Self-cleaning antibacterial fluorocarbon coating

A fluorocarbon coating and self-cleaning technology, applied in the field of coatings, can solve the problems that fluorocarbon coatings do not have a self-cleaning function, and the stain resistance and antibacterial properties cannot meet the requirements of high antibacterial and strong self-cleaning, so as to improve the self-cleaning performance and improve the The effect of photocatalytic efficiency and strong self-cleaning ability

Inactive Publication Date: 2015-03-11
ANHUI JINDUN PAINT
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although ordinary fluorocarbon resin has excellent gloss and color retention, fluorocarbon coating itself does not have self-cleaning fu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The self-cleaning antibacterial fluorocarbon coating of the present invention, its raw material comprises the following components by weight: 40 parts of fluorine-containing polyacrylic resin, 13 parts of silane coupling agent, 6 parts of amino resin, 15 parts of titanium dioxide, 2 parts of calcium carbonate , 10 parts of modified nano titanium dioxide, 6 parts of silicon nitride, 8 parts of zinc molybdate, 10 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 5-chloro-2- 0.3 parts of methyl-4-isothiazolin-3-one, 1.2 parts of defoamer, 1.8 parts of wetting agent, 0.3 parts of leveling agent, 1.5 parts of curing agent, and 30 parts of solvent.

Embodiment 2

[0022] The self-cleaning antibacterial fluorocarbon coating of the present invention, its raw material comprises the following components by weight: 60 parts of fluorine-containing polyacrylic resin, 5 parts of silane coupling agent, 1 part of amino resin, 3 parts of titanium dioxide, 6 parts of calcium carbonate , 28 parts of modified nano titanium dioxide, 2 parts of silicon nitride, 2 parts of zinc molybdate, 5 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 5-chloro-2- 1.2 parts of methyl-4-isothiazolin-3-one, 0.2 parts of defoamer, 0.5 parts of wetting agent, 0.8 parts of leveling agent, 0.6 parts of curing agent, 60 parts of solvent;

[0023] Wherein, the solvent is a combination of cyclohexane, acetone, and n-butanol in a ratio of 1:4:2 parts by weight;

[0024] The fluorine-containing polyacrylic acid resin is prepared according to the following process: by weight, 12 parts of cyclohexyl methacrylate, 20 parts of α-ethyl bromopropionate, 10 parts of cuprous i...

Embodiment 3

[0027] The self-cleaning antibacterial fluorocarbon coating of the present invention, its raw material comprises the following components by weight: 47.6 parts of fluorine-containing polyacrylic resin, 12 parts of silane coupling agent, 4.5 parts of amino resin, 7.8 parts of titanium dioxide, 3.2 parts of calcium carbonate , 12.6 parts of modified nano titanium dioxide, 4.2 parts of silicon nitride, 3.4 parts of zinc molybdate, 6.4 parts of 2,2,4-trimethyl-1,3 pentanediol monoisobutyrate, 5-chloro-2- 0.74 parts of methyl-4-isothiazolin-3-one, 0.8 parts of defoamer, 1.1 parts of wetting agent, 0.45 parts of leveling agent, 0.73 parts of curing agent, and 55.6 parts of solvent;

[0028] Wherein, the solvent is propylene glycol;

[0029] The fluorine-containing polyacrylic acid resin is prepared according to the following process: by weight, 18 parts of cyclohexyl methacrylate, 15 parts of α-ethyl bromopropionate, 15 parts of cuprous iodide and 18 parts of pentamethyldiethylene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a self-cleaning antibacterial fluorocarbon coating which comprises the following components in parts by weight: 40-60 parts of fluorine-containing polyacrylate resin, 5-13 parts of a silane coupling agent, 1-6 parts of amino resin, 3-15 parts of titanium dioxide, 2-6 parts of calcium carbonate, 10-28 parts of modified nano titanium dioxide, 2-6 parts of silicon nitride, 2-8 parts of zinc molybdate, 5-10 parts of 2,2,4-trimethyl-1,3-pentanediol isobutyrate, 0.3-1.2 parts of 5-chloro-2-methl-4-isothiazolin-3-ketone, 0.2-1.2 parts of defoaming agent, 0.5-1.8 parts of wetting agent, 0.3-0.8 parts of flatting agent, 0.6-1.5 parts of a curing agent and 30-60 parts of a solvent. The self-cleaning antibacterial fluorocarbon coating disclosed by the invention is high in self-cleaning ability and good in antibacterial property and can be applied in building outer walls.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a self-cleaning antibacterial fluorocarbon coating. Background technique [0002] Fluorocarbon coatings mainly refer to coatings with special functions that use pure fluororesin or modified fluororesin as the main film-forming substance, showing excellent amphobia, weather resistance, durability, acid and alkali resistance, and corrosion resistance. , insulation and non-adhesion, etc., which are beyond the reach of other common coatings, so researchers call it an excellent new type of special coating. Although ordinary fluorocarbon resin has excellent gloss and color retention, fluorocarbon coating itself does not have self-cleaning function, and its stain resistance and antibacterial properties cannot meet the requirements of high antibacterial and strong self-cleaning. Contents of the invention [0003] The invention provides a self-cleaning and antibacterial fluorocarbon c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/16C09D161/20C09D7/12C09D5/14C08F220/22C08F220/18C08F220/28
CPCC08F220/22C08K2201/011C09D5/14C09D7/61C09D7/62C09D7/63C09D133/16C08L61/20C08K13/06C08K9/06C08K2003/2241C08K2003/265C08K3/34C08K3/24C08K5/47C08F220/1806C08F220/281
Inventor 朱恒衡梅长林胡兰
Owner ANHUI JINDUN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap