One-component deoximation type room-temperature vulcanized silicone rubber sealant and preparation method thereof

A room temperature vulcanization, silicone rubber technology, used in adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of high industrialization threshold, high cost, poor versatility, etc., achieve high strength retention rate, improve adhesion. The effect of good bonding performance and good water resistance

Inactive Publication Date: 2015-05-13
TONSAN ADHESIVES INC
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high purity requirements of adhesion promoter products, the industrialization threshold is high and the cost is high
In addition, the special structure of the adhesi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-component deoximation type room-temperature vulcanized silicone rubber sealant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1:

[0031] Add 100 parts of α, ω-dihydroxy polydimethylsiloxane with a viscosity of 20,000 mPa.s and 2 parts of γ-aminopropyltrimethylsilane into the planetary stirring tank, heat it up to 80 ° C, at -0.09 Mix under ~-0.1MPa vacuum condition for 30min, cool down to below 40℃. Add 15 parts of dimethyl silicone oil with a viscosity of 500mpa.s, 80 parts of calcium carbonate, 10 parts of fumed silica, in N 2 Add 10 parts of vinyl tributyl ketoximinosilane and 0.3 part of dibutyltin dilaurate under the protection, and stir under -0.09~-0.1MPa vacuum condition until uniform without bubbles.

Example Embodiment

[0032] Example 2:

[0033] Add 100 parts of α,ω-dihydroxypolydimethylsiloxane with a viscosity of 20000 mPa.s and 3 parts of γ-aminopropyltriethoxysilane into the planetary stirring kettle, heat it up to 60°C, and at- Mix for 120min under the vacuum condition of 0.09~-0.1MPa, cool down to below 40℃, add 15 parts of dimethyl silicone oil with a viscosity of 100mpa.s, 100 parts of calcium carbonate, 8 parts of fumed silica, in N 2Under protection, 4 parts of methyltributanone oximinosilane, 6 parts of vinyltributanone oximosilane, and 0.2 part of dibutyltin dilaurate were added, and the mixture was stirred under vacuum conditions of -0.09 to -0.1 MPa until it was homogeneous and free of bubbles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a one-component deoximation type room-temperature vulcanized silicone rubber sealant and a preparation method thereof. The sealant is prepared through the following steps: mixing alpha,omega-dyhydroxylpolydimethylsiloxane and a silane coupling agent at a high temperature, terminating alpha,omega-dyhydroxylpolydimethylsiloxane with the silane coupling agent, and then adding dimethyl silicone oil, a de-ketoxime type cross-linking agent, a filling material and a catalyst. Compared with a traditional deoximation type sealant, the sealant has excellent adhesive properties for stainless steel, aluminium alloy, magnesium alloy, PPO, PC, PVC, PMMA, ABS, PET and the like, and can be used for adhesion and sealing in the industries of electronics, automobiles, household appliances, photovoltaic modules and the like. Besides, the sealant has excellent water resistance and especially has a high strength retention rate under high-temperature and high-humidity conditions.

Description

technical field [0001] The invention relates to a one-component deoxime type room temperature vulcanized silicone rubber, especially a one-component deoxime type room temperature vulcanized silicone rubber sealant with a wide range of bonding materials, high bonding strength, and excellent damp heat aging resistance and its preparation method. Background technique [0002] One-component room temperature vulcanized silicone rubber has been widely used in construction, electronics, automobiles, solar energy and other fields due to its excellent operability, temperature resistance and weather resistance. Condensed one-component RTV silicone rubber can be divided into deacidification type, dealcoholization type, deketoxime type, acetone removal type, and deamidation type according to the small molecules released during crosslinking. Among them, deketoxime type one-component room temperature vulcanized silicone rubber has the advantages of moderate vulcanization speed, small ket...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J183/06C09J183/04C09J11/06C09J11/04
Inventor 王瑶王德波孙应发苏丹
Owner TONSAN ADHESIVES INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products