A kind of water-based ultra-thin fireproof and thermal insulation material and preparation method thereof

A fire-proof and heat-preservation, ultra-thin technology, applied in the field of fire-proof and heat-preservation materials, can solve the problems of difficult construction, poor fireproof performance, high cost, etc., and achieve the goal of reducing construction cost and construction difficulty, reducing work intensity and pressure, and high fire-proof and heat-preservation quality Effect

Active Publication Date: 2016-09-07
赵丽芳
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, EPS boards and XPS boards have disadvantages such as poor fire resistance, weak bonding, and easy hanging.
The production process of cement foam insulation board is complicated, and construction personnel are required to measure and cut boards at special-shaped structural parts, which makes construction difficult and costly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A water-based ultra-thin fireproof and thermal insulation material, which comprises the following components by weight percentage:

[0034] Expanded Basalt Granules 40%

[0035] water 15%

[0036] Composite resin 40%

[0037] Stabilizer 1.5%

[0038] Dispersant 0.5%

[0039] Leveling agent 0.5%

[0040] Thickener 0.5%

[0041] Defoamer 0.5%

[0042] Insulation material MAS 1.5%;

[0043] Wherein, the expanded basalt particles are silica hollow microspheres with a thermal conductivity of 0.029W / (m K) and a dry density of 278kg / m 3 , the solar reflectance is 0.85, and the hemispherical emissivity is 0.86; the composite resin is a composite resin of a potassium silicate liquid ceramic binder and a silane coupling agent with a modulus of 5.1 to 5.4; the stabilizer is B Diol; the dispersant is stearic acid; the leveling agent is polyether modified polyacrylate; the thickener is the cross-linked polymer thickener ASE-60 containing acidic groups ; The defoamer is mine...

Embodiment 2

[0050] A water-based ultra-thin fireproof and thermal insulation material, which comprises the following components by weight percentage:

[0051] Expanded Basalt Granules 20%

[0052] water 15%

[0053] Composite resin 60%

[0054] Stabilizer 1.5%

[0055] Dispersant 0.9%

[0056] Leveling agent 0.2%

[0057] Thickener 0.2%

[0058] Defoamer 0.2%

[0059] Insulation material MAS 2%;

[0060] Wherein, the expanded basalt particles are silica hollow microspheres with a thermal conductivity of 0.029W / (m K) and a dry density of 278kg / m 3 , the solar reflectance is 0.85, and the hemispherical emissivity is 0.86; the composite resin is a composite resin of a potassium silicate liquid ceramic binder with a modulus of 5.1 to 5.4 and a silane coupling agent; the stabilizer is propylene glycol The dispersant is sodium dodecylbenzene sulfonate; the leveling agent is polyether modified polyacrylate; the thickener is non-ionic associative synergistic rheological agent STZC-920; T...

Embodiment 3

[0064] A water-based ultra-thin fireproof and thermal insulation material, which comprises the following components by weight percentage:

[0065] Expanded Basalt Granules 30%

[0066] Water 26%

[0067] Composite resin 35%

[0068] Stabilizer 3%

[0069] Dispersant 1.8%

[0070] Leveling agent 0.2%

[0071] Thickener 0.5%

[0072] Defoamer 0.5%

[0073] Insulation material MAS 3%

[0074] Wherein, the expanded basalt particles are silica hollow microspheres with a thermal conductivity of 0.029W / (m K) and a dry density of 278kg / m 3 , the solar reflectance is 0.85, and the hemispherical emissivity is 0.86; the composite resin is a composite resin of a potassium silicate liquid ceramic binder and a silane coupling agent with a modulus of 5.1 to 5.4; the stabilizer is B Diol; the dispersant is sodium dodecylbenzenesulfonate; the leveling agent is a polyether modified polyacrylate; the thickener is a non-ionic associative synergistic rheological agent STZC- 920; the defoa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water-borne ultrathin type fireproof heat insulating material and a preparation method thereof. The water-borne ultrathin type fireproof heat insulating material comprises the following components in percentage by weight: 20-40% of puffed basalt particles, 15-30% of water, 35-60% of composite resin, 1.5-3% of a stabilizer, 0.5-1.8% of a dispersant, 0.2-0.5% of a leveling agent, 0.2-0.5% of a thickening agent, 0.2-0.5% of a defoaming agent and 1.5-3% of a heat insulating material MAS. The water-borne ultrathin type fireproof heat insulating material disclosed by the invention is green and environment-friendly, does not release formaldehyde, benzene and other harmful gases, and is stable in performance and high in fireproof heat insulating quality. The water-borne ultrathin type fireproof heat insulating material is simple in preparation process and wide in application range, the problem of high manufacturing cost of EPS, XPS and cement foamed heat insulating plates is solved, meanwhile the working strength and stress of constructors are relieved, the construction difficulty during measuring of special shaped structural parts, cutting of plates and the like by the constructers is reduced, and the construction cost and constriction difficulty are reduced at the same time.

Description

technical field [0001] The invention relates to a fireproof heat preservation material, in particular to a water-based ultra-thin fireproof heat preservation material and a preparation method thereof. Background technique [0002] With the development of economy and society, people pay more and more attention to the functions of building materials such as heat preservation, energy saving, environmental protection and fire prevention. At present, the insulation materials used mainly include EPS board (benzene board), XPS (polystyrene insulation board), and cement foam insulation board. However, EPS boards and XPS boards have disadvantages such as poor fire resistance, weak bonding, and easy hanging. The manufacturing process of the cement foam insulation board is complicated, and construction personnel are required to measure and cut the board at the special-shaped structure, so the construction is difficult and the cost is high. Contents of the invention [0003] In orde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/32
Inventor 赵丽芳
Owner 赵丽芳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap