A sheath-core composite fiber containing tourmaline

A composite fiber and tourmaline technology, applied in the field of fibers, can solve the problems of comfort and environmental protection, antibacterial and breathable service life needs to be improved, etc., and achieve the effects of comfortable mood, high air ion concentration, and difficult to agglomerate

Active Publication Date: 2016-05-04
HEYE HEALTH TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the core material still needs to be improved in terms of comfort, environmental protection, antibacterial ventilation and service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A sheath-core composite fiber containing tourmaline
  • A sheath-core composite fiber containing tourmaline
  • A sheath-core composite fiber containing tourmaline

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] The preparation method of lignocellulose airgel liquid is:

[0056] a. crushing: crushing and sieving lignocellulosic biomass;

[0057] b. Purification: Dissolve the crushed and sieved lignocellulosic biomass in an alkaline aqueous solution system composed of polyethylene glycol, sodium hydroxide and water at a mass ratio of 60:1:100 for degradation and purification for 12 hours, so that the purified The residual lignin content is less than 3%; the mass ratio of lignocellulosic biomass to mixed liquor is 15:100;

[0058] c. Freezing and thawing: separate and purify the lignocellulosic biomass solution to obtain lignocellulose, place the lignocellulose in an aqueous solution of sodium hydroxide-urea, and freeze and thaw at low temperature and thaw at room temperature to obtain lignocellulose solution;

[0059] The mass ratio of sodium hydroxide to urea is 9:10;

[0060] The cryogenic temperature is -15°C;

[0061] The melting temperature at room temperature is 35°C; ...

Embodiment 2

[0073] Preparation of sheath-core composite fibers containing tourmaline:

[0074] Tourmaline treatment: Surface treatment of tourmaline powder with a particle size of ≤0.5 microns with titanate and octylphenol polyoxyethylene ether mixed at a mass ratio of 1:2; the mass ratio of coupling agent to tourmaline powder is 4:100 ;

[0075] Core material processing: the hemp fiber and the mountain palm fiber are processed through degumming, then carded and shortened into short hemp fiber and short brown fiber, then the short hemp fiber of 40 parts by weight and the short brown fiber of 50 parts by weight are combined in 400 parts by weight Lignocellulosic airgel liquid is mixed and impregnated for 20min, then taken out and drained and sent to the opener for opening and mixing; after opening, the short hemp fibers and short palm fibers are evenly dropped from the drum groove through the airflow , arranged uniformly to form figure 1 The net-like semi-finished product with S-shaped c...

Embodiment 3

[0080] Preparation of sheath-core composite fibers containing tourmaline:

[0081] Tourmaline treatment: Surface treatment of tourmaline powder with a particle size of ≤0.5 microns with titanate and octylphenol polyoxyethylene ether mixed at a mass ratio of 1:2.5; the mass ratio of coupling agent to tourmaline powder is 3:100 ;

[0082] Core material processing: the hemp fiber and the mountain palm fiber are processed through degumming, then carded and shortened into short hemp fiber and short brown fiber, and then the short hemp fiber of 35 parts by weight and the short brown fiber of 40 parts by weight are combined at 300 weight parts Lignocellulosic airgel liquid is mixed and impregnated for 18min, then taken out and drained and sent to the opener for opening and mixing; after opening, the short hemp fibers and short palm fibers are evenly dropped from the drum groove through the airflow , arranged uniformly to form figure 1 The net-like semi-finished product with S-shape...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to fibers, in particular to tourmaline-containing sheath-core composite fibers. The tourmaline-containing sheath-core composite fibers are prepared through the following steps: (1) tourmaline processing; (2) core layer material processing, that is, bast fibers and palm fibers after degumming processing are combed and cut into short bast fibers and short palm fibers, the short bast fibers and the short palm fibers are then soaked in a mixed manner in a lignocellulose aerogel solution for 15 to 20 minutes according to a formula, the short bast fibers and the short palm fibers after the mixed soaking are then taken out for draining, the short bast fibers and the short palm fibers after the draining are sent to an opener for opening and mixing, the short bast fibers and the short palm fibers after the opening and mixing pass through airflows and are arranged through a roller groove to form meshed semi-products with S-shaped section structures, and the meshed semi-products go through spunlace to form non-woven needled bast-palm fiber aerogel core layer materials; (3) sheath layer material processing, that is, a first pulp is prepared from processed tourmalines and ethylene glycol, phthalic acid and glycerol are used for esterification reaction, the first pulp, magnesium oxide and calcium hydroxide are added after the reaction for condensation polymerization, and polyester chip sheath layer materials are obtained through strip casting and sized dicing; (4) composite melt spinning for obtaining of the tourmaline-containing sheath-core composite fibers. The tourmaline-containing sheath-core composite fibers provided by the invention achieve the antibacterial and healthcare effects, high degree of comfort, as well as environment friendliness.

Description

technical field [0001] The invention relates to a fiber, in particular to a sheath-core composite fiber containing tourmaline. Background technique [0002] Hemp fiber is a natural cellulose fiber with outstanding product characteristics, low production cost, and low requirements on production conditions. It can grow in tidal flats and low-lying places, and does not compete with grain and cotton for land. The dependence on pesticides is low. [0003] CN101343815B (2012-7-4) discloses a silk hemp fiber mixed filling core material, the silk hemp fiber mixed filling core material body is made of hemp fiber and silk mixed fiber, the silk hemp fiber mixed filling hemp fiber in the core material The mass percent content is 20-60%. However, the core material still needs to be improved in terms of comfort and environmental protection, antibacterial ventilation and service life. Contents of the invention [0004] The object of the present invention is to provide a sheath-core co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/02D01F8/14D01F1/10D01D5/34D01D5/08D06M15/01D06M13/342D06M13/188D06M10/00D06M13/165D06M13/192D06M13/148D06M15/693D06M13/224D06M13/232D06M15/03D06M11/83D06M11/74D06M15/09C08F289/00C08F220/06D06M101/06
Inventor 李俊胡立江方志财蔡京昊
Owner HEYE HEALTH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com