Anion anti-oxidation coating for automotive leaf spring and preparation method of anion anti-oxidation coating

A technology for anti-oxidation coatings and automotive springs, applied in epoxy resin coatings, anti-corrosion coatings, polyurea/polyurethane coatings, etc., can solve problems such as insufficient corrosion resistance, insufficient stability and solvent resistance, and achieve cost reduction Low cost, improved anti-corrosion and hydrolysis resistance, and easy operation

Active Publication Date: 2015-02-18
SHANDONG LEOPARD AUTOMOTIVE HLDG
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, epoxy resin, glycoluril resin, etc. are commonly used as agents for chromate for surface treatment, but because the formed organi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anion anti-oxidation coating for automotive leaf spring and preparation method of anion anti-oxidation coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1: The invention provides a kind of anion anti-oxidation coating that is used for automobile spring steel plate, is made up of the component of following parts by weight:

[0048] 50 parts of butylated hydroxyl polyurethane;

[0049] Epoxy resin E44 10 parts;

[0050] Epoxy resin E51 10 parts;

[0051] 8 parts of zinc oxide powder;

[0052] 10 parts of alumina powder;

[0053] Tourmaline powder 10 parts;

[0054] 3 parts of 2,4-di-tert-butylphenol;

[0055] Acrylate 2 parts;

[0056] 3 parts of polydimethylsiloxane acrylate;

[0057] 3 parts of propylene glycol butyl ether;

[0058] 5 parts of propylene glycol methyl ether acetate;

[0059] 2 parts aluminum stearate;

[0060] 3 parts of polyoxypropylene propylene glycol ether;

[0061] 4 parts of methyl silicone oil.

[0062] 3 parts of silane coupling agent;

[0063] 1 part of melamine.

[0064] The present invention is used for the anion anti-oxidation coating of automobile spring steel plate...

Embodiment 2

[0067] Embodiment 2:The invention provides a kind of anion anti-oxidation coating that is used for automobile spring steel plate, is made up of the component of following parts by weight:

[0068] 55 parts of butylated hydroxyl polyurethane;

[0069] Epoxy resin E44 12 parts;

[0070] Epoxy resin E51 13 parts;

[0071] 12 parts of zinc oxide powder;

[0072] 24 parts of alumina powder;

[0073] Tourmaline powder 13 parts;

[0074] 4 parts of 2,4-di-tert-butylphenol;

[0075] Acrylate 3 parts;

[0076] 5 parts of polydimethylsiloxane acrylate;

[0077] 4 parts of propylene glycol butyl ether;

[0078] 6 parts of propylene glycol methyl ether acetate;

[0079] 3 parts aluminum stearate;

[0080] 4 parts of polyoxypropylene propylene glycol ether;

[0081] 5 parts of methyl silicone oil.

[0082] 3 parts of silane coupling agent;

[0083] 1 part of melamine.

[0084] The present invention is used for the anion anti-oxidation coating of automobile spring steel plate...

Embodiment 3

[0087] Embodiment 3: The invention provides a kind of anion anti-oxidation coating that is used for automobile spring steel plate, is made up of the component of following parts by weight:

[0088] 60 parts of butylated hydroxyl polyurethane;

[0089] Epoxy resin E44 14 parts;

[0090] Epoxy resin E51 16 parts;

[0091] 14 parts of zinc oxide powder;

[0092] 30 parts of alumina powder;

[0093] Tourmaline powder 15 parts;

[0094] 6 parts of 2,4-di-tert-butylphenol;

[0095] Acrylate 4 parts;

[0096] 6 parts of polydimethylsiloxane acrylate;

[0097] 5 parts of propylene glycol butyl ether;

[0098] 7 parts of propylene glycol methyl ether acetate;

[0099] 5 parts of aluminum stearate;

[0100] 4 parts of polyoxypropylene propylene glycol ether;

[0101] 6 parts of methyl silicone oil.

[0102] 4 parts of silane coupling agent;

[0103] 2 parts of melamine.

[0104] The present invention is used for the anion anti-oxidation coating of automobile spring steel ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anion anti-oxidation coating for an automotive leaf spring and a preparation method of the anion anti-oxidation coating, and belongs to the field of anti-oxidation coatings. The epoxy resin is improved by adopting polyurethane resin, so that the anticorrosion ability and the hydrolysis resistance are improved, and the oxidation resistance of the product is excellent. Butyl hydroxy polyurethane adopted by the invention is synthesized by olefine dihydric alcohol and toluene diisocynate; and relative to polyether or polyester polyurethane, butyl hydroxy polyurethane has relatively good stability, hydrolysis resistance and corrosion resistance due to stable main chain structure. The tourmaline contained in the coating can automatically release anions, has the environment-friendly function, can be used or effectively removing harmful pollutants in air, and is beneficial to air purification and human health; and the anion anti-oxidation coating is simple in preparation process, convenient to operate and low in cost.

Description

technical field [0001] The invention relates to a preparation method of an anti-oxidation coating, in particular to an anion anti-oxidation coating used for automobile spring steel plates and a preparation method thereof. Background technique [0002] Automotive spring steel plate, also known as leaf spring, is the most widely used elastic element in automobile suspension. It is an elastic beam of approximately equal strength composed of several alloy spring sheets of equal width but unequal length. Spring steel plates are primarily used to transmit vertical forces and to moderate shocks and vibrations caused by uneven road surfaces. Its advantages are simple structure, reliable operation, low cost and convenient maintenance. It is both the elastic element of the suspension and the guiding device of the suspension. One end of it is hinged with the frame, which can transmit various forces and moments, and determine the beating track of the wheel. However, when the spring s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/14C09D163/00C09D5/08C09D7/12C08G18/76C08G18/69
CPCC08G18/69C08G18/7614C08L2205/035C09D5/08C09D7/61C09D7/63C09D7/65C09D175/14C08L63/00C08L83/04C08L71/00C08K13/02C08K2003/2296C08K2003/2227C08K3/38C08K5/098C08K5/34922
Inventor 丁烨赵昱王宁李帅
Owner SHANDONG LEOPARD AUTOMOTIVE HLDG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap