: 1 part, sodium carboxymethylcellulose: sodium Base bentonite = 1.2: 1.5 weight ratio mixture: 5 parts, 4 parts of additives; additives include fatty alcohol polyvinyl ether, organic silicon and sodium chlorophenate.

[0026] The preparation method of the above-mentioned high-temperature wear-resistant coating for casting specifically includes the following steps:

[0027] (1) Put sodium carboxymethyl cellulose, sodium bentonite, water and isopropanol in a disperser and stir for 20 minutes at a stirring speed of 250 rpm;

[0028] (2) Visually inspect the mixture of sodium carboxymethyl cellulose, sodium bentonite, water and isopropanol stirred in step (1) when it is in...

Embodiment 2

[0030] This embodiment provides a high-temperature wear-resistant coating for casting, and the coating includes the following components in parts by mass:

[0031] Quartz: zircon powder: diatomaceous earth = 1:1.5:1 weight ratio mixture: 17 parts, water and isopropanol: 25 parts, polyvinyl alcohol: 3 parts, sodium carboxymethyl cellulose: sodium bentonite =1.2:1.5 weight ratio mixture: 3 parts, auxiliary agent: 6 parts; auxiliary agent is sodium dodecylbenzenesulfonate, amide and sodium chlorophenate.

[0032] The preparation method of the above-mentioned high-temperature wear-resistant coating for casting specifically includes the following steps:

[0033] (1) Put sodium carboxymethyl cellulose, sodium bentonite, water and isopropanol in a disperser and stir for 25 min at a stirring speed of 250 rpm;

[0034] (2) When the mixture of sodium carboxymethyl cellulose, sodium bentonite, water and isopropanol stirred in step (1) is visually in slurry form, add quartz, zircon powde...

Embodiment 3

[0036] This embodiment provides a high-temperature wear-resistant coating for casting, and the coating includes the following components in parts by mass:

[0037] Quartz: zircon powder: diatomaceous earth = 1:1.5:1 weight ratio mixture: 18 parts, water and isopropanol: 20 parts, water-soluble phenolic resin: 2 parts, sodium carboxymethyl cellulose: sodium base Bentonite=1.2:1.5 weight ratio mixture: 2 parts, auxiliary agent: 3 parts; the auxiliary agent is alkylbenzenesulfonic acid, polyether and sodium chlorophenate.

[0038] The preparation method of the above-mentioned high-temperature wear-resistant coating for casting specifically includes the following steps:

[0039] (1) Put sodium carboxymethyl cellulose, sodium bentonite, water and isopropanol in a disperser and stir for 22 minutes at a stirring speed of 250 rpm;

[0040] (2) Visually inspect the mixture of sodium carboxymethyl cellulose, sodium bentonite, water and isopropanol stirred in step (1) and when it is in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
flame retardantaaaaaaaaaa
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature wear-resisting coating for casting and a preparation method thereof. The coating comprises the following components: a fireproof material, a carrier, a bonding agent, a suspension agent and an auxiliary agent. The invention further designs the preparation method of the high-temperature wear-resisting coating for casting. The preparation method comprises the following steps: putting the suspension agent and the carrier into a dispersion machine and uniformly agitating; then adding the fireproof material and continually agitating; and slowly adding the bonding agent and the auxiliary agent in sequence under an agitating state; and agitating uniformly to obtain the high-temperature wear-resisting coating for casting. The high-temperature wear-resisting coating for casting is low in price, and is clean and is free from pollution; the preparation method is simple and the coating is high temperature resistant and wear resistant and is not easy to release; and a die for casting can be protected and the quality of a casting piece can be improved.

Description

technical field [0001] The invention relates to a coating and a preparation method thereof, in particular to a high-temperature wear-resistant coating for casting and a preparation method thereof, belonging to the technical field of casting. Background technique [0002] Foundry coating refers to a covering that is applied on the surface of the mold cavity or core to improve its surface refractoriness, chemical stability, metal erosion resistance, sand sticking resistance and other properties. Coating is the most effective measure to solve the sand sticking on the surface of castings and improve the surface quality of castings. The purpose of spraying paint on the casting model is to adjust the thermal specification of the system, prevent the cavity surface from direct contact with the molten metal, affect the structure and performance of the casting, facilitate machining, improve the surface quality and flatness of the casting, and make the molten metal It is easy to fill ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
CPCB22C3/00
Inventor 吴卫明吴正平
Owner YANCHENG AOTONG TESCO FOUNDRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com